The Project Gutenberg eBook of Researches on Cellulose, 1895-1900
    
This ebook is for the use of anyone anywhere in the United States and
most other parts of the world at no cost and with almost no restrictions
whatsoever. You may copy it, give it away or re-use it under the terms
of the Project Gutenberg License included with this ebook or online
at www.gutenberg.org. If you are not located in the United States,
you will have to check the laws of the country where you are located
before using this eBook.

Title: Researches on Cellulose, 1895-1900

Author: C. F. Cross
        E. J. Bevan

Release date: September 16, 2007 [eBook #22620]

Language: English

Credits: Produced by Juliet Sutherland, Josephine Paolucci and the
        Online Distributed Proofreading Team at http://www.pgdp.net.
        (This file was produced from images generously made
        available by The Internet Archive/Million Book Project).


*** START OF THE PROJECT GUTENBERG EBOOK RESEARCHES ON CELLULOSE, 1895-1900 ***




Produced by Juliet Sutherland, Josephine Paolucci and the
Online Distributed Proofreading Team at http://www.pgdp.net.
(This file was produced from images generously made
available by The Internet Archive/Million Book Project).










RESEARCHES ON CELLULOSE

1895-1900

BY

CROSS & BEVAN

(C. F. CROSS AND E. J. BEVAN)


_SECOND EDITION_


LONGMANS, GREEN, AND CO.
39 PATERNOSTER ROW, LONDON
NEW YORK, BOMBAY, AND CALCUTTA

1907

All rights reserved

       *       *       *       *       *

Transcriber's note:

For Text: A word surrounded by a cedilla such as ~this~ signifies that
the word is bolded in the text. A word surrounded by underscores like
_this_ signifies the word is italics in the text. The italic and bold
markup for single italized letters (such as variables in equations) and
"foreign" abbreviations are deleted for easier reading.

For numbers and equations: Parentheses have been added to clarify
fractions. Underscores before bracketed numbers in equations denote a
subscript. Superscripts are designated with a caret and brackets, e.g.
11.1^{3} is 11.1 to the third power. Greek letters in equations are
translated to their English version.

The sections in the Table of Contents are not used in the actual text.
They have been added for clarity.

Minor typos have been corrected and footnotes moved to the end of the
sections

       *       *       *       *       *





PREFACE TO SECOND EDITION


This edition is a _reprint_ of the first in response to a continuous
demand for the book. The matter, consisting as it does largely of
records, does not call for any revision, and, as a contribution to the
development of theory, any particular interest which it has is
associated with the date at which it was written.

The volume which has since appeared is the sequel, and aims at an
exposition of the subject "to date".




PREFACE


This volume, which is intended as a supplement to the work which we
published in 1895, gives a brief account of researches which have been
subsequently published, as well as of certain of our own investigations,
the results of which are now for the first time recorded.

We have not attempted to give the subject-matter the form of a connected
record. The contributions to the study of 'Cellulose' which are noticed
are spread over a large area, are mostly 'sectional' in their aim, and
the only cohesion which we can give them is that of classifying them
according to the plan of our original work. Their subject-matter is
reproduced in the form of a _précis_, as much condensed as possible; of
the more important papers the original title is given. In all cases we
have endeavoured to reproduce the Author's main conclusions, and in most
cases without comment or criticism.

Specialists will note that the basis of investigation is still in a
great measure empirical; and of this the most obvious criterion is the
confusion attaching to the use of the very word 'Cellulose.' This is due
to various causes, one of which is the curious specialisation of the
term in Germany as the equivalent of 'wood cellulose.' The restriction
of this general or group term has had an influence even in scientific
circles. Another influence preventing the recognition of the obvious
and, as we think, inevitable basis of classification of the 'celluloses'
is the empiricism of the methods of agricultural chemistry, which as
regards cellulose are so far chiefly concerned with its negative
characteristics and the analytical determination of the indigestible
residue of fodder plants. Physiologists, again, have their own views and
methods in dealing with cellulose, and have hitherto had but little
regard to the work of the chemist in differentiating and classifying the
celluloses on a systematic basis. There are many sides to the subject,
and it is only by a sustained effort towards centralisation that the
general recognition of a systematic basis can be secured.

We may, we hope usefully, direct attention to the conspicuous neglect of
the subject in this country. To the matter of the present volume,
excluding our own investigations, there are but two contributions from
English laboratories. We invite the younger generation of students of
chemistry to measure the probability of finding a working career in
connection with the cellulose industries. They will not find this
invitation in the treatment accorded to the subject in text-books and
lectures. It is probable, indeed, that the impression produced by their
studies is that the industries in coal-tar products largely exceed in
importance those of which the carbohydrates are the basis; whereas the
former are quite insignificant by comparison. A little reflection will
prove that cellulose, starch, and sugar are of vast industrial moment in
the order in which they are mentioned. If it is an open question to
what extent science follows industry, or _vice versa_, it is not open to
doubt that scientific men, and especially chemists, are called in these
days to lead and follow where industrial evolution is most active. There
is ample evidence of activity and great expansion in the cellulose
industries, especially in those which involve the chemistry of the raw
material; and the present volume should serve to show that there is
rapid advance in the science of the subject. Hence our appeal to the
workers not to neglect those opportunities which belong to the days of
small beginnings.

We have especially to acknowledge the services of Mr. J. F. BRIGGS in
investigations which are recorded on pp. 34-40 and pp. 125-133 of the
text.




CONTENTS

THE MATTER OF THIS VOLUME MAY BE DIVIDED INTO THE FOLLOWING SECTIONS


                                                                 PAGE

INTRODUCTION--DEALING WITH THE SUBJECT IN GENERAL OUTLINE           1


SECTION

I. GENERAL CHEMISTRY OF THE TYPICAL COTTON CELLULOSE               13

II. SYNTHETICAL DERIVATIVES--SULPHOCARBONATES AND ESTERS           27

III. DECOMPOSITIONS OF CELLULOSE SUCH AS THROW LIGHT
     ON THE PROBLEM OF ITS CONSTITUTION                            67

IV. CELLULOSE GROUP, INCLUDING HEMICELLULOSES AND
    TISSUE CONSTITUENTS OF FUNGI                                   97

V. FURFUROIDS, i.e. PENTOSANES AND FURFURAL-YIELDING
   CONSTITUENTS GENERALLY                                         114

VI. THE LIGNOCELLULOSES                                           125

VII. PECTIC GROUP                                                 152

VIII. INDUSTRIAL AND TECHNICAL. GENERAL REVIEW                    155


INDEX OF AUTHORS                                                  177

INDEX OF SUBJECTS                                                 178




CELLULOSE




INTRODUCTION


In the period 1895-1900, which has elapsed since the original
publication of our work on 'Cellulose,' there have appeared a large
number of publications dealing with special points in the chemistry of
cellulose. So large has been the contribution of matter that it has been
considered opportune to pass it under review; and the present volume,
taking the form of a supplement to the original work, is designed to
incorporate this new matter and bring the subject as a whole to the
level to which it is thereby to be raised. Some of our critics in
reviewing the original work have pronounced it 'inchoate.' For this
there are some explanations inherent in the matter itself. It must be
remembered that every special province of the science has its systematic
beginning, and in that stage of evolution makes a temporary 'law unto
itself.' In the absence of a dominating theory or generalisation which,
when adopted, gives it an organic connection with the general advance of
the science, there is no other course than to classify the
subject-matter. Thus 'the carbohydrates' may be said to have been in the
inchoate condition, qualified by a certain classification, prior to the
pioneering investigations of Fischer. In attacking the already
accumulated and so far classified material from the point of view of a
dominating theory, he found not only that the material fell into
systematic order and grew rapidly under the stimulus of fruitful
investigation, but in turn contributed to the firmer establishment of
the theoretical views to which the subject owed its systematic new
birth. On the other hand, every chemist knows that it is only the
simpler of the carbohydrates which are so individualised as to be
connoted by a particular formula in the stereoisomeric system. Leaving
the monoses, there is even a doubt as to the constitution of cane sugar;
and the elements of uncertainty thicken as we approach the question of
the chemical structure of starch. This unique product of plant life has
a literature of its own, and how little of this is fully known to what
we may term the 'average chemist' is seen by the methods he will employ
for its quantitative estimation. In one particular review of our work
where we are taken to task for producing 'an aggravating book, inchoate
in the highest degree ... disfigured by an obscurity of diction which
must materially diminish its usefulness' ['Nature,' 1897, p. 241], the
author, who is a well-known and competent critic, makes use of the short
expression in regard to the more complex carbohydrates, 'Above cane
sugar, higher in the series, all is chaos,' and in reference to starch,
'the subject is still enshrouded in mystery.' This 'material' complexity
is at its maximum with the most complex members of the series, which are
the celluloses, and we think accounts in part for the impatience of our
critic. 'Obscurity of diction' is a personal quantity, and we must leave
that criticism to the fates. We find also that many workers whose
publications we notice in this present volume quite ignore the _plan_ of
the work, though they make use of its matter. We think it necessary to
restate this plan, which, we are satisfied, is systematic, and, in fact,
inevitable. Cellulose is in the first instance a _structure_, and the
anatomical relationships supply a certain basis of classification. Next,
it is known to us and is defined by the negative characteristics of
resistance to hydrolytic actions and oxidations. These are dealt with in
the order of their intensity. Next we have the more positive definition
by ultimate products of hydrolysis, so far as they are known, which
discloses more particularly the presence of a greater or less proportion
of furfural-yielding groups. Putting all these together as criteria of
function and composition we find they supply common or general dividing
lines, within which groups of these products are contained. The
classification is natural, and in that sense inevitable; and it not only
groups the physiological and chemical facts, but the industrial also. We
do not propose to argue the question whether the latter adds any cogency
to a scientific scheme. We are satisfied that it does, and we do not
find any necessity to exclude a particular set of phenomena from
consideration, because they involve 'commercial' factors. We have dealt
with this classification in the original work (p. 78), and we discuss
its essential basis in the present volume (p. 28) in connection with the
definition of a 'normal' cellulose. But the 'normal' cellulose is not
the only cellulose, any more than a primary alcohol or an aliphatic
alcohol are the only alcohols. This point is confused or ignored in
several of the recent contributions of investigators. It will suffice to
cite one of these in illustration. On p. 16 we give an account of an
investigation of the several methods of estimating cellulose, which is
full of valuable and interesting matter. The purpose of the author's
elaborate comparative study is to decide which has the strongest claims
to be regarded as the 'standard' method. They appear to have a
preference for the method of Lange--viz. that of heating at high
temperatures (180°) with alkaline hydrates, but the investigation shows
that (as we had definitely stated in our original work, p. 214) this is
subject to large and variable errors. The adverse judgment of the
authors, we may point out, is entirely determined on the question of
aggregate weight or yield, and without reference to the ultimate
composition or constitution of the final product. None of the available
criteria are applied to the product to determine whether it is a
cellulose (anhydride) or a hydrate or a hydrolysed product. After these
alkali-fusion processes the method of chlorination is experimentally
reviewed and dismissed for the reason that the product retains
furfural-yielding groups, which is, from our point of view, a particular
recommendation, i.e. is evidence of the selective action of the chlorine
and subsequent hydrolysis upon the lignone group. As a matter of fact it
is the only method yet available for isolating the cellulose from a
lignocellulose by a treatment which is quantitatively to be accounted
for in every detail of the reactions. It does not yield a 'normal'
cellulose, and this is the expression which, in our opinion, the authors
should have used. It should have been pointed out, moreover, that, as
the cellulose is separated from actual condensed combination with the
lignone groups, it may be expected to be obtained in a hydrated form,
and also not as a homogeneous substance like the normal cotton
cellulose. The product is a cellulose of the second group of the
classification. Another point in this investigation which we must
criticise is the ultimate selection of the Schulze method of prolonged
maceration with nitric acid and a chlorate, followed by suitable
hydrolysis of the non-cellulose derivatives to soluble products. Apart
from its exceptional inconvenience, rendering it quite impracticable in
laboratories which are concerned with the valuation of cellulosic raw
materials for industrial purposes, the attack of the reagent is complex
and ill-defined. This criticism we would make general by pointing out
that such processes quite ignore the specific characteristics of the
non-cellulose components of the compound celluloses. The second division
of the plan of our work was to define these constituents by bringing
together all that had been established concerning them. These groups are
widely divergent in chemical character, as are the compound celluloses
in function in the plant. Consequently there is for each a special
method of attack, and it is a reversion to pure empiricism to expect any
one treatment to act equally on the pectocelluloses, lignocelluloses,
and cutocelluloses. Processes of isolating cellulose are really more
strictly defined as methods of selective and regulated attack of the
groups with which they occur, combined or mixed. A chemist familiar with
such types as rhea or ramie (pectocellulose), jute (lignocellulose), and
raffia (cutocellulose) knows exactly the specific treatment to apply to
each for isolating the cellulose, and must view with some surprise the
appearance at this date of such 'universal prescriptions' as the process
in question.

The third division of our plan of arrangement comprised the synthetical
derivatives of the celluloses, the sulphocarbonates first, as peculiarly
characteristic, and then the esters, chiefly the acetates, benzoates,
and nitrates. To these, investigators appear to have devoted but little
attention, and the contribution of new matter in the present volume is
mainly the result of our own researches. It will appear from this work
that an exhaustive study of the cellulose esters promises to assist very
definitely in the study of constitutional problems.

This brings us to the fourth and, to the theoretical chemist, the most
important aspect of the subject, the problem of the actual molecular
structure of the celluloses and compound celluloses. It is herein we are
of opinion that the subject makes a 'law unto itself.' If the
constitution of starch is shrouded in mystery and can only be vaguely
expressed by generalising a complex mass of statistics of its successive
hydrolyses, we can only still more vaguely guess at the distance which
separates us from a mental picture of the cellulose unit. We endeavour
to show by our later investigations that this problem merges into that
of the actual structure of cellulose in the mass. It is definitely
ascertained that a change in the molecule, or reacting unit, of a
cellulose, proportionately affects the structural properties of the
derived compounds, both sulphocarbonates and esters. This is at least an
indication that the properties of the visible aggregates are directly
related to the actual configuration of the chemical units. But it
appears that we are barred from the present discussion of such a problem
in absence of any theory of the solid state generally, but more
particularly of those forms of matter which are grouped together as
'colloids.'

Cellulose is distinguished by its inherent constructive functions, and
these functions take effect in the plastic or colloidal condition of the
substance. These properties are equally conspicuous in the synthetical
derivatives of the compound. Without reference, therefore, to further
speculations, and not deterred by any apparent hopelessness of solving
so large a problem, it is clear that we have to exhaust this field by
exact measurements of all the constants which can be reduced to
numerical expression. It is most likely that the issue may conflict with
some of our current views of the molecular state which are largely drawn
from a study of the relatively dissociated forms of matter. But such
conflicts are only those of enlargement, and we anticipate that all
chemists look for an enlargement of the molecular horizon precisely in
those regions where the forces of cell-life manifest themselves.

The _cellulose group_ has been further differentiated by later
investigations. The fibrous celluloses of which the typical members
receive important industrial applications, graduate by insensible stages
into the hemicelluloses which may be regarded as a well-established
sub-group. In considering their morphological and functional
relationships it is evident that the graduation accords with their
structure and the less permanent functions which they fulfil. They are
aggregates of monoses of the various types, chiefly mannose, galactose,
dextrose, &c., so far as they have been investigated.

Closely connected with this group are the constituents of the tissues of
fungi. The recent researches of Winterstein and Gilson, which are noted
in this present volume, have established definitely that they contain a
nitrogenous group in intimate combination with a carbohydrate complex.
This group is closely related to chitin, yielding glucosamin and acetic
acid as products of ultimate hydrolysis. Special interest attaches to
these residues, as they are in a sense intermediate products between the
great groups of the carbohydrates and proteids (E. Fischer, Ber. 19,
1920), and their further investigation by physiological methods may be
expected to disclose a genetic connection.

The _lignocelluloses_ have been further investigated. Certain new types
have been added, notably a soluble or 'pectic' form isolated from the
juice of the white currant (p. 152), and the pith-like wood of the
Æschynomene (p. 135).

Further researches on the typical fibrous lignocellulose have given us a
basis for correcting some of the conclusions recorded in our original
work, and a study of the esters has thrown some light on the
constitution of the complex (p. 130).

Of importance also is the identification of the hydroxyfurfurals as
constituents of the lignocelluloses generally, and the proof that the
characteristic colour-reactions with phenols (phloroglucinol) may be
ascribed to the presence of these compounds (p. 116).

The _pectocelluloses_ have not been the subject of systematic chemical
investigation, but the researches of Gilson ('La Cristallisation de la
Cellulose et la Composition Chimique de la Membrane Cellulaire
Végétale,' 'La Revue,' 'La Cellule,' i. ix.) are an important
contribution to the natural history of cellulose, especially in relation
to the 'pectic' constituents of the parenchymatous celluloses.
Indirectly also the researches of Tollens on the 'pectins' have
contributed to the subject in correcting some of the views which have
had a text-book currency for a long period. These are dealt with on p.
151. The results establish that the pectins are rather the soluble
hydrated form of cellulosic aggregates in which acid groups may be
represented; but such groups are not to be regarded as essentially
characteristic of this class of compounds.

~Furfural-yielding Substances~ (Furfuroids).--This group of plant products
has been, by later investigations, more definitely and exclusively
connected with the celluloses--i.e. with the more permanent of plant
tissues. From the characteristic property of yielding furfural, which
they have in common with the pentoses, they have been assumed to be the
anhydrides of these C_{5} sugars or pentosanes; but the direct evidence
for this assumption has been shown to be wanting. In regard to their
origin the indirect evidences which have accumulated all point to their
formation in the plant from hexoses. Of special interest, in its
bearings on this point, is the direct transformation of levulose into
furfural derivatives, which takes place under the action of condensing
agents. The most characteristic is that produced by the action of
anhydrous hydrobromic acid in presence of ether [Fenton], yielding a
brommethyl furfural

     C_{6}H_{12}O_{6} - 4H_{2}O + HBr = C_{5}H_{3}.O_{2}.CH_{2}Br

with a Br atom in the methyl group. These researches of Fenton's appear
to us to have the most obvious and direct bearings upon the genetic
relationships of the plant furfuroids and not only _per se_. To give
them their full significance we must recall the later researches of
Brown and Morris, which establish that cane sugar is a primary or direct
product of assimilation, and that starch, which had been assumed to be a
species of universal _matière première_, is probably rather a general
reserve for the elaborating work of the plant. If now the aldose groups
tend to pass over into the starch form, representing a temporary
overflow product of the assimilating energy, it would appear that the
ketose or levulose groups are preferentially used up in the elaboration
of the permanent tissue. We must also take into consideration the
researches of Lobry de Bruyn showing the labile functions of the typical
CO group in both aldoses and hexoses, whence we may conclude that in the
plant-cell the transition from dextrose to levulose is a very simple and
often occurring process.

We ourselves have contributed a link in this chain of evidence
connecting the furfuroids of the plant with levulose or other
keto-hexose. We have shown that the hydroxyfurfurals are constituents of
the lignocelluloses. The proportion present in the free state is small,
and it is not difficult to show that they are products of breakdown of
the lignone groups. If we assume that such groups are derived ultimately
from levulose, we have to account for the detachment of the methyl
group. This, however, is not difficult, and we need only call to mind
that the lignocelluloses are characterised by the presence of methoxy
groups and a residue which is directly and easily hydrolysed to acetic
acid. Moreover, the condensation need not be assumed to be a simple
dehydration with attendant rearrangement; it may very well be
accompanied or preceded by fixation of oxygen. Leaving out the
hypothetical discussion of minor variations, there is a marked
convergence of the evidence as to the main facts which establish the
general relationships of the furfuroid group. This group includes both
saturated and unsaturated or condensed compounds. The former are
constituents of celluloses, the latter of the lignone complex of the
lignocelluloses.

The actual production of furfural by boiling with condensing acids is a
quantitative measure of only a portion, i.e. certain members of the
group. The hydroxyfurfurals, not being volatile, are not measured in
this way. By secondary reactions they may yield some furfural, but as
they are highly reactive compounds, and most readily condensed, they are
for the most part converted into complex 'tarry' products. Hence we have
no means, as yet, of estimating those tissue constituents which yield
hydroxyfurfurals; also we have no measure of the furfurane-rings
existing performed in such a condensed complex as lignone. But, chemists
having added in the last few years a large number of facts and
well-defined probabilities, it is clear that the further investigation
of the furfuroid group will take its stand upon a much more adequate
basis than heretofore. On the view of 'furfural-yielding' being
co-extensive with 'pentose or pentosane,' not only were a number of
important facts obscured or misinterpreted, but there was a barrenness
of suggestion of genetic relationships. As the group has been widened
very much beyond these limits, it is clear that if any group term or
designation is to be retained that of 'furfuroid' is 'neutral' in
character, and equally applicable to saturated substances of such widely
divergent chemical character as pentoses, hexosones, glycuronic acid,
and perhaps, most important of all, levulose itself, all of which are
susceptible of condensation to furfural or furfurane derivatives, as
well as to those unsaturated compounds, constituents of plant tissues
which are already furfurane derivatives.

From the chemical point of view such terms are perhaps superfluous. But
physiological relationships have a significance of their own; and there
is a physiological or functional cohesion marking this group which
calls for recognition, at least for the time, and we therefore propose
to retain the term furfuroid.[1]

~General Experimental Methods.~--In the investigation of the cellulose
group it is clear that methods of ultimate hydrolysis are of first
importance. None are so convenient as those which are based on the
action of sulphuric acid, more or less concentrated (H_{2}SO_{4}.3H_{2}O
- H_{2}SO_{4}H_{2}O). Such methods have been frequently employed in the
investigations noted in this volume. We notice a common deficiency in
the interpretation of the results. It appears to be sufficient to
isolate and identify a crystalline monose, without reference to the
yield or proportion to the parent substance, to establish some main
point in connection with its constitution. On the other hand, it is
clear that in hydrolysing a given cellulose-complex we ought to aim at
complete, i.e. _quantitative, statistics_. The hydrolytic transformation
of starch to dextrins and maltose has been followed in this way, and the
methods may serve as a model to which cellulose transformations should
be approximated. In fact, what is very much wanted is a systematic
re-examination of the typical celluloses in which all the constants of
the terms between the original and the ultimate monose groups shall be
determined. Such constants are similar to those for the starch-dextrose
series, viz. opticity and cupric reduction. Various methods of
fractionation are similarly available, chiefly the precipitation of the
intermediate 'dextrins' by alcohol.

Where the original celluloses are homogeneous we should thus obtain
transformation series, similarly expressed to those of starch. In the
case of the celluloses which are mixtures, or of complex constitution,
there are various methods of either fractionating the original, or of
selectively attacking particular monoses resulting from the
transformation. By methods which are approximately quantitative a
mixture of groups, such as we have, for instance, in jute cellulose,
could be followed through the several stages of their resolution into
monoses. To put the matter generally, in these colloidal and complex
carbohydrates the ordinary physical criteria of molecular weight are
wanting. Therefore, we cannot determine the relationship of a given
product of decomposition to the parent molecule save by means of a
quantitative mass-proportion. Physical criteria are only of determining
value when associated with such constants as cupric reduction, and
these, again, must be referred to some arbitrary initial weight, such
as, for convenience, 100 parts of the original.

Instead of adopting these methods, without which, as a typical case, the
mechanism of starch conversions could not have been followed, we have
been content with a purely qualitative study of the analogous series
obtainable from the celluloses under the action of sulphuric acid. A
very important field of investigation lies open, especially to those who
are generally familiar with the methods of studying starch conversions;
and we may hope in this direction for a series of valuable contributions
to the problem of the actual constitution of the celluloses.

FOOTNOTES:

[1] In this we are confirmed by other writers. See Tollens, _J. für
Landw._ 1901, p. 27.




SECTION I. GENERAL CHEMISTRY OF THE TYPICAL COTTON CELLULOSE


(p. 3)[2] ~Ash Constituents.~--It is frequently asserted that silica has a
structural function _sui generis_ in the plant skeleton, having a
relationship to the cellulosic constituents of the plant, distinct from
that of the inorganic ash components with which it is associated. It
should be noted that the matter has been specifically investigated in
two directions. In Berl. Ber. 5, 568 (A. Ladenburg), and again in 11,
822 (W. Lange), appear two papers 'On the Nature of Plant Constituents
containing Silicon,' which contain the results of experimental
investigations of equisetum species--distinguished for their
exceptionally high 'ash' with large proportion of silica--to determine
whether there are any grounds for assuming the existence of
silicon-organic compounds in the plant, the analogues of carbon
compounds. The conclusions arrived at are entirely negative. In
reference to the second assumption that the cuticular tissues of cereal
straws, of esparto, of the bamboo, owe their special properties to
siliceous components, it has been shown by direct experiment upon the
former that their rigidity and resistance to water are in no way
affected by cultivation in a silica-free medium. In other words, the
structural peculiarities of the gramineæ in these respects are due to
the physical characteristics chiefly of the (lignified) cells of the
hypodermal tissue, and to the composition and arrangement of the cells
of the cuticle.

_'Swedish' filter papers_ of modern make are so far freed from inorganic
constituents that the weight of the ash may be neglected in nearly all
quantitative experiments [Fresenius, Ztschr. Anal Chem. 1883, 241]. It
represents usually about 1/1000 mgr. per 1 sq. cm. of area of the paper.

_The form of an 'ash'_ derived from a fibrous structure, is that of the
'organic' original, more or less, according to its proportion and
composition. The proportion of 'natural ash' is seldom large enough, nor
are the components of such character as to give a coherent ash, but if
in the case of a fibrous structure it is combined or intimately mixed
with inorganic compounds deposited within the fibres from solution, the
latter may be made to yield a perfect skeleton of the fibre after
burning off the organic matter. It is by such means that the mantles
used in the Welsbach system of incandescent lighting are prepared. A
purified cotton fabric--or yarn--is treated with a concentrated solution
of the mixed nitrates of thorium and cerium, and, after drying, the
cellulose is burned away. A perfect and coherent skeleton of the fabric
is obtained, composed of the mixed oxides. Such mantles have fulfilled
the requirements of the industry up to the present time, but later
experiments forecast a notable improvement. It has been found that
artificial cellulose fibres can be spun with solutions containing
considerable proportions of soluble compounds of these oxides. Such
fibres, when knitted into mantles and ignited, yield an inorganic
skeleton of the oxides of homogeneous structure and smooth contour. De
Mare in 1894, and Knofler in 1895, patented methods of preparing such
cellulose threads containing the salts of thorium and cerium, by
spinning a collodion containing the latter in solution. When finally
ignited, after being brought into the suitable mantle form, there
results a structure which proves vastly more durable than the original
Welsbach mantle. The cause of the superiority is thus set forth by V.
H. Lewes in a recent publication (J. Soc. of Arts, 1900, p. 858): 'The
alteration in physical structure has a most extraordinary effect upon
the light-giving life of the mantle, and also on its strength, as after
burning for a few hundred hours the constant bombardment of the mantle
by dust particles drawn up by the rush of air in the chimney causes the
formation of silicates on the surface of the mantle owing to silica
being present in the air, and this seems to affect the Welsbach
structure far more than it does the "Clamond" type, with the result that
when burned continuously the Welsbach mantle falls to so low a pitch of
light emissivity after 500 to 600 hours, as to be a mere shadow of its
former self, giving not more than one-third of its original light,
whilst the Knofler mantle keeps up its light-emitting power to a much
greater extent, and the Lehner fabric is the most remarkable of all. Two
Lehner mantles which have now been burning continuously in my laboratory
for over 3,000 hours give at this moment a brighter light emissivity
than most of the Welsbachs do in their prime.' ...'The new developments
of the Clamond process form as important a step in the history of
incandescent gas lighting as the discoveries which gave rise to the
original mantles.'

It has further been found that the oxides themselves can be dissolved in
the cellulose alkaline sulphocarbonate (viscose) solution, and
artificial threads have been spun containing from 25 to 30 p.ct. of the
oxides in homogeneous admixture with the cellulose. This method has
obvious advantages over the collodion method both in regard to the
molecular relationship of the oxides to the cellulose and to cheapness
of production.


UNTERSUCHUNGEN ÜBER VERSCHIEDENE BESTIMMUNGSMETHODEN DER CELLULOSE.

H. SURINGAR AND B. TOLLENS (Ztschr. angew. Chem. 1896, No. 23).

~INVESTIGATION OF METHODS OF DETERMINING CELLULOSE.~

_Introduction._--This is an exhaustive bibliography of the subject,
describing also the various methods of cellulose estimation, noted in
historical sequence. First, the Weende 'crude fibre' method (Henneberg)
with modifications of Wattenberg, Holdefleiss, and others is dealt with.
The product of this treatment, viz. 'crude fibre' is a mixture,
containing furfuroids and lignone compounds. Next follows a group of
processes which aim at producing a 'pure cellulose' by eliminating
lignone constituents, for which the merely hydrolytic treatments of the
Weende method are ineffectual. The method of F. Schulze--prolonged
digestion with dilute nitric acid, with addition of chlorate--has been
largely employed, though the composition of the product is more or less
divergent from a 'pure cellulose.'

Dilute nitric acid at 60-80° (Cross and Bevan) and a dilute mixture of
nitric and sulphuric acids (Lifschutz) have been employed for isolating
cellulose from the lignocelluloses. Hoffmeister modifies the method of
Schulze by substituting hydrochloric acid for the nitric acid. Treatment
with the halogens associated with alkaline processes of hydrolysis is
the basis of the methods of Hugo Muller (bromine water) and Cross and
Bevan (chlorine gas). Lastly, the authors notice the methods based upon
the action of the alkaline hydrates at high temperatures (180°) in
presence of water (Lange), or of glycerin (Gabriel). The process of
heating to 210° with glycerin only (Hönig) yields a very impure and
ill-defined product.

For comparative investigation of these processes certain celluloses and
cellulosic materials were prepared as follows:

(a) _'Rag' cellulose._--A chemical filter paper, containing only
cotton and linen celluloses, was further purified by boiling with dilute
acid and dilute alkali. After thorough washing it was air-dried.

(b) _Wood cellulose._--Pine wood sawdust was treated by digestion for
fourteen days with dilute nitric acid with addition of chlorate
(Schulze). The mass was washed and digested with alkaline lye (1.25
p.ct. KOH), and exhaustively washed, treated with dilute acetic acid;
again washed, and finally air-dried.

This product was found to yield 2.3 p.ct. furfural on distillation with
HCl (1.06 sp.gr.).

(c) _Purified wood._--Pine wood sawdust was treated in succession with
dilute alkalis and acids, in the cold, and with alcohol and ether until
exhausted of products soluble in these liquids and reagents.

In addition to the above the authors have also employed jute fibre and
raw cotton wool in their investigations.

They note that the yield of cellulose is in many cases sensibly lowered
by treating the material after drying at the temperature of 100°. The
material for treatment is therefore weighed in the air-dry condition,
and a similar sample weighed off for drying at 100° for determination of
moisture.

The main results of the experimental investigation are as follows:--

_Weende process_ further attacks the purified celluloses as follows:
Wood cellulose losing in weight 8-9 p.ct.; filter paper, 6-7.5 p.ct.,
and the latter treated a second time loses a further 4-5 p.ct. It is
clear, therefore, that the process is of purely empirical value.

_Schulze._--This process gave a yield of 47.6 p.ct. cellulose from pine
wood. The celluloses themselves, treated by the process, showed losses
of 1-3 p.ct. in weight, much less therefore than in the preceding case.

_Hönig's_ method of heating with glycerin to 210° was found to yield
products very far removed from 'cellulose.' The process may have a
certain value in estimations of 'crude fibre,' but is dismissed from
further consideration in relation to cellulose.

_Lange._--The purpose of the investigation was to test the validity of
the statement that the celluloses are not attacked by alkaline hydrates
at 180°. Experiments with pine wood yielded a series of percentages for
cellulose varying from 36 to 41; the 'purified wood' gave also variable
numbers, 44 to 49 per cent. It was found possible to limit these
variations by altering the conditions in the later stages of isolating
the product; but further experiments on the celluloses themselves
previously isolated by other processes showed that they were profoundly
and variably attacked by the 'Lange' treatment, wood cellulose losing 50
per cent. of its weight, and filter paper (cellulose) losing 15 per
cent. Further, a specimen of jute yielded 58 per cent. of cellulose by
this method instead of the normal 78 per cent. It was also found that
the celluloses isolated by the process, when subjected to a second
treatment, underwent a further large conversion into soluble
derivatives, and in a third treatment further losses of 5-10 per cent
were obtained. The authors attach value, notwithstanding, to the process
which they state to yield an 'approximately pure cellulose,' and they
describe a modified method embodying the improvements in detail
resulting from their investigation.

_Gabriel's_ method of heating with a glycerin solution of alkaline
hydrate is a combination of 'Hönig' and 'Lange.' An extended
investigation showed as in the case of the latter that the
celluloses themselves are more or less profoundly attacked by the
treatment--further that the celluloses isolated from lignocelluloses and
other complex raw materials are much 'less pure' than those obtained by
the Lange process. Thus, notably in regard to furfural yielding
constituents, the latter yield 1-2 p.ct. furfural, whereas _specimens of
'jute cellulose'_ obtained by the Gabriel process were found to yield _9
to 13 p.ct. furfural_.

_Cross and Bevan._--Chlorination process yielded in the hands of the
authors results confirming the figures given in 'Cellulose' for yield of
cellulose. Investigation of the products for yield of furfural, gave 9
p.ct. of this aldehyde showing the presence of celluloses, other than
the normal type.

_Conclusions._--The subjoined table gives the mean numerical results for
yield of end-product or 'cellulose' by the various methods. In the case
of the 'celluloses' the results are those of the further action of the
several processes on the end-product of a previous process.

                       |                 Methods
                       | F. Schulze | Weende | Lange | Gabriel |  Cross
                       |            |        |       |         | and Bevan
--------------------------------------------------------------------------
Wood cellulose         | 98.51      | 91.52  | 48.22 | 55.93   | --
Filter paper cellulose | 99.62      | 95.63  | 78.17 | 79.77   | --
Swedish filter paper   | 96.58      |  --    | 84.76 |  --     | --
Ordinary filter paper  | 98.17      | 93.39  | 86.58 |  --     | --
Cotton ('wool')        | 98.38      | 89.98  | 63.96 | 67.88   | --
Jute                   |  --        |  --    | 57.93 | 71.64   | 75.27
Purified wood          |  --        |  --    |{49.27 |  --     | --
                       |            |        |{46.56 |         |
Raw wood               | 47.60      |  --    |{40.82 |  --     | --
                       |            |        |{38.87 |         |
--------------------------------------------------------------------------

The final conclusion drawn from the results is that none of the
processes fulfil the requirements of an ideal method. Those which may
be carried out in a reasonably short time are deficient in two
directions: (1) they yield a 'cellulose' containing more or less
oxycellulose; (2) the celluloses themselves are attacked under the
conditions of treatment, and the end product or cellulose merely
represents a particular and at the same time variable equilibrium, as
between the resistance of the cellulose and the attack of the reagents
employed; this attack being by no means confined to the non-cellulose
constituents. Schulze's method appears to give the nearest approximation
to the 'actual cellulose' of the raw material.

       *       *       *       *       *

(p. 8) ~SOLUTIONS OF CELLULOSE~--(1) ~ZINC CHLORIDE.~--To prepare a
homogeneous solution of cellulose by means of the neutral chloride, a
prolonged digestion at or about 100° with the concentrated reagent is
required. The dissolution of the cellulose is not a simple phenomenon,
but is attended with hydrolysis and a certain degree of condensation.
The latter result is evidenced by the formation of furfural, the former
by the presence of soluble carbohydrates in the solution obtained by
diluting the original solution and filtering from the reprecipitated
cellulose. The authors have observed that in carefully conducted
experiments cotton cellulose may be dissolved in the reagent, and
reprecipitated with a loss of only 1 p.ct. in weight. This, however, is
a 'net' result, and leaves undetermined the degree of hydration of the
recovered cellulose as of hydrolysis of the original to groups of lower
molecular weights. Bronnert finds that a previous hydration of the
cellulose--e.g. by the process of alkaline mercerisation and removal of
the alkali by washing--enables the zinc chloride to effect its
dissolution by digestion in the cold. (U.S. patent, 646,799/1900. See
also p. 59.)

_Industrial applications._--(a) _Vulcanised fibre_ is prepared by
treating paper with four times its weight of the concentrated aqueous
solution (65-75° B.), and in the resulting gelatinised condition is
worked up into masses, blocks, sheets, &c., of any required thickness.
The washing of these masses to remove the zinc salt is a very lengthy
operation.

To render the product waterproof the process of nitration is sometimes
superadded [D.R.P. 3181/1878]. Further details of manufacture are given
in Prakt. Handbuch d. Papierfabrikation, p. 1703 [C. Hofmann].

(b) _Calico-printing._--The use of the solution as a thickener or
colour vehicle, more especially as a substitute for albumen in pigment
styles, was patented by E. B. Manby, but the process has not been
industrially developed [E.P. 10,466/1894].

(c) _Artificial silk._--This is a refinement of the earlier
applications of the solution in spinning cellulose threads for
conversion into carbon filaments for electrical glow-lamps. This section
will be found dealt with on p. 59.

(p. 13) (2) ~Cuprammonium solution.~--The application of the solution of
cellulose in cuprammonium to the production of a fine filament in
continuous length, 'artificial silk,' has been very considerably studied
and developed in the period 1897-1900, as evidenced by the series of
patents of Fremery and Urban, Pauly, Bronnert, and others. The subject
will also be found dealt with on p. 58.

       *       *       *       *       *

(p. 15) ~Reactions of cellulose with iodine.~--In a recent paper, F.
Mylius deals with the reaction of starch and cellulose with iodine,
pointing out that the blue colouration depends upon the presence of
water and iodides. In absence of the latter, and therefore in presence
of compounds which destroy or absorb hydriodic acid--e.g. iodic
acid--there results a _brown_ addition product. The products in question
have the characteristics of _solid solutions_ of the halogen. (Berl.
Ber. 1895, 390.)

(24) ~Mercerisation~--Notwithstanding the enormous recent developments in
the industrial application of the mercerising reaction, there have been
no noteworthy contributions to the theoretical aspects of the subject.
The following abstract gives an outline of the scope of an important
technical work on the subject.


DIE MERCERISATION DER BAUMWOLLE.

PAUL GARDNER (Berlin: 1898. J. Springer).

~THE MERCERISATION OF COTTON.~

This monograph of some 150 pages is chiefly devoted to the patent
literature of the subject. The chemical and physical modifications of
the cotton substance under the action of strong alkaline lye, were set
forth by Mercer in 1844-5, and there has resulted from subsequent
investigations but little increase in our knowledge of the fundamental
facts. The treatment was industrially developed by Mercer in certain
directions, chiefly (1) for preparing webs of cloth required to stand
considerable strain, and (2) for producing crêpon effects by local or
topical action of the alkali. But the results achieved awakened but a
transitory interest, and the matter passed into oblivion; so much so,
indeed, that a German patent [No. 30,966] was granted in 1884 to the
Messrs. Depouilly for crêpon effects due to the differential shrinkage
of fabrics under mercerisation, by processes and treatments long
previously described by Mercer. Such effects have had a considerable
vogue in recent years, but it was not until the discovery of the
lustreing effect resulting from the association of the mercerising
actions with the condition of strain or tension of the yarn or fabric
that the industry in 'mercerised' goods was started on the lines which
have led to the present colossal development. The merit of this
discovery is now generally recognised as belonging to Thomas and Prevost
of Crefeld, notwithstanding that priority of patent right belongs to the
English technologist, H. A. Lowe.

The author critically discusses the grounds of the now celebrated patent
controversy, arising out of the conflict of the claims of German patent
85,564/1895 of the former, and English patent 4452/1890 of the latter.
The author concludes that Lowe's specification undoubtedly describes the
lustreing effect of mercerising in much more definite terms than that of
Thomas and Prevost. These inventors, on the other hand, realised the
effect industrially, which Lowe certainly failed to do, as evidenced by
his allowing the patent to lapse. As an explanation of his failure, the
author suggests that Lowe did not sufficiently extend his observations
to goods made from Egyptian and other long-stapled cottons, in which
class only are the full effects of the added lustre obtained.

Following these original patents are the specifications of a number of
inventions which, however, are of insignificant moment so far as
introducing any essential variation of the mercerising treatment.

The third section of the work describes in detail the various mechanical
devices which have been patented for carrying out the treatment on yarn
and cloth.

The fourth section deals with the fundamental facts underlying the
process and effects summed up in the term 'mercerisation.' These are as
follows:--

(a) Although all forms of fibrous celluloses are similarly affected by
strong alkaline solutions, it is only the Egyptian and other
long-stapled cottons--i.e. the goods made from them--which under the
treatment acquire the special high lustre which ranks as 'silky.' Goods
made from American cottons acquire a certain 'finish' and lustre, but
the effects are not such as to have an industrial value--i.e. a value
proportional to the cost of treatment.

(b) The lustre is determined by exposing the goods to strong tension,
either when under the action of the alkali, or subsequently, but only
when the cellulose is in the special condition of hydration which is the
main chemical effect of the mercerising treatment.

(c) The degree of tension required is approximately that which opposes
the shrinkage in dimensions, otherwise determined by the action of the
alkali. The following table exhibits the variations of shrinkage of
Egyptian when mercerised without tension, under varying conditions as
regards the essential factors of the treatment--viz. (1) concentration
of the alkaline lye, (2) temperature, and (3) duration of action (the
latter being of subordinate moment):--

 _______________________________________________________________________
|               |             |             |                    |      |
| Concentration |             |             |                    |      |
| of lye (NaOH) |    5°B.     |    10°B.    |        15°B        | 25°B |
|               |   |    |    |   |    |    |      |      |      |      |
| Duration of   |   |    |    |   |    |    |      |      |      |      |
| action in     | 1 | 10 | 30 | 1 | 10 | 30 |   1  |  10  |  30  |      |
| minutes       |   |    |    |   |    |    |      |      |      |      |
|               |   |    |    |   |    |    |      |      |      |      |
| Temperatures  |   Percentage shrinkages (Egyptian yarns) as under:--  |
| as under:--   |   |    |    |   |    |    |      |      |      |      |
|  2°           | 0 |  0 |  0 | 1 |  1 |  1 | 12.2 | 15.2 | 15.8 | 19.2 |
| 18°           | 0 |  0 |  0 | 0 |  0 |  0 |  8.0 |  8.8 | 11.8 | 19.8 |
| 30°           | 0 |  0 |  0 | 0 |  0 |  0 |  4.6 |  4.6 |  6.0 | 19.0 |
| 80°           | 0 |  0 |  0 | 0 |  0 |  0 |  3.5 |  3.5 |  9.8 | 13.4 |
|_______________|___|____|____|___|____|____|______|______|______|______|
 _______________________________________________________________________
|               |             |                    |                    |
| Concentration |             |                    |                    |
| of lye (NaOH) |     25°B    |        30°B        |        35°B        |
|               |      |      |      |      |      |      |      |      |
| Duration of   |      |      |      |      |      |      |      |      |
| action in     |  10  |  30  |   1  |  10  |  30  |   1  |  10  |  30  |
| minutes       |      |      |      |      |      |      |      |      |
|               |      |      |      |      |      |      |      |      |
| Temperatures  |   Percentage shrinkages (Egyptian yarns) as under:--  |
| as under:--   |      |      |      |      |      |      |      |      |
|  2°           | 19.8 | 21.5 | 22.7 | 22.7 | 22.7 | 24.2 | 24.5 | 24.7 |
| 18°           | 20.1 | 21.0 | 21.2 | 22.0 | 22.3 | 23.5 | 23.8 | 24.7 |
| 30°           | 19.5 | 19.0 | 18.5 | 19.5 | 19.8 | 20.7 | 21.0 | 21.1 |
| 80°           | 13.7 | 14.2 | 15.0 | 15.1 | 15.5 | 15.0 | 15.2 | 15.4 |
|_______________|______|______|______|______|______|______|______|______|

The more important general indications of the above results are--(1) The
mercerisation action commences with a lye of 10°B., and increases with
increased strength of the lye up to a maximum at 35°B. There is,
however, a relatively slight increase of action with the increase of
caustic soda from 30-40°B. (2) For optimum action the temperature should
not exceed 15-20°C. (3) The duration of action is of proportionately
less influence as the concentration of the lye increases. As the maximum
effect is attained the action becomes practically instantaneous, the
only condition affecting it being that of penetration--i.e. actual
contact of cellulose and alkali.

(d) The question as to whether the process of 'mercerisation' involves
chemical as well as physical effects is briefly discussed. The author is
of opinion that, as the degree of lustre obtained varies with the
different varieties of cotton, the differentiation is occasioned by
differences in chemical constitution of these various cottons. The
influence of the chemical factors is also emphasised by the increased
dyeing capacity of the mercerised goods, which effect, moreover, is
independent of those conditions of strain or tension under mercerisation
which determine lustre. It is found in effect that with a varied range
of dye stuffs a given shade is produced with from 10 to 30 p.ct. less
colouring matter than is required for the ordinary, i.e. unmercerised,
goods.

In reference to the constants of strength and elasticity, Buntrock gives
the following results of observations upon a 40^{5} twofold yarn, five
threads of 50 cm. length being taken for each test(Prometheus, 1897, p.
690): (a) the original yarn broke under a load of 1440 grms.; (b)
after mercerisation without tension the load required was 2420 grms.;
(c) after mercerisation under strain, 1950 grms. Mercerisation,
therefore, increases the strength of the yarn from 30 to 66 p.ct., the
increase being lessened proportionately to the strain accompanying
mercerisation. _Elasticity_, as measured by the extension under the
breaking load, remains about the same in yarns mercerised under strain,
but when allowed to shrink under mercerisation there is an increase of
30-40 p.ct. over the original.

The _change of form_ sustained by the individual fibres has been studied
by H. Lange [Farberzeitung, 1898, 197-198], whose microphotographs of
the cotton fibres, both in length and cross-section, are reproduced. In
general terms, the change is from the flattened riband of the original
fibre to a cylindrical tube with much diminished and rounded central
canal. The effect of strain under mercerisation is chiefly seen in the
contour of the surface, which is smooth, and the obliteration at
intervals of the canal. Hence the increased transparency and more
complete reflection of the light from the surface, and the consequent
approximation to the optical properties of the silk fibre.

The work concludes with a section devoted to a description of the
various practical systems of mercerisation of yarns in general practice
in Germany, and an account of the methods adopted in dyeing the
mercerised yarns.


RESEARCHES ON MERCERISED COTTON.

A. FRAENKEL and P. FRIEDLAENDER (Mitt. k.-k. Techn. Gew. Mus., Wien,
1898, 326).

The authors, after investigation, are inclined to attribute the lustre
of mercerised cotton to the absence of the cuticle, which is destroyed
and removed in the process, partly by the chemical action of the alkali,
and partly by the stretching at one or other stage of the process. The
authors have investigated the action of alcoholic solutions of soda
also. The lustre effects are not obtained unless the action of water is
associated.

In conclusion, the authors give the following particulars of breaking
strains and elasticity:--

--------------------------------------------------------------------------
Treatment                 | Experiments | Breaking strain |  Elasticity
--------------------------------------------------------------------------
                          |             |                 |  Elongation
                          |             |     Grammes     |  in mm.
                          |             |                 |
Cotton unmercerised.      |       1     |       360       |   20
                          |       2     |       356       |   20
                          |       3     |       360       |   22
                          |             |                 |
Mercerised with           |             |                 |
  Soda 35°B.              |       1     |       530       |   44
                          |       2     |       570       |   40
                          |       3     |       559       |   35
                          |             |                 |
  Alcoholic soda 10 p.ct. |       1     |       645       |   24
    cold                  |       2     |       600       |   27
                          |       3     |       610       |   33
                          |             |                 |
  Alcoholic soda 10 p.ct. |       5     |       740       |   33
    hot                   |       2     |       730       |   38
                          |       3     |       690       |   30
--------------------------------------------------------------------------

FOOTNOTES:

[2] This and other similar references are to the matter of the original
volume (1895).




SECTION II. SYNTHETICAL DERIVATIVES--SULPHOCARBONATES AND ESTERS


(p. 25) ~Cellulose sulphocarbonate.~--Further investigations of the
reaction of formation as well as the various reactions of decomposition
of the compound, have not contributed any essential modification or
development of the subject as originally described in the author's first
communications. A large amount of experimental matter has been
accumulated in view of the ultimate contribution of the results to the
general theory of colloidal solutions. But viscose is a complex product
and essentially variable, through its pronounced tendency to progressive
decomposition with reversion of the cellulose to its insoluble and
uncombined condition. The solution for this reason does not lend itself
to exact measurement of its physical constants such as might elucidate
in some measure the progressive molecular aggregation of the cellulose
in assuming spontaneously the solid (hydrate) form. Reserving the
discussion of these points, therefore, we confine ourselves to recording
results which further elucidate special points.

_Normal and other celluloses._--We may certainly use the sulphocarbonate
reaction as a means of defining a normal cellulose. As already pointed
out, cotton cellulose passes quantitatively through the cycle of
treatments involved in solution as sulphocarbonate and decomposition of
the solution with regeneration as structureless or amorphous cellulose
(hydrate).

Analysis of this cellulose shows a fall of carbon percentage from 44.4
to 43.3, corresponding with a change in composition from
C_{6}H_{10}O_{5} to 4C_{6}H_{10}O_{5}.H_{2}O. The partial hydrolysis
affects the whole molecule, and is limited to this effect, whereas, in
the case of celluloses of other types, there is a fractionation of the
mass, a portion undergoing a further hydrolysis to compounds of lower
molecular weight and permanently soluble. Thus in the case of the wood
celluloses the percentage recovered from solution as viscose is from 93
to 95 p.ct. It is evident that these celluloses are not homogeneous. A
similar conclusion results from the presence of furfural-yielding
compounds with the observation that the hydrolysis to soluble
derivatives mainly affects these derivatives. In the empirical
characterisation of a normal cellulose, therefore, we may include the
property of quantitative regeneration or recovery from its solution as
sulphocarbonate.

In the use of the word 'normal' as applied to a 'bleached' cotton, we
have further to show in what respects the sulphocarbonate reaction
differentiates the bleached or purified cotton cellulose from the raw
product. The following experiments may be cited: Specimens of American
and Egyptian cottons in the raw state, freed from mechanical, i.e.
non-fibrous, impurities, were treated with a mercerising alkali, and the
alkali-cotton subsequently exposed to carbon disulphide. The product of
reaction was further treated as in the preparation of the ordinary
solution; but in place of the usual solution, structureless and
homogeneous, it was observed to retain a fibrous character, and the
fibres, though enormously swollen, were not broken down by continued
vigorous stirring. After large dilution the solutions were filtered, and
the fibres then formed a gelatinous mass on the filters. After
purification, the residue was dried and weighed. The American cotton
yielded 90.0 p.ct., and the Egyptian 92.0 p.ct. of its substance in the
form of this peculiar modification. The experiment was repeated,
allowing an interval of 24 hours to elapse between the conversion into
alkali-cotton and exposure of this to the carbon disulphide. The
quantitative results were identical.

There are many observations incidental to chemical treatments of cotton
fabrics which tend to show that the bleaching process produces other
effects than the mere removal of mechanical impurities. In the
sulphocarbonate reaction the raw cotton, in fact, behaves exactly as a
compound cellulose. Whether the constitutional difference between raw
and bleached cotton, thus emphasised, is due to the group of components
of the raw cotton, which are removed in the bleaching process, or to
internal constitutional changes determined by the bleaching treatments,
is a question which future investigation must decide.

_The normal sulphocarbonate (viscose)._--In the industrial applications
of viscose it is important to maintain a certain standard of composition
as of the essential physical properties of the solution, notably
viscosity. It may be noted first that, with the above-mentioned
exception, the various fibrous celluloses show but slight differences in
regard to all the essential features of the reactions involved. In the
mercerising reaction, or alkali-cellulose stage, it is true the
differences are considerable. With celluloses of the wood and straw
classes there is a considerable conversion into soluble
alkali-celluloses. If treated with water these are dissolved, and on
weighing back the cellulose, after thorough washing, treatment with
acid, and finally washing and drying, it will be found to have lost from
15 to 20 p.ct. in weight. The lower grade of celluloses thus dissolved
are only in part precipitated in acidifying the alkaline solution. On
the other hand, after conversion into viscose, the cellulose when
regenerated re-aggregates a large proportion of these lower grade
celluloses, and the final loss is as stated above, from 5 to 7 p.ct.
only.

Secondly, it is found that all the conditions obtaining in the
alkali-cellulose stage affect the subsequent viscose reaction and the
properties of the final solution. The most important are obviously the
proportion of alkali to cellulose and the length of time they are in
contact before being treated with carbon disulphide. An excess of
alkali beyond the 'normal' proportion--viz. 2NaOH per 1 mol.
C_{6}H_{10}O_{5}--has little influence upon the viscose reaction, but
lowers the viscosity of the solution of the sulphocarbonate prepared
from it. But this effect equally follows from addition of alkali to the
viscose itself. The alkali-cellulose changes with age; there is a
gradual alteration of the molecular structure of the cellulose, of which
the properties of the viscose when prepared are the best indication.
There is a progressive loss of viscosity of the solution, and a
corresponding deterioration in the structural properties of the
cellulose when regenerated from it--especially marked in the film form.
In regard to viscosity the following observations are typical:--

     (a) A viscose of 1.8 p.ct. cellulose prepared from an
     alkali-cellulose (cotton) fourteen days old.

     (b) Viscose of 1.8 p.ct. cellulose from an alkali-cellulose
     (cotton) three days old.

     (c) Glycerin diluted with 1/3 vol. water.

                                        a       b       b          c
                                                    Diluted with
                                                    equal vol.
                                                      water
Times of flow of equal volumes from    112     321     103        170
  narrow orifice in seconds

Similarly the cellulose in reverting to the solid form from these
'degraded' solutions presents a proportionate loss of cohesion and
aggregating power expressed by the inferior strength and elasticity of
the products. Hence, in the practical applications of the product where
the latter properties are of first importance, it is necessary to adopt
normal standards, such as above indicated, and to carefully regulate all
the conditions of treatment in each of the two main stages of reaction,
so that a product of any desired character may be invariably obtained.

Incidentally to these investigations a number of observations have been
made on the alkali-cellulose (cotton) after prolonged storage in closed
vessels. It is well known that starch undergoes hydrolysis in contact
with aqueous alkalis of a similar character to that determined by acids
[Béchamp, Annalen, 100, 365]. The recent researches of Lobry de Bruyn
[Rec. Trav. Chim. 14, 156] upon the action of alkaline hydrates in
aqueous solution on the hexoses have established the important fact of
the resulting mobility of the CO group, and the interchangeable
relationships of typical aldoses and ketoses. It was, therefore, not
improbable that profound hydrolytic changes should occur in the
cellulose molecule when kept for prolonged periods as alkali-cellulose.

We may cite an extreme case. A series of products were examined after
12-18 months' storage. They were found to contain only 3-5 p.ct.
'soluble carbohydrates'; these were precipitated by Fehling's solution
but without reduction on boiling. They were, therefore, of the cellulose
type. On acidifying with sulphuric acid and distilling, traces only of
volatile acid were produced. It is clear, therefore, that the change of
molecular weight of the cellulose, the disaggregation of the undoubtedly
large molecule of the original 'normal' cellulose--which effects are
immediately recognised in the viscose reactions of such products--are of
such otherwise limited character that they do not affect the
constitution of the unit groups. We should also conclude that the
cellulose type of constitution covers a very wide range of minor
variations of molecular weight or aggregation.

The resistance of the normal cellulose to the action of alkalis under
these hydrolysing conditions should be mentioned in conjunction with the
observations of Lange, and the results of the later investigations of
Tollens, on its resistance to 'fusion' with alkaline hydrates at high
temperatures (180°). The degree of resistance has been established only
on the empirical basis of weighing the product recovered from such
treatment. The product must be investigated by conversion into typical
cellulose derivatives before we can pronounce upon the constitutional
changes which certainly occur in the process. But for the purpose of
this discussion it is sufficient to emphasise the extraordinary
resistance of the normal cellulose to the action of alkalis, and to
another of the more significant points of differentiation from starch.

_Chemical constants of cellulose sulphocarbonate (solution)._--In
investigations of the solutions we make use of various analytical
methods, which may be briefly described, noting any results bearing upon
special points.

_Total alkali._--This constant is determined by titration in the usual
way. The cellulose ratio, C_{6}H_{10}O_{5} : 2NaOH, is within the
ordinary error of observation, 2 : 1 by weight. A determination of alkali
therefore determines the percentage of cellulose.

_Cellulose_ may be regenerated in various ways--viz. by the action of
heat, of acids, of various oxidising compounds. It is purified for
weighing by boiling in neutral sulphite of soda (2 p.ct. solution) to
remove sulphur, and in very dilute acids (0.33 p.ct. HCl) to decompose
residues of 'organic' sulphur compounds. It may also be treated with
dilute oxidants. After weighing it may be ignited to determine residual
inorganic compounds.

_Sulphur._--It has been proved by Lindemann and Motten [Bull. Acad. R.
Belg. (3), 23, 827] that the sulphur of sulphocarbonates (as well as of
sulphocyanides) is fully oxidised (to SO_{3}) by the hypochlorites
(solutions at ordinary temperatures). The method may be adapted as
required for any form of the products or by-products of the viscose
reaction to be analysed for _total sulphur_.

The sulphur present in the form of dithiocarbonates, including the
typical cellulose xanthogenic acid, is approximately isolated and
determined as CS_{2} by adding a zinc salt in excess, and distilling off
the carbon disulphide from a water bath. From freshly prepared solutions
a large proportion of the disulphide originally interacting with the
alkali and cellulose is recovered, the result establishing the general
conformity of the reaction to that typical of the alcohols. On keeping
the solutions there is a progressive interaction of the bisulphide and
alkali, with formation of trithiocarbonates and various sulphides. In
decomposing these products by acid reagents hydrogen sulphide and free
sulphur are formed, the estimation of which presents no special
difficulties.

In the spontaneous decomposition of the solution a large proportion of
the sulphur resumes the form of the volatile disulphide. This is
approximately measured by the loss in total sulphur in the following
series of determinations, in which a viscose of 8.5 p.ct. strength
(cellulose) was dried down as a thin film upon glass plates, and
afterwards analysed:

(a) Proportion of sulphur to cellulose (100 pts.) in original.
(b) After spontaneous drying at ordinary temperature.
(c) After drying at 40°C.
(d) As in (c), followed, by 2 hours' heating at 98°.
(e) As in (c), followed by 5 hours' heating at 98°.

                          a     b     c     d     e
         Total sulphur   40.0  25.0  31.0  23.7  10.4

The dried product in (b) and (c) was entirely resoluble in water; in
(d) and (e), on the other hand, the cellulose was fully regenerated,
and obtained as a transparent film.

_Iodine reaction._--Fresh solutions of the sulphocarbonate show a fairly
constant reaction with normal iodine solution. At the first point, where
the excess of iodine visibly persists, there is complete precipitation
of the cellulose as the bixanthic sulphide; and this occurs when the
proportion of iodine added reaches 3I_{2} : 4Na_{2}O, calculated to the
total alkali.

_Other decompositions._--The most interesting is the interaction which
occurs between the cellulose xanthogenate and salts of ammonia, which is
taken advantage of by C. H. Stearn in his patent process of spinning
artificial threads from viscose. The insoluble product which is formed
in excess of the solution of ammonia salt is free from soda, and
contains 9-10 p.ct. total sulphur. The product retains its solubility in
water for a short period. The solution may be regarded as containing the
ammonium cellulose xanthate. This rapidly decomposes with liberation of
ammonia and carbon disulphide, and separation of cellulose (hydrate). As
precipitated by ammonium-chloride solution the gelatinous thread
contains 15 p.ct. of cellulose, with a sp.gr. 1.1. The process of
'fixing'--i.e. decomposing the xanthic residue--consists in a short
exposure to the boiling saline solution. The further dehydration, with
increase of gravity and cellulose content, is not considerable. The
thread in its final air-dry state has a sp.gr. 1.48.

       *       *       *       *       *

~Cellulose Benzoates.~--These derivatives have been further studied by the
authors. The conditions for the formation of the monobenzoate
[C_{6}H_{9}O_{4}.O.CO.Ph] are very similar to those required for the
sulphocarbonate reaction. The fibrous cellulose (cotton), treated with a
10 p.ct. solution NaOH, and subsequently with benzoyl chloride, gives
about 50 p.ct. of the theoretical yield of monobenzoate. Converted by 20
p.ct. solution NaOH into alkali-cellulose, and with molecular
proportions as below, the following yields were obtained:--

                                                              Calc. for
                                                             Monobenzoate
(a) C_{6}H_{10}O_{5} : 2.0-2.5 NaOH : C_{6}H_{5}.COCl--       150.8}
                                                                   }164.0
(b) C_{6}H_{10}O_{5} : 2.0-2.5 NaOH : 1.5 mol. C_{6}H_{5}COCl 159.0}

An examination of (a) showed that some dibenzoate (about 7 p.ct.) had
been formed. The product () was exhaustively treated with cuprammonium
solution, to which it yielded about 20 p.ct. of its weight, which was
therefore unattacked cellulose.

Under conditions as above, but with 2.5 mol. C_{6}H_{5}COCl, a careful
comparison was made of the behaviour of the three varieties of cotton,
which were taken in the unspun condition and previously fully bleached
and purified.

 ___________________________________________________________________
|                                |            |          |          |
|                                | Sea Island | Egyptian | American |
|________________________________|____________|__________|__________|
|                                |            |          |          |
| Aggregate yield of benzoate    |   153      |  148     |  152     |
| Moisture in air dry state      |     5.28   |    5.35  |    5.15  |
| Proportion of dibenzoate p.ct. |     8.30   |   13.70  |    9.4   |
| Yield of cellulose by          |    58.0    |   54.0   |   58.3   |
|   saponification               |            |          |          |
|________________________________|____________|__________|__________|

It appears from these results that the benzoate reaction may proceed to
a higher limit (dibenzoate) in the case of Egyptian cotton. This would
necessarily imply a higher limit of 'mercerisation,' under equal
conditions of treatment with the alkaline hydrate. It must be noted that
in the conversion of the fibrous cellulose into these (still) fibrous
monobenzoates, there are certain mechanical conditions imported by the
structural features of the ultimate fibres. For the elimination of the
influence of this factor a large number of quantitative comparisons will
be necessary. The above results are therefore only cited as typical of a
method of comparative investigation, more especially of the still open
questions of the cause of the superior effects in mercerisation of
certain cottons (see p. 23). It is quite probable that chemical as well
as structural factors co-operate in further differentiating the cottons.

Further investigation of the influence upon the benzoate reaction, of
increase of concentration of the soda lye, used in the preliminary
alkali cellulose reaction, from 20 to 33 p.ct. NaOH, established (1)
that there is no corresponding increase in the benzoylation, and (2)
that this ester reaction and the sulphocarbonate reaction are closely
parallel, in that the degree and limit of reaction are predetermined by
the conditions of formation of the alkali cellulose.

_Monobenzoate_ prepared as above described is resistant to all solvents
of cellulose and of the cellulose esters, and is therefore freed from
cellulose by treatment with the former, and from the higher benzoate by
treatment with the latter. Several of these, notably pyridine, phenol
and nitrobenzene, cause considerable swelling and gelatinisation of the
fibres, but without solution.

_Structureless celluloses_ of the 'normal' type, and insoluble therefore
in alkaline lye, treated under similar conditions to those described
above for the fibrous celluloses, yield a higher proportion of
dibenzoate. The following determinations were made with the cellulose
(hydrate) regenerated from the sulphocarbonate:--

Mol. proportions of reagents          Yield       Dibenzoate p.ct.
C_{6}H_{10}O_{5} : 2NaOH : 2BzCl        145             34.7
  [Caustic soda at 10 per cent. NaOH]

C_{6}H_{10}O_{5} : 4NaOH : 2BzCl        162             62.7
  [Caustic soda at 20 per cent. NaOH]

_Limit of reaction._--The cellulose in this form having shown itself
more reactive, it was taken as the basis for determining the maximum
proportion of OH groups yielding to this later reaction. The systematic
investigations of Skraup [Monatsh. 10, 389] have determined that as
regards the interacting groups the molecular proportions 1 OH : 7 NaOH :
5 BzCl, ensure complete or maximum esterification. The maximum of OH
groups in cellulose being 4, the reagents were taken in the proportion
C_{6}H_{10}O_{5} : 4 [7 NaOH : 5 BzCl]. The yield of crude product, after
purifying as far as possible from the excess of benzoic acid, was 240
p.ct. [calculated for dibenzoate 227 p.ct.]. On further investigating
the crude product by treatment with solvents, it was found to have still
retained benzoic acid. There was also present a proportion of only
partially attacked cellulose (monobenzoate). The soluble benzoate
amounted to 90 p.ct. of the product. It may be generally concluded that
the dibenzoate represents the normal maximum but that with the hydrated
and partly hydrolysed cellulose molecule, as obtained by regeneration
from the sulphocarbonate, other OH groups may react, but they are only a
fractional proportion in relation to the unit group C_{6}H_{10}O_{5}. In
this respect again there is a close parallelism between the
sulphocarbonate and benzoyl-ester reactions.

_The dibenzoate_, even when prepared from the fibrous celluloses, is
devoid of structure, and its presence in admixture with the fibrous
monobenzoate is at once recognised as it constitutes a structureless
incrustation. Under the microscope its presence in however minute
proportion is readily observed. As stated it is soluble in certain of
the ordinary solvents of the cellulose esters, e.g. chloroform, acetic
acid, nitrobenzene, pyridine, and phenol. It is not soluble in ether or
alcohol.

_Hygroscopic moisture of benzoates._--The crude monobenzoate retains
5.0-5.5 p.ct. moisture in the air-dry condition. After removal of the
residual cellulose this is reduced to 3.3 p.ct. under ordinary
atmospheric conditions. The purified dibenzoates retain 1.6 p.ct. under
similar conditions.

_Analysis of benzoates._--On saponification of these esters with
alcoholic sodium hydrate, anomalous results are obtained. The acid
numbers, determined by titration in the usual way, are 10-20 p.ct. in
excess of the theoretical, the difference increasing with the time of
boiling. Similarly the residual cellulose shows a deficiency of 5-9
p.ct.

It is by no means improbable that in the original ester reaction there
is a constitutional change in the cellulose molecule causing it to break
down in part under the hydrolysing treatment with formation of acid
products. This point is under investigation. Normal results as regards
acid numbers, on the other hand, are obtained by saponification with
sodium ethylate in the cold, the product being digested with the
half-saturated solution for 12 hours in a closed flask.

The following results with specimens of mono- and dibenzoate, purified,
as far as possible, may be cited:

           Combustion results           Saponification results
                      Calc.     C_{6}H_{5}.COOH  Calc.  Cellulose  Calc.
Monobenzoate  C 56.60  58.65}
              H  5.06   5.26}       46.0          45.9    58.0     60.8

Dibenzoate    C 63.10  64.86}
              H  3.40   4.86}       65.5          66.6    34.3     40.3

The divergence of the numbers, especially for the dibenzoate, in the
case of the hydrogen, and yield of cellulose on hydrolysis are
noteworthy. They confirm the probability of the occurrence of secondary
changes in the ester reactions.

_Action of nitrating acid upon the benzoates._--From the benzoates above
described, mixed nitro-nitric esters are obtained by the action of the
mixture of nitric and sulphuric acids. The residual OH groups of the
cellulose are esterified and substitution by an NO_{2} group takes place
in the aromatic residue, giving a mixed nitric nitrobenzoic ester. The
analysis of the products points to the entrance of 1 NO_{2} group in the
benzoyl residue in either case; in the cellulose residue 1 OH readily
reacts. Higher degrees of nitration are attained by the process of
solution in concentrated nitric acid and precipitation by pouring into
sulphuric acid. In describing these mixed esters we shall find it
necessary to adopt the C_{12} unit formula.

In analysing these products we have employed the Dumas method for _total
nitrogen_. For the O.NO_{2} groups we have found the nitrometer and the
Schloesing methods to give concordant results. For the NO_{2} groups it
was thought that Limpricht's method, based upon reduction with stannous
chloride in acid solution (HCl), would be available. The quantitative
results, however, were only approximate, owing to the difficulty of
confining the reduction to the NO_{2} groups of the nitrobenzoyl
residue. By reduction with ammonium sulphide the O.NO_{2} groups were
entirely removed as in the case of the cellulose nitrates; the NO_{2}
was reduced to NH_{2} and there resulted a cellulose amidobenzoate,
which was diazotised and combined with amines and phenols to form yellow
and red colouring matters, the reacting residue remaining more or less
firmly combined with the cellulose.

_Cellulose dinitrate-dinitrobenzoate, and cellulose
trinitrate-dinitrobenzoate._--On treating the fibrous benzoate--which is
a dibenzoate on the C_{12} basis--with the acid mixture under the usual
conditions, a yellowish product is obtained, with a yield of 140-142
p.ct. The nitrobenzoate is insoluble in ether alcohol, but is soluble in
acetone, acetic acid, and nitrobenzene. In purifying the product the
former solvent is used to remove any cellulose nitrates. To obtain the
maximum combination with nitroxy-groups, the product was dissolved in
concentrated nitric acid, and the solution poured into sulphuric acid.

The following analytical results were obtained (a) for the product
obtained directly from the fibrous benzoate and purified as indicated,
(b) for the product from the further treatment of (a) as described:

                       Found                   Calc. for
                    (a)       (b)       Dinitrate      Trinitrate
                                     dinitrobenzoate dinitrobenzoate
Total Nitrogen     7.84       8.97         7.99            9.24
O.NO_{2}  "        5.00       5.45         4.00            5.54
NO_{2} (Aromatic)  2.84       3.52         3.99            3.70

With the two benzoyl groups converted into nitro-benzoyl in each
product, the limit of the ester reaction with the cellulose residue is
reached at the third OH group.

The nitrogen in the amidobenzoate resulting from the reduction with
ammonium sulphide was 4.5 p.ct.--as against 5.0 p.ct. calculated. The
moisture retained by the fibrous nitrate--nitrobenzoate--in the air-dry
state was found to be 1.97 p.ct.

The product from the structureless dibenzoate or tetrabenzoate on the
C_{12} formula, was prepared and analysed with the following results:

                                              Calc. for
                                    Mononitrate tetranitrobenzoate
Total Nitrogen               6.76                7.25
O.NO_{2}  "                  1.30                1.45
NO_{2}    "  (Aromatic)      5.46                5.80

The results were confirmed by the yield of product, viz. 131 p.ct. as
against the calculated 136 p.ct. They afford further evidence of the
generally low limit of esterification of the cellulose molecule. From
the formation of a 'normal' tetracetate--i.e. octacetate of the C_{12}
unit--we conclude that 4/5 of the oxygen atoms are hydroxyl oxygen. Of
the 8 OH groups five only react in the mixed esters described above, and
six only in the case of the simple nitric esters. The ester reactions
are probably not simple, but accompanied by secondary reactions within
the cellulose molecule.

       *       *       *       *       *

(p. 34) ~Cellulose Acetates.~--In the first edition (p. 35) we have
committed ourselves to the statement that 'on boiling cotton with acetic
anhydride and sodium acetate no reaction occurs.' This is erroneous. The
error arises, however, from the somewhat vague statements of
Schutzenberger's researches which are current in the text-books [e.g.
Beilstein, 1 ed. p. 586] together with the statement that reaction only
occurs at elevated temperatures (180°). As a matter of fact, reaction
takes place at the boiling temperature of the anhydride. We have
obtained the following results with bleached cotton:

                                 Yield        Calc. for Monoacetate
                                           C_{6}H_{7}O_{4}O.C_{2}H_{3}O

Ester reaction                  121 p.ct.           125 p.ct.

                 {Cellulose       79.9                79.9
Saponification   {
                 {Acetic acid     29.9                29.4

This product is formed without apparent structural alteration of the
fibre. It is entirely insoluble in all the ordinary solvents of the
higher acetates. Moreover, it entirely resists the actions of the
special solvents of cellulose--e.g. zinc chloride and cuprammonium. The
compound is in other respects equally stable and inert. The hygroscopic
moisture under ordinary atmospheric conditions is 3.2 p.ct.

_Tetracetate._--This product is now made on the manufacturing scale: it
has yet to establish its industrial value.


NITRIRUNG VON KOHLENHYDRATEN.

W. WILL und P. LENZE (Berl. Ber., 1898, 68).

~NITRATES OF CARBOHYDRATES.~

(p. 38) The authors have studied the nitric esters of a typical series
of the now well-defined carbohydrates--pentoses, hexoses, both aldoses
and ketoses--bioses and trioses, the nitrates being prepared under
conditions designed to produce the highest degree of esterification.
Starch, wood, gum, and cellulose were also included in the
investigations. The products were analysed and their physical properties
determined. They were more especially investigated in regard to
temperatures of decomposition, which were found to lie considerably
lower than that of the cellulose nitrates. They also show marked and
variable instability at 50° C. A main purpose of the inquiry was to
throw light upon a probable cause of the instability of the cellulose
nitrates, viz. the presence of nitrates of hydrolysed products or
carbohydrates of lower molecular weight.

The most important results are these:

_Monoses._--The _aldoses_ are fully esterified, in the pentoses 4 OH, in
the hexoses 5 OH groups reacting. The pentose nitrates are comparatively
stable at 50°; the hexose nitrates on the other hand are extremely
unstable, showing a loss of weight of 30-40 p.ct. when kept 24 hours at
this temperature.

Xylose is differentiated by tending to pass into an anhydride form
(C_{5}H_{10}O_{5}-H_{2}O) under this esterification. When treated in
fact with the mixed acids, instead of by the process usually adopted by
the authors of solution in nitric acid and subsequent addition of the
sulphuric acid, it is converted into the dinitrate
C_{5}H_{6}O_{2}.(NO_{3})_{2}.

_Ketoses_ (C_{6}).--These are sharply differentiated from the corresponding
aldoses by giving _tri_nitrates C_{6}H_{7}O_{2}(NO_{3})_{3} instead
of _penta_nitrates, the remaining OH groups probably undergoing internal
condensation. The products are, moreover, _extremely stable_. It is also
noteworthy that levulose gave this same product, the trinitrate of the
anhydride (levulosan) by both methods of nitration (_supra_).

_The bisaccharides or bioses_ all give the octonitrates. The degree of
instability is variable. Cane-sugar gives a very unstable nitrate. The
lactose nitrate is more stable. Thus at 50° it loses only 0.7 p.ct. in
weight in eight days; at 75° it loses 1 p.ct. in twenty-four hours, but
with a rapid increase to 23 p.ct. in fifty-four hours. The maltose
octonitrate melts (with decomposition) at a relatively high temperature,
163°-164°. At 50°-75° it behaves much like the lactose nitrate.

_Trisaccharide._--Raffinose yielded the product

     C_{18}H_{21}O_{5}.(NO_{3})_{11}.

_Starch_ yields the hexanitrate (C_{12}) by both methods of nitration.
The product has a high melting and decomposing point, viz. 184°, and
when thoroughly purified is quite stable. It is noted that a yield of
157 p.ct. of this nitrate was obtained, and under identical conditions
cellulose yielded 170 p.ct.

_Wood gum_, from beech wood, gave a tetranitrate (C_{10} formula)
insoluble in all the usual solvents for this group of esters.

The authors point out in conclusion that the conditions of instability
and decomposition of the nitrates of the monose-triose series are
exactly those noted with the cellulose nitrates as directly prepared and
freed from residues of the nitrating acids. They also lay stress upon
the superior stability of the nitrates of the anhydrides, especially of
the ketoses.


NITRATED CARBOHYDRATES AS FOOD MATERIAL FOR MOULDS.

THOMAS BOKORNY (Chem. Zeit., 1896, 20, 985-986).

(p. 38) Cellulose trinitrate (nitrocellulose) will serve as a food
supply for moulds when suspended in distilled water containing the
requisite mineral matter and placed in the dark. The growth is rapid,
and a considerable quantity of the vegetable growth accumulates round
the masses of cellulose nitrate, but no growth is observed if mineral
matter is absent. Cellulose itself cannot act as a food supply, and it
seems probable that if glycerol is present cellulose nitrate is no
longer made use of.


NITRATION OF CELLULOSE, HYDROCELLULOSE, AND OXYCELLULOSE.

LEO VIGNON (Compt. rend., 1898, 126, 1658-1661).

(p. 38) Repeated treatment of cellulose, hydrocellulose, and
oxycellulose with a mixture of sulphuric and nitric acids in large
excess, together with successive analyses of the compounds produced,
showed that the final product of the reaction corresponded, in each
case, with the fixation of 11 NO groups by a molecule containing 24
atoms of carbon. On exposure to air, nitrohydrocellulose becomes yellow
and decomposes; nitro-oxycellulose is rather more stable, whilst
nitrocellulose is unaffected. The behaviour of these nitro-derivatives
with Schiff's reagent, Fehling's solution, and potash show that all
three possess aldehydic characters, which are most marked in the case of
nitro-oxycellulose. The latter also, when distilled with hydrochloric
acid, yields a larger proportion of furfuraldehyde than is obtained from
nitrocellulose and nitrohydrocellulose.

       *       *       *       *       *

~CELLULOSE NITRATES-EXPLOSIVES.~

(p. 38) The uses of the cellulose nitrates as a basis for explosives are
limited by their fibrous character. The conversion of these products
into the structureless homogeneous solid or semi-solid form has the
effect of controlling their combustion. The use of nitroglycerin as an
agent for this purpose gives the curious result of the admixture of two
high or blasting explosives to produce a new explosive capable of
extended use for military purposes. The leading representatives of this
class of propulsive explosives, or 'smokeless powders' are ballistite
and cordite, the technology of which will be found fully discussed in
special manuals of the subject. Since the contribution of these
inventions to the development of cellulose chemistry does not go beyond
the broad, general facts above mentioned, we must refer the reader for
technical details to the manuals in question.

There are, however, other means of arriving at structureless cellulose
nitrates. One of these has been recently disclosed, and as the results
involve chemical and technical points of novelty, which are dealt with
in a scientific communication, we reproduce the paper in question,
viz.:--


A RE-INVESTIGATION OF THE CELLULOSE NITRATES.

A. LUCK and C. F. CROSS (J. Soc. Chem. Ind., 1900).

The starting-point of these investigations was a study of the nitrates
obtained from the structureless cellulose obtained from the
sulphocarbonate (viscose). This cellulose in the form of a fine meal was
treated under identical conditions with a sample of pure cotton
cellulose, viz. digested for 24 hours in an acid mixture containing in
100 parts HNO_{3}--24 : H_{2}SO_{4}--70 : H_{2}O--6: the proportion of
acid to cellulose being 60 : 1--. After careful purification the
products were analysed with the following results:

                                    Soluble in
                       Nitrogen    Ether alcohol

Fibrous nitrate         13.31         4.3 p.ct.
Structureless nitrate   13.35         5.6  "

Examined by the 'heat test' (at 80°) and the 'stability test' (at 135°)
they exhibited the usual instability, and in equal degrees. Nor were the
tests affected by exhaustive treatment with ether, benzene, and alcohol.
From this it appears that the process of solution as sulphocarbonate and
regeneration of the cellulose, though it eliminates certain constituents
of an ordinary bleached cellulose, which might be expected to cause
instability, has really no effect in this direction. It also appears
that instability may be due to by-products of the esterification process
derived from the cellulose itself.

The investigation was then extended to liquids having a direct solvent
action on these higher nitrates, more especially acetone. It was
necessary, however, to avoid this solvent action proper, and having
observed that dilution with water in increasing proportions produced a
graduated succession of physical changes in the fibrous ester, we
carried out a series of treatments with such diluted acetones.
Quantities of the sample (A), purified as described, but still unstable,
were treated each with five successive changes of the particular liquid,
afterwards carefully freed from the acetone and dried at 40°C. The
products, which were found to be more or less disintegrated, were then
tested by the ordinary heat test, stability test, and explosion test,
with the results shown in the table on next page.

In this series of trials the sample 'A' was used in the condition of
pulp, viz. as reduced by the process of wet-beating in a Hollander. A
similar series was carried out with the guncotton in the condition in
which it was directly obtained from the ester reaction. The results were
similar to above, fully confirming the progressive character of the
stabilisation with increasing proportions of acetone. These results
prove that washing with the diluted acetone not only rendered the
nitrate perfectly stable, but that the product was more stable than that
obtained by the ordinary process of purification, viz. long-continued
boiling and washing in water. We shall revert to this point after
briefly dealing with the associated phenomenon of structural
disintegration. This begins to be well marked when the proportion of
acetone exceeds 80 p.ct. The optimum effect is obtained with mixtures of
90 to 93 acetone and 10 to 7 water (by volume). In a slightly diluted
acetone of such composition, the guncotton is instantly attacked, the
action being quite different from the gelatinisation which precedes
solution in the undiluted solvent. The fibrous character disappears, and
the product assumes the form of a free, bulky, still opaque mass, which
rapidly sinks to the bottom of the containing vessel. The disintegration
of the bulk of the nitrate is associated with

 __________________________________________________________________________
|                   |                        |             |       |       |
|                   |  Proportions by volume |             |       |       |
|                   |________________________| Temperature | Heat  | Heat  |
|                   |              |         |     of      | Test  | Test  |
|                   |   Acetone    | Water   |  Explosion  |  80°  | 134°  |
|___________________|______________|_________|_____________|_______|_______|
|                   |              |         |             |       |       |
|                 __|              |         |    Deg.     | Mins. | Mins. |
|                   |      20      |   80    |    137      |   3   |   4   |
|                   |      30      |   70    |    160      |   3   |   4   |
|                   |      40      |   60    |    180      |   7   |  18   |
|                   |              |         |             |       |   No  |
|                   |              |         |             |       | fumes |
|                   |              |         |             |       | after |
| From 'A' sample.  |     50       |   50    |    187.5    |  55   |  100  |
|                   |     60       |   40    |    187      |  45   |  100  |
|                   |     70       |   30    |    185      |  45   |  100  |
|                   |     80       |   20    |             |  50   |  100  |
|                 __|     92       |    8    |    185      |  50   |  100  |
|                   |  Structure-  |         |             |       |       |
|                   | less powder. |         |             |       |       |
|  "   'B' sample __|     50       |   50    |    183      |   35  |  100  |
|  "   'C' sample   |  Ordinary service      |    185      |   10  |   41  |
|                   |   guncotton            |             |       |       |
|___________________|______________|_________|_____________|_______|_______|

a certain solvent action, and on adding an equal bulk of water, the
dissolved nitrate for the most part is precipitated, at the same time
that the undissolved but disintegrated and swollen product undergoes
further changes in the direction of increase of hardness and density.
The product being now collected on a filter, freed from acetone by
washing with water and dried, is a hard and dense powder the fineness of
which varies according to the attendant conditions of treatment. With
the main product in certain cases there is found associated a small
proportion of nitrate retaining a fibrous character, which may be
separated by means of a fine sieve. On examining such a residue, we
found it to contain only 5.6 p.ct. N, and as it was insoluble in strong
acetone, it may be regarded as a low nitrate or a mixture of such with
unaltered cellulose. Confirming this we found that the product passing
through the sieve showed an increase of nitrogen to 13.43 p.ct. from the
13.31 p.ct. in the original. Tested by the heat test (50 minutes) and
stability test (no fumes after 100 minutes), we found the products to
have the characteristics previously noticed.

It is clear, therefore, that this specifically regulated action of
acetone produces the effects (a) of disintegration, and (b)
stabilisation. It remains to determine whether the latter effect was
due, as might be supposed, to the actual elimination of a compound or
group of compounds present in the original nitrate, and to be regarded
as the effective cause of instability. It is to be noted first that as a
result of the treatment with the diluted acetone and further dilution
after the specific action is completed, collecting the disintegrated
product on a filter and washing with water, the loss of weight sustained
amounts to 3 to 4 p.ct. This loss is due, therefore, to products
remaining dissolved in the filtrate--that is to say, in the much diluted
acetone. These filtrates are in fact opalescent from the presence of a
portion of nitrate in a colloidal (hydrated) form. On distilling off the
acetone, a precipitation is determined. The precipitates are nitrates of
variable composition, analysis showing from 9 to 12 p.ct. of nitric
nitrogen. The filtrate from these precipitates containing only
fractional residues of acetone still shows opalescence. On
long-continued boiling a further precipitation is determined, the
filtrates from which are clear. It was in this final clear filtrate that
the product assumed to cause the instability of the original nitrate
would be present. The quantity, however, is relatively so small that we
have only been able to obtain and examine it as residue from evaporation
to dryness. An exhaustive qualitative examination established a number
of negative characteristics, with the conclusion that the products were
not direct derivatives of carbohydrates nor aromatic compounds. On the
other hand the following positive points resulted. Although the original
diluted acetone extract was neutral to test papers, yet the residue was
acid in character. It contained combined nitric groups, fused below 200°
giving off acid vapours, and afterwards burning with a smoky flame. On
adding lead acetate to the original clear solution, a well-marked
precipitation was determined. The lead compounds thus isolated are
characteristic. They have been obtained in various ways and analysed.
The composition varies with the character of the solution in which the
lead compound is formed. Thus in the opalescent or milky solutions in
which a proportion of cellulose nitrate is held in solution or
semi-solution by the acetone still present, the lead acetate causes a
dense coagulation. The precipitates dried and analysed showed 16-20
p.ct. PbO and 11-9 p.ct. N. It is clear that the cellulose nitrates are
associated in these precipitates with the lead salts of the acid
compounds in question. When the latter are obtained from clear
solutions, i.e. in absence of cellulose nitrates, they contain 60-63
p.ct. PbO and 3.5 p.ct. N (obtained as NO).

In further confirmation of the conclusion from these results, viz. that
the nitrocelluloses with no tendency to combine with PbO are associated
with acid products or by-products of the ester reaction combining with
the oxide, the lead reagent was allowed to react in the presence of 90
p.ct. acetone. Water was added, the disintegrated mass collected, washed
with dilute acetic acid, and finally with water. Various estimations of
the PbO fixed in this way have given numbers varying from 2 to 2.5 p.ct.
Such products are perfectly stable. This particular effect of
stabilisation appears, therefore, to depend upon the combination of
certain acid products present in ordinary nitrocelluloses with metallic
oxides. In order to further verify this conclusion, standard specimens
of cellulose nitrates have been treated with a large number of metallic
salts under varying conditions of action. It has been finally
established (1) that the effects in question are more particularly
determined by treatment with salts of lead and zinc, and (2) that the
simplest method of treatment is that of boiling the cellulose nitrates
with dilute aqueous solutions of salts of these metals, preferably the
acetates. The following results may be cited, obtained by boiling a
purified 'service' guncotton (sample C) with a 1 p.ct. solution of lead
acetate and of zinc acetate respectively. After boiling 60 minutes the
nitrates were washed free from the soluble metallic salts, dried and
tested.

 __________________________________________________
|                          |           |           |
|                          | Heat Test | Heat Test |
|                          |   at 80°  |   at 134° |
|__________________________|___________|___________|
|                          |           |           |
| Original sample C        |     10    |    41     |
|Treated with lead acetate |     67    |    45     |
|     "       zinc    "    |     91    |    45     |
|__________________________|___________|___________|

In conclusion we may briefly resume the main points arrived at in these
investigations.

_Causes of instability of cellulose nitrates._--The results of our
experiments so far as to the causes of instability in cellulose nitrates
may be summed up as follows:--

(1) Traces of free nitrating acids, which can only occur in the finished
products through careless manufacture, will undoubtedly cause
instability, indicated strongly by the ordinary heat test at 80°, and to
a less extent by the heat test at 134°.

(2) Other compounds exist in more intimate association with the
cellulose nitrates causing instability which cannot be removed by
exhaustive washing with either hot or cold water, by digestion in cold
dilute alkaline solutions such as sodium carbonate, or by extracting
with ether, alcohol, benzene, &c.; these compounds, however, are soluble
in the solvents of highly nitrated cellulose such as acetone, acetic
ether, pyridine, &c., even when these liquids are so diluted with water
or other non-solvent liquids to such an extent that they have little or
no solvent action upon the cellulose nitrate itself. These solutions
containing the bodies causing instability are neutral to test paper, but
become acid upon evaporation by heating. (This probably explains the
presence of free acid when guncotton is purified by long-continued
boiling in water without any neutralising agent being present.)

(3) The bodies causing instability are products or by-products of the
original ester reaction, acid bodies containing nitroxy-groups, but
otherwise of ill-defined characteristics. They combine with the oxides
of zinc or lead, giving insoluble compounds. They are precipitated from
their solutions in diluted acetone upon the addition of soluble salts of
these metals.

(4) Cellulose nitrates are rendered stable either by eliminating these
compounds, or by combining them with the oxides of lead or zinc whilst
still in association with cellulose nitrates.

(5) Even the most perfectly purified nitrocellulose will slowly
decompose with formation of unstable acid products by boiling for a long
time in water. This effect is much more apparent at higher temperatures.

_Dense structureless or non-fibrous cellulose nitrates_ can be
industrially prepared (1) by nitrating the amorphous forms of cellulose
obtained from its solution as sulphocarbonate (viscose). The cellulose
in this condition reacts with the closest similarity to the original
fibrous cellulose; the products are similar in composition and
properties, including that of instability.

(2) By treating the fibrous cellulose nitrates with liquid solvents of
the high nitrate diluted with non-solvent liquids, and more especially
water. The optimum effect is a specific disintegration or breaking down
of their fibrous structure quite distinct from the gelatinisation which
precedes solution in the undiluted solvent, and occurring within narrow
limits of variation in the proportion of the diluting and non-solvent
liquid--for industrial work the most convenient solution to employ is
acetone diluted with about 10 p.ct. of water by volume.

The industrial applications of these results are the basis of English
patents 5286 (1898), 18,868 (1898), 18,233 (1898), Luck and Cross (this
Journal, 1899, 400, 787).

The structureless guncotton prepared as above described is of quite
exceptional character, and entirely distinct from the ordinary fibrous
nitrate or the nitrate prepared by precipitation from actual solution in
an undiluted solvent.[3] By the process described, the nitrate is
obtained at a low cost in the form of a very fine, dense, structureless,
white powder of great purity and stability, entirely free from all
mechanical impurities. The elimination of these mechanical impurities,
and also to a very great extent of coloured compounds contained in the
fibrous nitrate, makes the product also useful in the manufacture of
celluloids, artificial silk, &c., whilst its very dense form gives it a
great advantage over ordinary fibrous guncotton for use in shells and
torpedoes, and for the manufacture of gelatinised gunpowders, &c. It can
be compressed with ease into hard masses; and experiments are in
progress with a view of producing from it, in admixture with 'retaining'
ingredients, a military explosive manufactured by means of ordinary
black gunpowder machinery and processes.

_Manufacture of sporting powder._--The fact that the fibrous structure
of ordinary guncotton or other cellulose nitrate can be completely or
partially destroyed by treatment with diluted acetone and without
attendant solution, constitutes a process of value for the manufacture
of sporting powder having a base of cellulose nitrate of any degree of
nitration. The following is a description of the hardening process.

'Soft grains' are manufactured from ordinary guncotton or other
cellulose nitrate either wholly or in combination with other
ingredients, the process employed being the usual one of revolving in a
drum in the damp state and sifting out the grains of suitable size after
drying. These grains are then treated with diluted acetone, the degree
of dilution being fixed according to the hardness and bulk of the
finished grain it is desired to produce (J. Soc. Chem. Ind., 1899, 787).
Owing to the wide limits of dilution and corresponding effect, the
process allows of the production of either a 'bulk' or a 'condensed'
powder.

We prefer to use about five litres of the liquid to each one kilo. of
grain operated upon, as this quantity allows of the grains being freely
suspended in the liquid upon stirring. The grains are run into the
liquid, which is then preferably heated to the boiling-point for a few
minutes whilst the whole is gently stirred. Under this treatment the
grains assume a more or less rounded gelatinous condition according to
the strength of the liquid. There is, however, no solution of the
guncotton and practically no tendency of the grains to cohere. Each
grain, however, is acted upon _throughout_ and perfectly _equally_.
After a few minutes' treatment, water is gradually added, when the
grains rapidly harden. They are then freed from acetone and certain
impurities by washing with water, heating, and drying. The process is of
course carried out in a vessel provided with any means for gentle
stirring and heating, and with an outlet for carrying off the
volatilised solvent which is entirely recovered by condensation, the
grains parting with the acetone with ease.

_Stabilising cellulose nitrates._--The process is of especial value in
rendering stable and inert the traces of unstable compounds which always
remain in cellulose nitrate after the ordinary boiling and washing
process. It is of greatest value in the manufacture of collodion cotton
used for the preparation of gelatinous blasting explosives and all
explosives composed of nitroglycerin and cellulose nitrates. Such
mixtures seem peculiarly liable to decomposition if the cellulose
nitrate is not of exceptional stability (J. Soc. Chem. Ind., 1899,
787).


EMPLOI DE LA CELLULOSE POUR LA FABRICATION DE FILS BRILLANTS IMITANT LA
SOIE.

E. BRONNERT (1) (Rev. Mat. Col., 1900, September, 267).

V. ~USE OF CELLULOSE IN THE MANUFACTURE OF IMITATIONS OF SILK
(LUSTRA-CELLULOSE).~

(p. 45) _Introduction._--The problem of spinning a continuous thread of
cellulose has received in later years several solutions. Mechanically
all resolve themselves into the preparation of a structureless filtered
solution of cellulose or a cellulose derivative, and forcing through
capillary orifices into some medium which either absorbs or decomposes
the solvent. The author notes here that the fineness and to a great
extent the softness of the product depends upon the dimensions of the
capillary orifice and concentration of the solution. The technical idea
involved in the spinning of artificial fibres is an old one. Réaumur (2)
forecast its possibility, Audemars of Lausanne took a patent as early as
1855 (3) for transforming nitrocellulose into fine filaments which he
called 'artificial silk.' The idea took practical shape only when it
came to be used in connection with filaments for incandescent lamps. In
this connection we may mention the names of the patentees:--Swinburne
(4), Crookes, Weston (5), Swan (6), and Wynne and Powell (7). These
inventors prepared the way for Chardonnet's work, which has been
followed since 1888 with continually increasing success.

At this date the lustra-celluloses known may be divided into four
classes.

1. 'Artificial silks' obtained from the nitrocelluloses.

2. 'Lustra-cellulose' made from the solution of cellulose in
cuprammonium.

3. 'Lustra-cellulose' prepared from the solution of cellulose in
chloride of zinc.

4. 'Viscose silks,' by the decomposition of sulphocarbonate of cellulose
(Cross and Bevan).

GROUP 1. The early history of the Chardonnet process is discussed and
some incidental causes of the earlier failures are dealt with. The
process having been described in detail in so many publications the
reader is referred to these for details. [See Bibliography, (1) and (2),
(3) and (4).] The denitrating treatment was introduced in the period
1888-90 and of course altogether changed the prospects of the industry;
not only does it remove the high inflammability, but adds considerably
to softness, lustre, and general textile quality. In Table I will be
found some important constants for the nitrocellulose fibre; also the
fibre after denitration and the comparative constants for natural silk.

TABLE 1.

 _______________________________________________________________________
|                                          |           |                |
|                                          | Tenacity  |   Elasticity   |
|                                          | (grammes) | (% elongation) |
|__________________________________________|___________|________________|
|                                          |           |                |
| Nitrocellulose according to Chardonnet   |           |                |
|   German Patent No. 81,599               |    150    |       23       |
| The same after denitration               |    110    |        8       |
| Denitrated fibre moistened with water    |     25    |        --      |
| Nitrocellulose: Bronnert's German Patent |           |                |
|   No. 93,009                             |    125    |       28       |
| The same after denitration (dry)         |    115    |       13       |
| The same after denitration (wetted)      |     32    |       --       |
| Natural silk                             |    300    |       18       |
|__________________________________________|___________|________________|

     1. Tenacity is the weight in grammes required to break the
     thread.

     2. Elasticity is the elongation per cent. at breaking.

     The numbers are taken for thread of 100 deniers (450 metres of
     0.05 grammes = 1 denier). It must be noted that according to
     the concentration of the solution and variations in the process
     of denitration the constants for the yarn are subject to very
     considerable variation.

In regard to the manufacture a number of very serious difficulties have
been surmounted. First, instead of drying the nitrated cellulose, which
often led to fires, &c., it was found better to take it moist from the
centrifugal machine, in which condition it is dissolved (5). It was
next found that with the concentrated collodion the thread could be spun
direct into the air, and the use of water as a precipitant was thus
avoided.

With regard to denitration which is both a delicate and disagreeable
operation: none of the agents recommended to substitute the sulphydrates
have proved available. Of these the author mentions ferrous chloride
(6), ferrous chloride in alcohol (7), formaldehyde (8),
sulphocarbonates. The different sulphydrates (9) have very different
effects. The calcium compound tends to harden and weaken the thread. The
ammonia compound requires great care and is costly. The magnesium
compound works rapidly and gives the strongest thread. Investigations
have established the following point. In practice it is not necessary to
combine the saponification of cellulose ester with complete reduction of
the nitric acid split off. The latter requires eight molecules of
hydrogen sulphide per one molecule tetranitrocellulose, but with
precautions four molecules suffice. It is well known that the
denitration is nearly complete, traces only of nitric groups surviving.
Their reactions with diphenylamine allow a certain identification of
artificial silks of this class. Various other inventors, e.g. Du Vivier
(10), Cadoret (11), Lehner (12), have attempted the addition of other
substances to modify the thread. These have all failed. Lehner, who
persisted in his investigations, and with success, only attained this
success, however, by leaving out all such extraneous matters. Lehner
works with 10 p.ct. solutions; Chardonnet has continually aimed at
higher concentration up to 20 p.ct. Lehner has been able very much to
reduce his pressures of ejection in consequence; Chardonnet has had to
increase up to pressures of 60 k. per cm. and higher. The latter
involves very costly distributing apparatus. Lehner made next
considerable advance by the discovery of the fact that the addition of
sulphuric acid to the collodion caused increase of fluidity (13), which
Lehner attributes to molecular change. Chardonnet found similar results
from the addition of aldehyde and other reagents (14), but not such as
to be employed for the more concentrated collodions. The author next
refers to his discoveries (15) that alcoholic solutions of a number of
substances, organic and inorganic, freely dissolve the lower cellulose
nitrates. The most satisfactory of these substances is chloride of
calcium (16). It is noted that acetate of ammonia causes rapid changes
in the solution, which appear to be due to a species of hydrolysis. The
result is sufficiently remarkable to call for further investigation. The
chloride of calcium, it is thought possible, produces a direct
combination of the alcohol with a reactive group of the nitrocellulose.
The fluidity of this solution using one mol. CaCl_{2} per 1 mol.
tetranitrate (17) reaches a maximum in half an hour's heating at
60°-70°C. The fluidity is increased by starting from a cotton which has
been previously mercerised. After nitration there is no objection to a
chlorine bleach. Chardonnet has found on the other hand that in
bleaching before nitration there is a loss of spinning quality in the
collodion. The author considers that the new collodion can be used
entirely in place of the ordinary ether-alcohol collodion. With regard
to the properties of the denitrated products they fix all basic colours
without mordant and may be regarded as oxycellulose therefore. The
density of the thread is from 1.5 to 1.55. The thread of 100 deniers
shows a mean breaking strain of 120 grammes with an elasticity of 8-12
p.ct. The cardinal defect of these fibres is their property of
combination with water. Many attempts have been made to confer
water-resistance (18), but without success. Strehlenert has proposed the
addition of formaldehyde (19), but this is without result (20). In
reference to these effects of hydration, the author has made
observations on cotton thread, of which the following table represents
the numerical results:

                                                       Breaking Strain
                                                   Mean of 20 experiments

Skein of bleached cotton without treatment                 825
Skein of bleached cotton without treatment, but wetted     942
Ditto after conversion into hexanitrate, dry               884
The above, wetted                                          828
The cotton denitrated from above, dry                      529
The cotton denitrated as above and wetted                  206

The author considers that other patents which have been taken for
spinning nitrocellulose are of little practical account (21) and (22).
The same conclusion also applies to the process of _Langhans_, who
proposes to spin solutions of cellulose in sulphuric acid (23) (24) and
mixtures of sulphuric acid and phosphoric acid.

GROUP 2. _Lustra-cellulose._--Thread prepared by spinning solutions of
cellulose in cuprammonium.

This product is made by the Vereinigte Glanzstoff-Fabriken, Aachen,
according to a series of patents under the names of H. Pauly, M. Fremery
and Urban, Consortium mulhousien pour la fabrication de fils brillants,
E. Bronnert, and E. Bronnert and Fremery and Urban (1). The first patent
in this direction was taken by Despeissis in 1890 (2). It appears this
inventor died shortly after taking the patent (3) The matter was later
developed by Pauly (4) especially in overcoming the difficulty of
preparing a solution of sufficient concentration. (It is to be noted
that Pauly's patents rest upon a very slender foundation, being
anticipated in every essential detail by the previous patent of
Despeissis.) For this very great care is required, especially, first,
the condition of low temperature, and, secondly, a regulated proportion
of copper and ammonia to cellulose. The solution takes place more
rapidly if the cellulose has been previously oxidised. Such cellulose
gives an 8 p.ct. solution, and the thread obtained has the character of
an oxycellulose, specially seen in its dyeing properties. The best
results are obtained, it appears, by the preliminary mercerising
treatment and placing the alkali cellulose in contact with copper and
ammonia. (All reagents employed in molecular proportions.) The author
notes that the so-called hydrocellulose (Girard) (5) is almost insoluble
in cuprammonium, as is starch. It is rendered soluble by alkali
treatment.

GROUP 3. _Lustra-cellulose_ prepared by spinning a solution of cellulose
in concentrated chloride of zinc.

This solution has been known for a long time and used for making
filaments for incandescent lamps. The cellulose threads, however, have
very little tenacity. This is no doubt due to the conditions necessary
for forming the solution, the prolonged digestion causing powerful
hydrolysis (1). Neither the process of Wynne and Powell (2) nor that of
Dreaper and Tompkins (3), who have endeavoured to bring the matter to a
practical issue, are calculated to produce a thread taking a place as a
textile. The author has described in his American patent (4) a method of
effecting the solution in the cold, viz. again by first mercerising the
cellulose and washing away the caustic soda. This product dissolves in
the cold and the solution remains unaltered if kept at low temperature.
Experiments are being continued with these modifications of the process,
and the author anticipates successful results. The modifications having
the effect of maintaining the high molecular weight of the cellulose, it
would appear that these investigations confirm the theory of Cross and
Bevan that the tenacity of a film or thread of structureless regenerated
cellulose is directly proportional to the molecular weight of the
cellulose, i.e. to its degree of molecular aggregation (5).

GROUP 4. 'Viscose' silks obtained by spinning solutions of xanthate of
cellulose.

In 1892, Cross and Bevan patented the preparation of a new and curious
compound of cellulose, the thiocarbonate (1) (2) (3). Great hopes were
based upon this product at the time of its discovery. It was expected
to yield a considerable industrial and financial profit and also to
contribute to the scientific study of cellulose. The later patents of C.
H. Stearn (4) describe the application of viscose to the spinning of
artificial silk. The viscose is projected into solutions of chloride of
ammonium and washed in a succession of saline solutions to remove the
residual sulphur impurities. The author remarks that though it has a
certain interest to have succeeded in making a thread from this compound
and thus adding another to the processes existing for this purpose, he
is not of opinion that it shows any advance on the lustra-cellulose (2)
and (3). He also considers that the bisulphide of carbon, which must be
regarded as a noxious compound, is a serious bar to the industrial use
of the process, and for economic work he considers that the regeneration
of ammonia from the precipitating liquors is necessary and would be as
objectionable as the denitration baths in the collodion process. The
final product not being on the market he does not pronounce a finally
unfavourable opinion.

The author and the Vereinigte Glanzstoff-Fabriken after long
investigation have decided to make nothing but the lustra-cellulose (2)
and (3). A new factory at Niedermorschweiler, near Mulhouse, is
projected for this last production.


BIBLIOGRAPHY

_Introduction_

(1) Bull. de la Soc. industr. de Mulhouse, 1900.

(2) Réaumur, Mémoire pour servir à l'histoire des insectes, 1874, 1, p.
154.

(3) English Pat. No. 283, Feb. 6, 1855.

(4) Swinburne, Electrician, 18, 28, 1887, p. 256.

(5) Weston (Swinburne), Electrician, 18, 1887, p. 287. Eng. Pat. No.
22866, Sept. 12, 1882.

(6) German Pat. No. 3029. English Pat. No. 161780, April 28, 1884
(Swan).

(7) Wynne-Powell, English Pat. No. 16805, Dec. 22, 1884.


_Group I_

(1) German Pat No. 38368, Dec. 20, 1885. German Pat. No. 46125, March 4,
1888. German Pat. No. 56331, Feb. 6, 1890. German Pat. No. 81599, Oct.
11, 1893. German Pat. No. 56655, April 23, 1890. French Pat. No. 231230,
June 30, 1893.

(2) Industrie textile, 1899, 1892. Wyss-Noef, Zeitschrift für angewandte
Chemie, 1899, 30, 33. La Nature, Jan. 1, 1898, No. 1283. Revue générale
des sciences, June 30, 1898.

(3) German Pat. No. 46125, March 4, 1888. German Pat. No. 56655, April
23, 1890.

(4) Swan, English Pat. 161780, June 28, 1884. See also Béchamp, Dict. de
Chimie de Wurtz.

(5) German Pat. No. 81599, Oct 11, 1893.

(6) Béchamp, art. Cellulose, Dict. de Chimie de Wurtz, p. 781.

(7) Chardonnet, addit. March 3, 1897, to the French Pat. 231230, May 30,
1893.

(8) Knofler, French Pat. 247855, June 1, 1895. German Pat. 88556, March
28, 1894.

(9) Béchamp, art. Cellulose, Dict. de Chimie de Wurtz. Blondeau, Ann.
Chim. et Phys. (3), 1863, 68, p. 462.

(10) Revue industrielle, 1890, p. 194. German Pat. 52977, March 7, 1889.

(11) French Pat. 256854, June 2, 1896.

(12) German Pat. 55949, Nov. 9, 1889. German Pat. 58508, Sept. 16, 1890.
German Pat. 82555, Nov. 15, 1894.

(13) German Pat. 58508, Sept. 16, 1900.

(14) French Pat. 231230, June 30, 1893.

(15) German Pat. 93009, Nov. 19, 1895. French Pat. 254703, March 12,
1896. English Pat. 6858, March 28, 1896.

(16) American Pat. 573132, Dec. 15, 1896.

(17) This proportion is the most advantageous, and furnishes the best
liquid collodions that can be spun.

(18) French Pat. 259422, Sept. 3, 1896.

(19) English Pat. 22540, 1896.

(20) Application for German Pat. not granted, 4933 IV. 296, Mar. 16,
1897.

(21) German Pat. 96208, Feb. 10, 1897. Addit. Pat. 101844 and 102573,
Dec. 10, 1897.

(22) Oberle et Newbold, French Pat. 25828, July 22, 1896. Granquist,
Engl. applic. 2379, Nov. 28, 1899.

(23) German Pat. 72572, June 17, 1891.

(24) Voy. Stern, Ber., 28, ch. 462.


_Group II_

(1) German Pat. 98642, Dec. 1, 1897 (Pauly). French Pat. 286692, March
10, 1899, and addition of October 14, 1899 (Fremery and Urban). French
Pat. 286726, March 11, 1899, and addition of December 4, 1899. German
Pat. 111313, March 16, 1899 (Fremery and Urban). English Pat. 18884,
Sept. 19, 1899 (Bronnert). English Pat. 13331, June 27, 1899 (Consort.
mulhousien).

(2) French Pat. 203741, Feb. 12, 1890.

(3) The actual lapse of this patent is due to the death of Despeissis
shortly after it was taken.

(4) Without questioning the good faith of Pauly, it is nevertheless a
fact that the original patent remains as a document, and therefore that
the value of the Pauly patents is very questionable.

(5) Girard, Ann. Chim. et Phys, 1881 (5), 24, p. 337-384.


_Group III_

(1) Cross and Bevan, Cellulose, 1895, p. 8.

(2) English Pat. 16805, Dec. 22, 1884.

(3) English Pat. 17901, July 30, 1897.

(4) Bronnert, American Pat. 646799, April 3, 1900.

(5) Cross and Bevan, Cellulose, 1895, p. 12.


_Group IV_

(1) English Pat. 8700, 1892. German Pat. 70999, Jan. 13, 1893.

(2) English Pat. 4713, 1896. German Pat. 92590, Nov. 21, 1896.

(3) Comptes rendus (loc. cit.). Berichte, c. 9, 65a.

(4) English Pat. 1020, 1898. German Pat. 108511, Oct. 18, 1898.


~Artificial Silk--Lustra-cellulose.~

C. F. CROSS and E. J. BEVAN (J. Soc. Chem. Ind., 1896, 317).

The object of this paper is mainly to correct current statements as to
the artificial or 'cellulose silks' being explosive or highly
inflammable (ibid., 1895, 720). A specimen of the 'Lehner' silk was
found to retain only 0.19 p.ct. total nitrogen, showing that the
denitration is sufficiently complete to dispose of any suggestion of
high inflammability.

The product yielded traces only of furfural; on boiling with a 1 p.ct.
solution of sodium hydrate, the loss of weight was 9.14 p.ct.; but the
solution had no reducing action on Fehling's solution. The product in
denitration had therefore reverted completely to a cellulose (hydrate),
no oxy-derivative being present.

       *       *       *       *       *

The authors enter a protest against the term 'artificial silk' as
applied to these products, and suggest 'lustra-cellulose.'


DIE KÜNSTLICHE SEIDE-IHRE HERSTELLUNG, EIGENSCHAFTEN UND VERWENDUNG.

CARL SÜVERN, Berlin, 1900, J. Springer.

~ARTIFICIAL SILK--ITS PRODUCTION, PROPERTIES, AND APPLICATIONS.~

This work of some 130 pages is an important monograph on the subject of
the preparation of artificial cellulose threads--so far as the technical
elements of the problems involved are discussed and disclosed in the
patent literature. The first section, in fact, consists almost
exclusively of the several patent specifications in chronological order
and ranged under the sub-sections: (a) The Spinning of Nitrocellulose
(collodion); (b) The Spinning of other Solutions of Cellulose; (c)
The Spinning of Solutions of the Nitrogenous Colloids.

In the second section the author deals with the physical and chemical
proportions of the artificial threads.

_Chardonnet 'silk'_ is stated to have a mean diameter of 35µ, but with
considerable variations from the mean in the individual fibres; equally
wide variations in form are observed in cross-section. The general form
is elliptical, but the surface is marked by deep striæ, and the
cross-section is therefore of irregular outline. This is due to
irregular conditions of evaporation of the solvents, the thread being
'spun' into the air from cylindrical orifices of regulated dimensions.
Chardonnet states that when the collodion is spun into alcohol the
resultant thread is a perfect cylinder (Compt. rend. 1889, 108, 962).
The strength of the fibre is variously stated at from 50-80 p.ct. that
of 'boiled off' China tram; the true elasticity is 4-5 p.ct., the
elongation under the breaking strain 15-17 p.ct. The sp.gr. is 1.49,
i.e. 3-5 p.ct. in excess of boiled off silk.

_Lehner 'silk'_ exhibits the closest similarity to the Chardonnet
product. In cross-section it is seen to be more regular in outline, and
a round, pseudo-tubular form prevails, due to the conditions of
shrinkage and collapse of the fibre in parting with the solvents, and in
then dehydrating. The constants for 'breaking strain,' both in the
original and moistened condition, for elasticity, &c., are closely
approximate to those for the Chardonnet product.

_Pauly 'silk'._--The form of the ultimate fibres is much more regular
and the contour of the cross-section is smooth. The product shows more
resistance to moisture and to alkaline solutions.

_Viscose 'silk'_ is referred to in terms of a communication appearing in
'Papier-Zeitung,' 1898, 2416.

     In the above section the following publications are referred
     to: Chardonnet, 'Compt. rend.,' 1887, 105, 900; and 1889, 108,
     962; Silbermann, 'Die Seide,' 1897, v. 2, 143; Herzog,
     'Farber-Zeitung,' 1894/5, 49-50; Thiele, ibid. 1897, 133; O.
     Schlesinger, 'Papier-Zeitung,' 1895, 1578-81, 1610-12.


_Action of Reagents upon Natural and Artificial Silks._

1. _Potassium hydrate_ in solution of maximum concentration dissolves
the silks proper, (a) China silk on slight warming, (b) Tussah silk
on boiling. The cellulose 'silks' show swelling with discolouration, but
the fibrous character is not destroyed even on boiling.

2. _Potassium hydrate_ 40 p.ct. China silk dissolves completely at
65°-85°; Tussah silk swells considerably at 75° and dissolves at
100°-120°. The cellulose 'silks' are attacked with discolouration; at
140° (boiling-point of the solution) there is progressive solvent
action, but the action is incomplete. The Pauly product is most
resistant.

3. _Zinc chloride_, 40 p.ct. solution. Both the natural silks and
lustra-celluloses are attacked at 100°, and on raising the temperature
the further actions are as follows: China silk is completely dissolved
at 110-120°; Tussah silk at 130-135°; the collodion products at
140-145°; the Pauly product was again most resistant, dissolving at
180°.

4. _Alkaline cupric oxide_ (glycerin) solution was prepared by
dissolving 10 grs. of the sulphate in 100 c.c. water, adding 5 grs.
glycerin and 10 c.c. of 40 p.ct. KOH. In this solution the China silk
dissolved at the ordinary temperature; Tussah silk and the
lustra-celluloses were not appreciably affected.

5. _Cuprammonium solution_ was prepared by dissolving the precipitated
cupric hydrate in 24 p.ct. ammonia. In this reagent also the China silk
dissolved, and the Tussah silk as well as the lustra-celluloses
underwent no appreciable change.

6. _An ammoniacal solution of nickel oxide_ was prepared by dissolving
the precipitated hydrated oxide in concentrated ammonia. The China silk
was dissolved by this reagent; Tussah silk and the lustra-celluloses
entirely resisted its action.

7. _Fehling's solution_ is a solvent of the natural silks, but is
without action on the lustra-celluloses.

8. _Chromic acid_--20 p.ct. CrO_{3}--solution dissolves both the natural
silks and the lustra-celluloses at the boiling temperature of the
solution.

9. _Millon's reagent_, at the boiling solution, colours the natural
silks violet: the lustra-celluloses give no reaction.

10. _Concentrated nitric acid_ attacks the natural silks powerfully in
the cold; the lustra-celluloses dissolve on heating.

11. _Iodine solution_ (I in KI) colours the China silk a deep brown,
Tussah a pale brown; the celluloses from collodion are coloured at first
brown, then blue. The Pauly product, on the other hand, does not react.

12. _Diphenylamine sulphate._--A solution of the base in concentrated
sulphuric acid colours the natural silks a brown; the collodion 'silks'
give a strong blue reaction due to the presence of residual
nitro-groups. The Pauly product is not affected.

13. _Brucin sulphate_ in presence of concentrated sulphuric acid colours
the natural silks only slightly (brown); the collodion 'silks' give a
strong red colouration. The Pauly product again is without reaction.

14. _Water._--The natural silks do not soften in the mouth as do the
lustra-celluloses.

15. _Water of condition_ was determined by drying at 100°; the following
percentages resulted (a). The percentages of water (b) taken up from
the atmosphere after forty-three hours' exposure were:

                                   (a)        (b)
     China (raw) silk             7.97       2.24
     Tussah silk                  8.26       5.00

     Lustra-celluloses:

     Chardonnet (Besançon)       10.37       5.64
         "    Spreitenbach       11.17       5.77
     Lehner                      10.71       5.97
     Pauly                       10.04       6.94

16. _Behaviour on heating at 200°._--After two hours' heating at this
temperature the following changes were noted:

     China silk      Much discoloured (brown).
     Tussah silk     Scarcely affected.

Lustra-celluloses:

     Chardonnet   Converted into a blue-black charcoal, retaining the
     Lehner       form ofthe fibres.

     Pauly       A bright yellow-brown colouration, without carbonisation.

17. The _losses of weight_ accompanying these changes and calculated per
100 parts of fibre dried at 100° were:

     China silk       3.18
     Tussah silk      2.95

Lustra-celluloses:

     Chardonnet      33.70
     Lehner          26.56
     Pauly            1.61

18. _Inorganic constituents._--Determinations of the total ash gave for
the first five of the above, numbers varying from 1.0 to 1.7 p.ct. The
only noteworthy point in the comparison was the exceptionally small ash
of the Pauly product, viz. 0.096 p.ct.

19. _Total nitrogen._--The natural silks contain the 16-17 p.ct. N
characteristic of the proteids. The lustra-celluloses contain 0.05-0.15
p.ct. N which in those spun from collodion is present in the form of
nitric groups.

The points of chemical differentiation which are established by the
above scheme of comparative investigation are summed up in tabular form.

_Methods of dyeing._--The lustra-celluloses are briefly discussed. The
specific relationship of these forms of cellulose to the colouring
matters are in the main those of cotton, but they manifest in the
dye-bath the somewhat intensified attraction which characterises
mercerised cotton, or more generally the cellulose hydrates.

_Industrial applications_ of the lustra-celluloses are briefly noticed
in the concluding section of the book.

FOOTNOTES:

[3] With these products it is easy to observe that they have a definite
fusion point 5°-10° below the temperature of explosion.




SECTION III. DECOMPOSITIONS OF CELLULOSE SUCH AS THROW LIGHT ON THE
PROBLEM OF ITS CONSTITUTION


UEBER CELLULOSE.

G. BUMCKE und R. WOLFFENSTEIN (Berl. Ber., 1899, 2493).

(p. 54) _Theoretical Preface._--The purpose of these investigations is
the closer characterisation of the products known as 'oxycellulose' and
'hydracellulose,' which are empirical aggregates obtained by various
processes of oxidation and hydrolysis; these processes act concurrently
in the production of the oxycelluloses. The action of hydrogen peroxide
was specially investigated. An oxycellulose resulted possessing strongly
marked aldehydic characteristics. The authors commit themselves to an
explanation of this paradoxical result, i.e. the production of a body
of strongly 'reducing' properties by the action of an oxidising agent
upon the inert cellulose molecule (? aggregate) as due to the
_hydrolytic_ action of the peroxide: following Wurster (Ber. 22, 145),
who similarly explained the production of reducing sugars from cane
sugar by the action of the peroxide.

The product in question is accordingly termed _hydralcellulose_. By the
action of alkalis this is resolved into two bodies of alcoholic
(cellulose) and acid ('acid cellulose') characteristics respectively.
The latter in drying passes into a lactone. The acid product is also
obtained from cellulose by the action of alkaline lye (boiling 30 p.ct.
NaOH) and by solution in Schweizer's reagent.

It is considered probable that the cellulose nitrates are hydrocellulose
derivatives, and experimental evidence in favour of this conclusion is
supplied by the results of 'nitrating' the celluloses and their oxy- and
hydro- derivatives. Identical products were obtained.

_Experimental investigations._--The filter paper employed as 'original
cellulose,' giving the following numbers on analysis:

     C   44.56    44.29    44.53    44.56
     H    6.39     6.31     6.46     6.42

was exposed to the action of pure distilled H_{2}O_{2} at 4-60 p.ct.
strength, at ordinary temperatures until disintegrated: a result
requiring from nineteen to thirty days. The series of products gave the
following analytical results:

     C   43.61   43.61   43.46   43.89   44.0   43.87   43.92   43.81
     H    6.00    6.29    6.28    6.26    6.13   6.27    6.24    6.27

results lying between the requirements of the formulæ:

     5 C_{6}H_{10}O_{5}.H_{2}O  and  8 C_{6}H_{10}O_{5}.H_{2}O.

Hydrazones were obtained with 1.7-1.8 p.ct. N. Treated with caustic soda
solution the hydrazones were dissolved in part: on reprecipitation a
hydrazone of unaltered composition was obtained. The original product
shows therefore a uniform distribution of the reactive CO- groups.

The hydralcellulose boiled with Fehling's solution reduced 1/12 of the
amount required for an equal weight of glucose.

Digested with caustic soda solution it yielded 33 p.ct. of its weight of
the soluble 'acid cellulose.' This product was purified and analysed
with the following result: C 43.35 H 6.5. For the direct production of
the 'acid' derivative, cellulose was boiled with successive quantities
of 30 p.ct. NaOH until _dissolved_. It required eight treatments of one
hour's duration. On adding sulphuric acid to the solutions the product
was precipitated. Yield 40 p.ct. Analyses:

     C    43.8     43.8     43.7
     H     6.2      6.2      6.3

The cellulose reprecipitated from solution in Schweizer's reagent gave
similar analytical results:

     C    43.9    43.8    44.0
     H     6.5     6.3     6.4

_Conversion into nitrates._--The original cellulose, hydral- and acid
cellulose were each treated with 10 times their weight of HNO_{3} of
1.48 sp.gr. and heated at 85° until the solution lost its initial
viscosity.

The products were precipitated by water and purified by solution in
acetone from which two fractions were recovered, the one being
relatively insoluble in ethyl alcohol. The various nitrates from the
several original products proved to be of almost identical composition,

     C 32.0   H 4.2    N 8.8

with a molecular weight approximately 1350. The conclusion is that
these products are all derivatives of a 'hydralcellulose'
6C_{6}H_{10}O_{5}H_{2}O.


FORMATION OF FURFURALDEHYDE FROM CELLULOSE, OXYCELLULOSE, AND
HYDROCELLULOSE.

By LEO VIGNON (Compt. rend., 1898, 126, 1355-1358).

(p. 54) Hydrocellulose, oxycellulose, and 'reduced' cellulose, the last
named being apparently identical with hydrocellulose, were obtained by
heating carefully purified cotton wool (10 grams) in water (1,000 c.c.),
with (1) 65 c.c. of hydrochloric acid (1.2 sp.gr.), (2) 65 c.c. of
hydrochloric acid and 80 grams of potassium chlorate, (3) 65 c.c. of
hydrochloric acid and 50 grams of stannous chloride. From these and some
other substances, the following percentage yields of furfuraldehyde were
obtained: Hydrocellulose, 0.854; oxycellulose, 2.113; reduced cellulose,
0.860; starch, 0.800; bleached cotton, 1.800; oxycellulose, prepared by
means of chromic acid, 3.500. Two specimens of oxycellulose were
prepared by treating cotton wool with hydrochloric acid and potassium
chlorate (A), and with sulphuric acid and potassium dichromate (B), and
25 grams of each product digested with aqueous potash. Of the product A,
16.20 grams were insoluble in potash, 2.45 grams were precipitated on
neutralisation of the alkaline solution, and 6.35 grams remained in
solution, whilst B yielded 11.16 grams of insoluble matter, 1.42 grams
were precipitated by acid, and 12.42 grams remained in solution. The
percentage yields of furfuraldehyde obtained from these fractions were
as follows: A, insoluble, 0.86; precipitated, 4.35; dissolved, 1.10. B,
insoluble, 0.76; precipitated, 5.11; dissolved, 1.54. It appears, from
the foregoing results, that the cellulose molecule, after oxidation, is
easily decomposed by potash, the insoluble and larger portion having all
the characters of the original cellulose, whilst the soluble portion is
of an aldehydic nature, and contains a substance, precipitable by acids,
which yields a relatively large amount of furfuraldehyde.


UNTERSUCHUNGEN ÜBER DIE OXYCELLULOSE.

O. V. FABER und B. TOLLENS (Berl. Ber., 1899, 2589).

~Investigations of Oxycellulose.~

(p. 61) The author's results are tersely summed up in the following
conclusions set forth at the end of the paper: The oxycelluloses are
mixtures of cellulose and a derivative oxidised compound which contains
one more atom O than cellulose (cellulose = C_{6}H_{10}O_{5}), and for
which the special designation _Celloxin_ is proposed.

Celloxin may be formulated C_{8}H_{6}O_{6} or C_{6}H_{10}O_{6}, of which
the former is the more probable.

The various oxycelluloses may be regarded as containing one celloxin
group to 1-4 cellulose groups, according to the nature of the original
cellulose, and the degree of oxidation to which subjected. These groups
are in chemical union.

Celloxin has not been isolated. On boiling the oxycelluloses with
lime-milk it is converted into isosaccharinic and dioxybutyric acids.
The insoluble residue from the treatment is cellulose.

The following oxycelluloses were investigated:

A. _Product of action of nitric acid upon pine wood_ (Lindsey and
Tollens, Ann. 267, 366).--The oxycelluloses contained

1 mol celloxin:  {2 mol. cellulose on 6 hours' heating
                 {3 mol. cellulose on 3 hours' heating

with a ratio H : O = 1 : 9 and 1 : 8.7 respectively: they yielded 7
p.ct. furfural.

B. _By action of bromine in presence of water and_ CaCO_{3} _upon
cotton_.--Yield, (air-dry) 85 p.ct. Empirical composition
C_{12}H_{20}O_{11} = C_{6}H_{10}O_{5}.C_{6}H_{10}O_{6}: yielded furfural
1.7 p.ct.

C. _Cotton and nitric acid at_ 100°, two and a half hours (Cross and
Bevan).--Yield, 70 p.ct. Composition

     4 C_{6}H_{10}O_{5}.C_{6}H_{8}O_{6}

yielded furfural 2.3 p.ct.

D. _Cotton and nitric acid at_ 100° (four hours).--A more highly
oxidised product resulted, viz. 3 C_{6}H_{10}O_{5}.C_{6}H_{8}O_{6}:
yielded furfural 3.2 p.ct.

_By-products of oxidation._--The liquors from B were found to contain
saccharic acid: the acid from C and B contained a dibasic acid which
appeared to be tartaric acid.

The isolation of (1) isosaccharinic and (2) dioxybutyric acid from the
products of digestion of the oxycelluloses with lime-milk at 100° was
effected by the separation of their respective calcium salts, (1) by
direct crystallisation, (2) by precipitation alcohol after separation of
the former.


CELLULOSES, HYDRO- AND OXYCELLULOSES, AND CELLULOSE ESTERS.

L. VIGNON (Bull. Soc. Chim., 1901 [3], 25, 130).

(a) _Oxycelluloses from cotton, hemp, flax, and ramie._--The
comparative oxidation of these celluloses, by treatment with HClO_{3}
at 100°, gave remarkably uniform results, as shown by the following
numbers, showing extreme variations: yields, 68-70 p.ct.; hydrazine
reaction, N fixed 1.58-1.69; fixation of basic colouring matters
(relative numbers), saffranine, 100-200, methylene blue, 100-106. The
only points of difference noted were (1) hemp is somewhat more resistant
to the acid oxidation; (2) the cotton oxycellulose shows a somewhat
higher (25 p.ct.) cupric reduction.

(b) _'Saccharification' of cellulose, cellulose hydrates, and
hydrocellulose._--The products were digested with dilute hydrochloric
acid six hours at 100°, and the cupric reduction of the soluble products
determined and calculated to dextrose.

  100 grms. of                   gave reducing products equal to Dextrose

Purified cotton                                                      3.29
  "      Hydrocellulose                                              9.70
Cotton mercerised (NaOH 30° B.)                                      4.39
Cotton mercerised (NaOH 40° B.)                                      3.51
Cellulose reprecipitated from cuprammonium                           4.39
Oxycellulose                                                        14.70
Starch                                                              98.6

These numbers show that cellulose may be hydrated both by mercerisation
and solution, without affecting the constitutional relationships of the
CO groups. The results also differentiate the cellulose series from
starch in regard to hydrolysis.

(c) _Cellulose and oxycellulose nitrates._--The nitric esters of
cellulose have a strong reducting action on alkaline copper solutions.
The author has studied this reaction quantitatively for the esters both
of cellulose and oxycellulose, at two stages of 'nitration,' represented
by 8.2-8.6 p.ct. and 13.5-13.9 p.ct. total nitrogen in the
ester-products, respectively. The results are expressed in terms (c.c.)
of the cupric reagent (Pasteur) reduced per 100 grs. compared with
dextrose (=17767).

    Cellulose maximum nitration (13.5 p.ct. N)             3640
    Oxycellulose maximum nitration (13.9 p.ct. N)          3600
    Cellulose minimum nitration (8.19 p.ct. N)             3700
    Oxycellulose minimum nitration (8.56 p.ct. N)          3620

The author concludes that, since the reducing action is independent of
the degree of nitration, and is the same for cellulose and the
oxycelluloses, the ester reaction in the case of the normal cellulose is
accompanied by oxidation, the product being an oxycellulose ester.

_Products of 'denitration'._--The esters were treated with ferrous
chloride in boiling aqueous solution. The products were oxycelluloses,
with a cupric reduction equal to that of an oxycellulose directly
prepared by the action of HClO_{3}. On the other hand, by treatment with
ammonium sulphide at 35°-40° 'denitrated' products were obtained without
action on alkaline copper solutions.


OXYCELLULOSES AND THE MOLECULAR WEIGHT OF CELLULOSE.

H. NASTUKOFF (Berl. Ber. 33 [13] 2237).

(p. 61) The author continues his investigations of the oxidation of
cellulose. [Compare Bull. Mulhouse, 1892.] The products described were
obtained by the action of hypochlorites and permanganates upon Swedish
filter paper (Schleicher and Schüll).

4. _Oxidation by hypochlorites._--(1) The cellulose was digested 24 hrs.
with 35 times its weight of a filtered solution of bleaching power of
4°B.; afterwards drained and exposed for 24 hrs. to the atmosphere.
These treatments were then repeated. After washing, treatment with
dilute acetic acid and again washing, the product was treated with a 10
p.ct. NaOH solution. The oxycellulose was precipitated from the
filtered solution: yield 45 p.ct. The residue when purified amounted to
30 p.ct. of the original cellulose, with which it was identical in all
essential properties.

The oxycellulose, after purification, dried at 110°, gave the following
analytical numbers:

     C    43.64     43.78    43.32    43.13
     H     6.17      6.21     5.98     6.08

Its compound with phenylhydrazine (_loc. cit._) gave the following
analytical numbers:

     N      0.78     0.96    0.84

(2) The reagents were as in (1), but the conditions varied by passing a
stream of carbonic acid gas through the solution contained in a flask,
until Cl compounds ceased to be given off. The analysis of the purified
oxycellulose gave C 43.53, H 6.13.

(3) The conditions were as in (2), but a much stronger hypochlorite
solution--viz. 12°B.--was employed. The yield of oxycellulose
precipitated from solution in soda lye (10 p.ct. NaOH) was 45 p.ct.
There was only a slight residue of unattacked cellulose. The analytical
numbers obtained were:

    Oxycellulose              C  43.31   43.74   43.69
        "                     H   6.47    6.42    6.51
                              ________________________

    Phenylhydrazine compound  N           0.62    0.81

B. _Oxidation by permanganate_ (KMnO_{4}). (1) The cellulose 16 grms.
was treated with 1100 c.c. of a 1 p.ct. solution of KMnO_{4} in
successive portions. The MnO_{2} was removed from time to time by
digesting the product with a dilute sulphuric acid (10 p.ct.
H_{2}SO_{4}). The oxycellulose was purified as before, yield 40 p.ct.
Analytical numbers:

    Oxycellulose              C          42.12    42.9
        "                     H           6.20     6.11
                              ________________________

    Phenylhydrazine compound  N   1.35    1.08     1.21

(2) The cellulose (16 grms.) was digested 14 days with 2500 c.c. of 1
p.ct. KMnO_{4} solution. The purified oxycellulose was identical in all
respects with the above: yield 40 p.ct. C 42.66, H 6.19.

(3) The cellulose (16 grms.) was heated in the water-bath with 1600 c.c.
of 15 p.ct. H_{2}SO_{4} to which were added 18 grms. KMnO_{4}. The yield
and composition of the oxycellulose was identical with the above. It
appears from these results that the oxidation with hypochlorites acids 1
atom of O to 4-6 of the unit groups C_{6}H_{10}O_{5}; and the oxidation
with permanganate 2 atoms O per 4-6 units of C_{6}H_{10}O_{5}. The
molecular proportion of N in the phenylhydrazine residue combining is
fractional, representing 1 atom O, i.e. 1 CO group reacting per 4
C_{36}H_{60}O_{31} and 6 C_{24}H_{49}O_{21} respectively, assuming the
reaction to be a hydrazone reaction.

Further investigations of the oxycelluloses by treatment with (a)
sodium amalgam, (b) bromine (water), and (c) dilute nitric acid at
110°, led to no positive results.

By treatment with alcoholic soda (NaOH) the products were resolved into
a soluble and insoluble portion, the properties of the latter being
those of a cellulose (hydrate).

_Molecular weight of cellulose and oxycellulose._--The author endeavours
to arrive at numbers expressing these relations by converting the
substances into acetates by Schutzenberger's method, and observing the
boiling-points of their solution in nitrobenzene.


FERMENTATION OF CELLULOSE

V. OMELIANSKI (Compt. Rend., 1897, 125, 1131-1133).

Pure paper was allowed to ferment in the presence of calcium carbonate
at a temperature of 35° for 13 months. The products obtained from
3.4743 grams of paper were: acids of the acetic series, 2.2402 grams;
carbonic anhydride, 0.9722 grams; and hydrogen, 0.0138 gram. The acids
were chiefly acetic and butyric acid, the ratio of the former to the
latter being 1.7 : 1. Small quantities of valeric acid, higher alcohols,
and odorous products were formed.

The absence of methane from the products of fermentation is remarkable,
but the formation of this gas seems to be due to a special organism
readily distinguishable from the ferment that produces the fatty acids.
This organism is at present under investigation.

       *       *       *       *       *

(p. 75) ~Constitution of Cellulose.~--It may be fairly premised that the
problem of the constitution of cellulose cannot be solved independently
of that of molecular aggregation. We find in effect that the structural
properties of cellulose and its derivatives are directly connected with
their constitution. So far we have only a superficial perception of this
correlation. We know that a fibrous cellulose treated with acids or
alkalis in such a way that only hydrolytic changes can take place is
converted into a variety of forms of very different structural
characteristics, and these products, while still preserving the main
chemical characteristics of the original, show when converted into
derivatives by simple synthesis, _e.g._ esters and sulphocarbonates, a
corresponding differentiation of the physical properties of these
derivatives, from the normal standard, and therefore that the new
reacting unit determines a new physical aggregate. Thus the
sulphocarbonate of a 'hydrocellulose' is formed with lower proportions
of alkaline hydrate and carbon disulphide, gives solutions of relatively
low viscosity, and, when decomposed to give a film or thread of the
regenerated cellulose, these are found to be deficient in strength and
elasticity. Similarly with the acetate. The normal acetate gives
solutions of high viscosity, films of considerable tenacity, and when
those are saponified the cellulose is regenerated as an unbroken film.
The acetates of hydrolysed celluloses manifest a retrogradation in
structural and physical properties, proportioned to the degree of
hydrolysis of the original.

We may take this opportunity of pointing out that the celluloses not
only suggest with some definiteness the connection of the structural
properties of visible aggregates--that is, of matter in the mass--with
the configuration of the chemical molecule or reacting unit, but supply
unique material for the actual experimental investigation of the
problems involved. Of all the 'organic' colloids cellulose is the only
one which can be converted into a variety of derivative forms, from each
of which a regular solid can be produced in continuous length and of any
prescribed dimensions. Thus we can compare the structural properties of
cellulose with those of its hydrates, nitrates, acetates, and benzoates,
in terms of measurements of breaking strain, extensibility, elasticity.
Investigations in this field are being prosecuted, but the results are
not as yet sufficiently elaborated for reduction to formulæ. One
striking general conclusion is, however, established, and that is that
the structural properties of cellulose are but little affected by
esterification and appear therefore to be a function of the special
arrangement of the carbon atoms, i.e. of the molecular constitution.
Also it is established that the molecular aggregate which constitutes a
cellulose is of a resistant type, and undoubtedly persists in the
solutions of the compounds.

It may be urged that it is superfluous to import these questions of
mass-aggregation into the problem of the chemical constitution of
cellulose. But we shall find that the point again arises in attempting
to define the reacting unit, which is another term for the molecule. In
the majority of cases we rely for this upon physical measurements; and
in fact the purely chemical determination of such quantities is
inferential. Attempts have been made to determine the molecular weights
of the cellulose esters in solution, by observations of depression of
solidifying and boiling-points. But the numbers have little value. The
only other well-defined compound is the sulphocarbonate. It has been
pointed out that, by successive precipitations of this compound, there
occurs a continual aggregation of the cellulose with dissociation of the
alkali and CS residues and it has been found impossible to assign a
limit to the dissociation, i.e. to fix a point at which the transition
from soluble sulphocarbonate to insoluble cellulose takes place.

On these grounds it will be seen we are reduced to a somewhat
speculative treatment of the hypothetical ultimate unit group, which is
taken as of C_{6} dimensions.

As there has been no addition of experimental facts directly
contributing to the solution of the problem, the material available for
a discussion of the probabilities remains very much as stated in the
first edition, pp. 75-77. It is now generally admitted that the
tetracetate _n_ [C_{6}H_{6}O.(OAc)_{4}] is a normal cellulose ester;
therefore that four of the five O atoms are hydroxylic. The fifth is
undoubtedly carbonyl oxygen. The reactions of cellulose certainly
indicate that the CO- group is ketonic rather than aldehydic. Even when
attacked by strong sulphuric acid the resolution proceeds some
considerable way before products are obtained reducing Fehling's
solution. This is not easily reconcilable with any polyaldose formula.
Nor is the resistance of cellulose to very severe alkaline treatments.
The probability may be noted here that under the action of the alkaline
hydrates there occurs a change of configuration. Lobry de Bruyn's
researches on the change of position of the typical CO- group of the
simple hexoses, in presence of alkalis, point very definitely in this
direction. It is probable that in the formation of alkali cellulose
there is a constitutional change of the cellulose, which may in effect
be due to a migration of a CO- position within the unit group. Again
also we have the interesting fact that structural changes accompany the
chemical reaction. It is surprising that there should have been no
investigation of these changes of external form and structure, otherwise
than as mass effects. We cannot, therefore, say what may be the
molecular interpretation of these effects. It has not yet been
determined whether there are any intrinsic volume changes in the
cellulose substance itself: and as regards what changes are determined
in the reacting unit or molecule, we can only note a fruitful subject
for future investigation. _A priori_ our views of the probable changes
depend upon the assumed constitution of the unit group. If of the
ordinary carbohydrate type, formulated with an open chain, there is
little to surmise beyond the change of position of a CO- group. But
alternative formulæ have been proposed. Thus the tetracetate is a
derivative to be reckoned with in the problem. It is formed under
conditions which preclude constitutional changes within the unit groups.
The temperature of the main reaction is 30°-40°, the reagents are used
but little in excess of the quantitative proportions, and the yields are
approximately quantitative. If now the derivative is formed entirely
without the hydrolysis the empirical formula C_{6}H_{6}O.(OAc)_{4}
justifies a closed-ring formula for the original viz.
CO<[CHOH]_{4}>CH_{2}; and the preference for this formula depends upon
the explanation it affords of the aggregation of the groups by way of
CO-CH_{2} synthesis.

The exact relationship of the tetracetate to the original cellulose is
somewhat difficult to determine. The starting-point is a cellulose
hydrate, since it is the product obtained by decomposition of the
sulphocarbonate. The degree of _hydrolysis_ attending the cycle of
reactions is indicated by the formula 4 C_{6}H_{10}O_{5}.H_{2}O. It has
been already shown that this degree of hydrolysis does not produce
molecular disaggregation. If this hydrate survived the acetylation it
would of course affect the empirical composition, i.e. chiefly the
carbon percentage, of the product. It may be here pointed out that the
extreme variation of the carbon in this group of carbohydrate esters is
as between C_{14}H_{20}O_{10} (C = 48.3 p.ct.) and C_{14}H_{18}O_{9} (C
= 50.8 p.ct.) i.e. a tetracetate of C_{6}H_{12}O_{6} and
C_{6}H_{10}O_{5} respectively. In the fractional intermediate terms it
is clear that we come within the range of ordinary experimental errors,
and to solve this critical point by way of ultimate analysis must
involve an extended series of analyses with precautions for specially
minimising and quantifying the error. The determination of the acetyl by
saponification is also subject to an error sufficiently large to
preclude the results being applied to solve the point. While, therefore,
we must defer the final statement as to whether the tetracetate is
produced from or contains a partly hydrolysed cellulose molecule, it is
clear that at least a large proportion of the unit groups must be
acetylated in the proportion C_{6}H_{6}O.(OAc)_{4}.

It has been shown that by the method of Franchimont a higher proportion
of acetyl groups can be introduced; but this result involves a
destructive hydrolysis of the cellulose: the acetates are not
derivatives of cellulose, but of products of hydrolytic decomposition.

It appears, therefore, that with the normal limit of acetylation at the
tetracetate the aggregation of the unit groups must depend upon the CO-
groups and a ring formula of the general form CO<[CHOH]_{4}>CH_{2} is
consistent with the facts.

Vignon has proposed for cellulose the constitutional formula

     O------CH
     |      | \
     |      O  \[CHOH]_{3}
     |      |  /
     CH_{2}-CH/

with reference to the highest nitrate, and the decomposition of the
nitrate by alkalis with formation of hydroxypyruvic acid. While these
reactions afford no very sure ground for deductions as to constitutional
relationships, it certainly appears that, if the aldose view of the unit
group is to be retained, this form of the anhydride contains suggestions
of the general tendency of the celluloses on treatment with condensing
acids to split off formic acid in relatively large quantity [Ber. 1895,
1940]; the condensation of the oxycelluloses to furfural; the
non-formation of the normal hydroxy-dicarboxylic acids by nitric acid
oxidations. Indirectly we may point out that any hypothesis which
retains the polyaldose view of cellulose, and so fails to differentiate
its constitution from that of starch, has little promise of progress.
The above formula, moreover, concerns the assumed unit group, with no
suggestion as to the mode of aggregation in the cellulose complex. Also
there is no suggestion as to how far the formula is applicable to the
celluloses considered as a group. In extending this view to the
oxycelluloses, Vignon introduces the derived oxidised group

     CHO.(CHOH)_{3}.CH . CO
                    |_O__|

--of which one is apportioned to three or four groups of the cellulose
previously formulated: these groups in condensed union together
constitute an oxycellulose.

These views are in agreement with the experimental results obtained by
Faber and Tollens (p. 71). They regard the oxycelluloses as compounds of
'celloxin' C_{6}H_8{O}_{6} with 1-4 mols. unaltered cellulose; and the
former they particularly refer to as a lactone of glycuronic acid. But
on boiling with lime they obtain dioxybutyric and isosaccharinic acids;
both of which are not very obviously related to the compounds formulated
by Vignon. We revert with preference to a definitely ketonic formula,
for which, moreover, some farther grounds remain to be mentioned. In the
systematic investigation of the nitric esters of the carbohydrates (p.
41) Will and Lenze have definitely differentiated the ketoses from the
aldoses, as showing an internal condensation accompanying the ester
reaction. Not only are the OH groups taking part in the latter
consequently less by two than in the corresponding aldoses, but the
nitrates show a much increased stability. This would give a simple
explanation of the well-known facts obtaining in the corresponding
esters of the normal cellulose. We may note here that an important item
in the quantitative factors of the cellulose nitric ester reaction has
been overlooked: that is, the yield calculated to the NO_{3} groups
fixed. The theoretical yields for the higher nitrates are

                     Yield p.ct.    N p.ct.
                    of cellulose  of nitrate
    Pentanitrate        169         12.7
    Hexanitrate         183         14.1

From such statistics as are recorded the yields are not in accordance
with the above. There is a sensible deficiency. Thus Will and Lenze
record a yield of 170 p.ct. for a product with 13.8 p.ct. N, indicating
a deficiency of about 10 p.ct. As the by-products soluble in the acid
mixture are extremely small, the deficiency represents approximately the
water split off by an internal reaction. In this important point the
celluloses behave as ketoses.

In the lignocelluloses the condensed constituents of the complex are of
well-marked ketonic, i.e. quinonic, type. In 'nitrating' the
lignocelluloses this phenomenon of internal condensation is much more
pronounced (see p. 131). As the reaction is mainly confined to the
cellulose of the fibre, we have this additional evidence that the
typical carbonyl is of ketonic function. It is still an open question
whether the cellulose constituents of the lignocelluloses are
progressively condensed--with progress of 'lignification'--to the
unsaturated or lignone groups. There is much in favour of this view,
the evidence being dealt with in the first edition, p. 180. The
transition from a cellulose-ketone to the lignone-ketone involves a
simple condensation without rearrangement; from which we may argue back
to the greater probability of the ketonic structure of the cellulose. We
must note, however, that the celluloses of the lignocelluloses are
obtained as residues of various reactions, and are not homogeneous. They
yield on boiling with condensing acids from 6 to 9 p.ct. furfural. It is
usual to regard furfural as invariably produced from a pentose residue.
But this interpretation ignores a number of other probable sources of
the aldehyde. It must be particularly remembered that lævulose is
readily condensed (a) to a methylhydroxyfurfural

C_{6}H_{1}O_{6} - 3H_{2}O = C_{6}H_{6}O_{3} = C_{5}(OH).H_{2}.(CH_{3})O_{2}

and (b) by HBr, with further loss of OH, as under:

C_{6}H_{12}O_{6} - 4H_{2}O + HBr = C_{5}H_{3}(CH_{2}Br)O

and generally the ketoses are distinguished from the aldoses by their
susceptibility to condensation. Such condensation of lævulose has been
effected by two methods: (a) by heating the concentrated aqueous
solution with a small proportion of oxalic acid at 3 atm. pressure
[Kiermayer, Chem. Ztg. 19, 100]; (b) by the action of hydrobromic acid
(gas) in presence of anhydrous ether; the actual compound obtained being
the omega-brommethyl derivative [Fenton, J. Chem. Soc. 1899, 423].

This latter method is being extended to the investigation of typical
celluloses, and the results appear to confirm the view that cellulose
may be of ketonic constitution.

The evidence which is obtainable from the synthetical side of the
question rests of course mainly upon the physiological basis. There are
two points which may be noted. Since the researches of Brown and Morris
(J. Chem. Soc. 1893, 604) have altered our views of the relationships of
starch and cane sugar to the assimilation process, and have placed the
latter in the position of a primary product with starch as a species of
overflow and reserve product, it appears that lævulose must play an
important part in the elaboration of cellulose. Moreover, A. J. Brown,
in studying the cellulosic cell-collecting envelope produced by the
_Bacterium xylinum_, found that the proportion of this product to the
carbohydrate disappearing under the action of the ferment was highest in
the case of lævulose. These facts being also taken into consideration
there is a concurrence of suggestion that the typical CO group in the
celluloses is of ketonic character. That the typical cotton cellulose
breaks down finally under the action of sulphuric acid to dextrose
cannot be held to prove the aldehydic position of the carbonyls in the
unit groups of the actual cellulose molecule or aggregate.

We again are confronted with the problem of the aggregate and as to how
far it may affect the constitution of the unit groups. That it modifies
the functions or reactivity of the ultimate constituent groups we have
seen from the study of the esters. Thus with the direct ester reactions
the normal fibrous cellulose (C_{6}H_{16}O_{5}) yields a monoacetate,
dibenzoate, and a trinitrate respectively under conditions which
determine, with the simple hexoses and anhydrides, the maximum
esterification, i.e. all the OH groups reacting. If the OH groups are of
variable function, we should expect the CO groups _a fortiori_ to be
susceptible of change of function, i.e. of position within the unit
groups.

But as to how far this is a problem of the constitution or phases of
constitution of the unit groups or of the aggregate under reaction we
have as yet no grounds to determine.

The subjoined communication, appearing after the completion of the MS.
of the book, and belonging to a date subsequent to the period intended
to be covered, is nevertheless included by reason of its exceptional
importance and special bearing on the constitutional problem above
discussed.


~THE ACTION OF HYDROGEN BROMINE ON CARBOHYDRATES.~[4]

H. J. H. FENTON and MILDRED GOSTLING (J. Chem. Soc., 1901, 361).

The authors have shown in a previous communication (Trans., 1898, 73,
554) that certain classes of carbohydrates when acted upon at the
ordinary temperature with dry hydrogen bromide in ethereal solution give
an intense and beautiful purple colour.[5] It was further shown (Trans.,
1899, 75, 423) that this purple substance, when neutralised with sodium
carbonate and extracted with ether, yields golden-yellow prisms of
omega-brommethylfurfural,

     CH:C.CH_{2}Br
     |  |
     |  O
     |  |
     CH:C.CHO.

This reaction is produced by lævulose, sorbose, cane sugar, and inulin,
an intense colour being given within an hour or two. Dextrose, maltose,
milk sugar, galactose, and the polyhydric alcohols give, if anything,
only insignificant colours, and these only after long standing. The
authors therefore suggested that the reaction might be employed as a
means of distinguishing these classes of carbohydrates, the rapid
production of the purple colour being indicative of _ketohexoses_, or of
substances which produce these by hydrolysis.

By relying only on the production of the purple colour, however, a
mistake might possibly arise, owing to the fact that _xylose_ gives a
somewhat similar colour after standing for a few hours. Hence, the
observations should be confirmed by isolation of the crystals of
brommethylfurfural. No trace of this substance is obtained from the
xylose product.

In order to identify the substance, the ether extract, after
neutralisation, is allowed to evaporate to a syrup, and crystallisation
promoted either by rubbing with a glass rod, or by the more certain and
highly characteristic method of 'sowing' with the most minute trace of
omega-brommethylfurfural, when crystals are almost instantly formed.
These are recrystallised from ether, or a mixture of ether and light
petroleum, and further identified by the melting-point (59.5-60.5°),
and, if considered desirable, by estimation of the bromine.

It is now found, so reactive is the bromine atom in this compound, that
the estimation may be accurately made by titration with silver nitrate
according to Volhard's process, the crystals for this purpose being
dissolved in dilute alcohol:

0.1970 gram required 10.5 c.c. _N_/10 AgNO_{3}. Br = 42.63
p.ct., calculated 42.32 p.ct.

This method of applying hydrogen bromide in ethereal solution is, of
course, unsuitable for investigations where a higher temperature has to
be employed, or where long standing is necessary, since, under such
circumstances, the ether itself is attacked. Wishing to make
investigations under these conditions, the authors have tried several
solvents, and, at present, find that chloroform is best suited to the
purpose. In each of the following experiments, 10 grms. of the
substance were covered with 250 c.c. of chloroform which had been
saturated at 0° with dry hydrogen bromide. The mixture was contained in
an accurately stoppered bottle, firmly secured with an iron clamp, and
heated in a water-bath to about the boiling temperature for two hours.
After standing for several hours, the mixture was treated with sodium
carbonate (first anhydrous solid, and afterwards a few drops of strong
solution), filtered, and the solution dried over calcium chloride. Most
of the chloroform was then distilled off, and the remaining solution
allowed to evaporate to a thick syrup in a weighed dish.

The product was then tested for omega-brommethylfurfural by 'sowing'
with the most minute trace of the substance, as described above. It was
then warmed on a water-oven, kept in a vacuum desiccator over solid
paraffin, and the weight estimated. When necessary, the product was
recrystallised from ether, and further identified by the tests
mentioned. The following results were obtained:

                      Weight of
                    crude residue.
Swedish filter paper     3.0      crystallised at once by 'sowing.'
Ordinary cotton          3.3          "                     "
Mercerised cotton        2.1          "                     "
Straw cellulose[6]       2.3          "                     "
Lævulose                 2.2          "                     "
Inulin                   1.3          "                     "
Potato starch            0.37         "                     "
Cane sugar               0.85         "                     "
Dextrose                 0.33     uncrystallisable.
Milk sugar               0.37         "
Glycogen                 0.34         "
Galactose                0.34         "

The products from _dextrose_, _milk sugar_, and _galactose_ absolutely
refused to crystallise even when extracted with ether and again
evaporated, or by 'sowing,' stirring, &c.

The _glycogen_ product deposited a very small amount of crystalline
matter on standing, but the quantity was too minute for examination;
moreover, it refused altogether to crystallise in contact with the
aldehyde. It may fairly be stated, therefore, that these last four
substances give absolutely negative results as regards the formation of
omega-brommethylfurfural; if any is formed, its quantity is altogether
too small to be detected.

The specimen of _starch_ examined was freshly prepared from potato, and
purified by digestion for twenty-four hours each with _N_/10 KOH, _N_/4
HCl, and strong alcohol; it was then washed with water and allowed to
dry in the air. It will be seen that this substance gave a positive
result, but that the yield was extremely small, and might yet be due to
impurity. Considering the importance of the behaviour of starch, for the
purpose of drawing general conclusions from these observations, it was
thought advisable to make further experiments with specimens which could
be relied upon, and also to investigate the behaviour of dextrin. This
the authors have been enabled to do upon a series of specimens specially
prepared by C. O'Sullivan, and thus described by him:

     1. Rice starch, specially purified by the permanganate method.

     2. Wheat starch       "                "                 "

     3. Oat starch, contains traces of oil, washed with dilute KOH
     and dilute HCl.

     4. Pea starch, first crop, washed with alkali, acid (HCl), and
     strong alcohol.

     5. Natural dextrin, D = 3.87, alpha_{D} = 194.7; K = 0.95, (c
     2.628).

     6. alpha-Dextrin, C equation purified without fermentation, 30
     precipitations with alcohol (Trans., 1879, 35, 772).

The examination of these specimens was conducted on a smaller scale, but
under the same conditions as before, _one gram_ of the substance being
treated with 12.5 c.c. of the saturated chloroform solution and heated
in sealed tubes for two hours as above. The results were as follows:

                    Weight of
                  crude residue.
1. Rice starch       0.046   crystallised at once by 'sowing.'
2. Wheat starch      0.044        "                 "
3. Oat starch        0.049        "                 "
4. Pea starch        0.064        "                 "
5. Natural dextrin   0.088        "                 "
6. alpha-Dextrin     0.055        "                 "

The results may therefore be summarised as follows:--Treated under these
particular conditions all forms of cellulose give large yields of
omega-brommethylfurfural, some varieties giving as much as 33 per cent.
Lævulose, inulin, and cane sugar give yields varying from 22 to 8.5 per
cent.; various starches give small yields (average about 4.5 per cent.);
and dextrins 5 to 8 per cent., whereas dextrose, milk sugar, and
galactose give, apparently, none at all.

The yields represent the solid crystalline residue; this when purified
by recrystallisation gives, probably, about three-quarters of its weight
of pure crystals. (In the case of dextrose, &c., the yields represent
the weight of syrup.)

These numbers, however, by no means represent the maximum yields
obtainable, owing to the comparatively slight solubility of hydrogen
bromide in chloroform. The process was conducted in the above manner
only for the sake of uniform comparison. The ether method previously
described gives much larger yields; for example, 12 grms. of inulin
treated with only 60 c.c. of the saturated ether gave 2.5 grms. of
substance. For the purpose of obtaining larger yields, other methods are
being investigated.

The facts recorded above, taken in conjunction with those given in our
previous communications, appear to point definitely to the following
general conclusions. First, that the various forms of _cellulose_
contain one or more groups or nuclei identical with that contained in
_lævulose_, and that such groups constitute the main or essential part
of the molecule. Secondly, that similar groupings are contained in
_starches_ and _dextrins_, but that the proportion of such groupings
represents a relatively small part of the whole structure.

The nature of this grouping is, according to the generally accepted
constitution of _lævulose_, the six-carbon chain with a ketonic group:

     C·C·C·C·C·C
             || .
             O

But the results might, on the other hand, be considered indicative of
the anhydride or 'lacton' grouping, which Tollens suggested for
lævulose:

     C·C·C·C·C·C
        \   /
         \ /  .
          O

The latter very simply represents the formation of
omega-brommethylfurfural from lævulose,[7]

              ------O-----
              |   H   H  |
              |   |   |  |
     OH·C-----C---C---C--C-----CH_{2}·OH
        H_{2} OH  OH  OH H

giving

          H H
     HC·C:C·C:C·CH_{2}Br
      || \   /    ,
      O   \ /
           O


although by a little further 'manipulation' of the symbols the change
could, of course, be represented by reference to the ketonic formula.


~The Ketonic Constitution of Cellulose.~

C. F. CROSS and E. J. BEVAN (J. Chem. Soc., 1901, 366).

In this paper the authors discuss more fully the theoretical bearings of
the observations of Fenton and Gostling, the two papers being
simultaneously communicated. The paper is mainly devoted to a review of
the antecedent evidence, chemical and physiological, and to a general
summing up in favour of the view that cellulose is a polyketose
(anhydride).

       *       *       *       *       *

(p. 79) ~Composition of the Seed Hair of Eriodendron~ (~Anf.~)--Some
interest attaches to the results of an analytical investigation which we
have made of this silky floss. There is little doubt that cotton is
entirely exceptional in its characteristics: both in structure and
chemical composition it fails to show any adaptation to what we may
regard as the _more obvious_ functions of a seed hair--which certainly
do not demand either structural strength or chemical resistance. The
following numbers determined for the kapok differentiate it widely from
the cottons:

     Ash, 1.3; moisture, 9.3; alkaline hydrolysis (loss) (a) 16.7,
     (b) 21.8. Cellulose, by chlorination, &c., 71.1.

In reacting with chloride it shows the presence of unsaturated groups,
similar to the lignone of the woods. This was confirmed by a
well-marked reaction with ferric ferricyanide with increase of weight
due to the fixation of the blue cyanide.

But the most characteristic feature is the high yield of furfural on
boiling with condensing acids. The following numbers were determined:

     Total furfural from original fibre    14.84
     In residue from alkali hydrolysis     11.5
     In cellulose isolated by Cl method    10.4

Treated with sulphuric acids of concentration, (a) 92.1 grs.
H_{2}SO_{4} per 100 c.c., (b) 105.8 grs. per 100 c.c., the fibres
dissolve, and diluted immediately after complete solution it was
resolved into

                                      (a)        (b)

Reprecipitated fraction               68.7       43.7
Soluble fraction yielding furfural    13.2       14.3

By these observations it is established that the furfuroids are of the
cellulose type and behave very much as the furfuroids of the cereal
celluloses.

This group of seed hairs invites exhaustive investigation. The furfuroid
constituents are easily isolated, and as they constitute at least
one-third of the fibre substance it is especially from this point of
view that they invite study.


RECHERCHES SUR L'OXYCELLULOSE.

L. VIGNON.

~Résumé of investigations (1898-1900) of Oxycellulose, published as a
brochure~ (Rey, Lyon, 1900).

(a) A typical oxycellulose prepared from cotton cellulose by the
action of HClO_{3} (HCl + KClO_{3}) in dilute solution at 100° for one
hour gave the following numbers:

                                                  C        H        O
Elementary composition                          43.55    6.03     50.42

                                        Oxycellulose   Original cellulose
  Analysis by Lange's method
    Soluble in KOH (at 180°)               87.6           12.0
    Insoluble in KOH (at 180°)             12.4           88.0

                                           Oxycellulose  Original cellulose
  Heat of combustion                        4124-4133      4190-4224
Heat evolved in contact with 50 times wt.}
  normal KOH per 100 grms.               }  1.3 cal.       0.74 cal.

                                            Oxycellulose  Cellulose
Absorption of colouring       } Saffranine       0.7          0.0
matters at 100° per 100 grms. } Methylene blue   0.6          0.2

(b) _Yield of furfural from cellulose, oxy- and
hydro-cellulose._--From the hydrocelluloses variously prepared the
author obtains 0.8 p.ct. furfural; from bleached cotton 1.8 p.ct.; and
from the oxycelluloses variously prepared 2.0-3.5 p.ct. The 'furfuroid'
is relatively more soluble in alkaline solutions (KOH) in the cold. The
insoluble residue is a normal cellulose.

(c) _Nitrates of cellulose, oxy- and hydro-cellulose._--Treated with
the usual acid mixture (H_{2}SO_{4} 3 p., HNO_{3} 1 p.) under conditions
for maximum action, the resulting esters showed uniformly a fixation of
11.0 NO_{2} groups per unit mol. of C_{24}. The oxycellulose nitrate
was treated directly with dilute solution of potassium hydrate in the
cold. From the products of decomposition the author obtained the osazone
of hydroxypyruvic acid [Will, Ber. 24, 400].

(d) _Osazones of the oxycelluloses._--Oxycelluloses prepared by
various methods are found to fix varying proportions of phenylhydrazine
(residue), viz. from 3.4-8.5 p.ct. of the cellulose derivative reacting,
corresponding with, i.e. calculated from, the nitrogen determined in the
products (0.87-2.2 p.ct.). The reaction is assumed to be that of osazone
formation.

The author has also established a relation between the phenylhydrazine
fixed and the furfural which the substance yields on boiling with
condensing acids. This is illustrated by the subjoined series of
numbers:

                              Phenylhydrazine     Furfural
                                 Fixed p.ct.    formed p.ct.
Cotton (bleached)                   1.73            1.60
Oxycellulose (HClO_{3})             7.94            2.09
     "       (HClO)                 3.37            1.79
     "       (CrO_{3}) (1)          7.03            3.00
     "       (CrO_{3}) (2)          7.71            3.09
     "       (CrO_{3}) (3)          8.48            3.50

(e) _Constitution of cellulose and oxycellulose._--The results of
these investigations are generalised as regards cellulose (C_6) by the
constitutional formula

                 CH--CH_{2}
               / |   |
     (CHOH)_{3}  O   |
               \ |   |
                 CH--O .

The oxycelluloses contain the characteristic group

                COH
               /
     (CHOH)_{3}
               \
                CH--CO
                 \ /
                  O

in union with varying proportions of residual cellulose.


QUANTITATIVE SEPARATION OF CELLULOSE-LIKE CARBOHYDRATES IN VEGETABLE
SUBSTANCES.

WILHELM HOFFMEISTER (Landw. Versuchs-Stat., 1897, 48, 401-411).

To separate the hemicelluloses, celluloses, and the constituents of
lignin without essential change, the substance, after being freed from
fat, is extracted with dilute hydrochloric acid and ammonia, and the
residue frequently agitated for a day or two with 5-6 p.ct. caustic soda
solution. It is then diluted, the extract poured off, neutralised with
hydrochloric acid, treated with sufficient alcohol, and the
hemicellulose filtered, dried, and weighed. The residue from the soda
extract is washed on a filter with hot water, and extracted with
Schweizer's reagent.

When the final residue (lignin) is subjected to prolonged extraction
with boiling dilute ammonia (a suitable apparatus is described, with
sketch) until the ammonia is no longer coloured, a residue is obtained
which mostly dissolves in Schweizer's reagent, and on repeating the
process the residue is found to consist largely of mineral matter. The
dissolved cellulose-like substances often contain considerable amounts
of pentosanes.

According to the nature of the substance, the extraction with ammonia
may take weeks, or months, or even longer; the ammonia extracts of hard
woods (as lignum vitæ) and of cork are dark brown, and give an odour of
vanilla when evaporated down. The residues, which are insoluble in
water, but redissolve in ammonia, have the properties of humic acids.
Other vegetable substances, when extracted, yielded, besides humic
acids, a compound, C_{6}H_{7}O_{2}, soluble in alcohol and chloroform,
but insoluble in water, ether, and benzene; preparations from different
sources melted between 200° and 210°.

FOOTNOTES:

[4] The original paper is reproduced with slight alterations.

[5] This purple colour would appear to be due to a highly dissociable
compound of omega-brommethylfurfural with hydrogen bromide. The aldehyde
gives yellow or colourless solutions in various solvents, which are
turned purple by a sufficient excess of hydrogen bromide. Dilution, or
addition of water, at once discharges the colour.

[6] Other forms of cellulose were also examined--for example, pinewood
cellulose--and the substances separated from solution as thiocarbonate
(powder and film). All of these gave good yields of
omega-brommethylfurfural.

[7] The change is empirically represented as

C_{6}H_{12}O_{6} + HBr - 4H_{2}O = C_{6}H_{5}O_{2}Br.




SECTION IV. CELLULOSE GROUP, INCLUDING HEMICELLULOSES AND TISSUE
CONSTITUENTS OF FUNGI


VERSUCHE ZUR BESTIMMUNG DES GEHALTS EINIGER PFLANZEN UND PFLANZENTEILE
AN ZELLWANDBESTANDTEILEN AN HEMICELLULOSEN UND AN CELLULOSE.

A. KLEIBER (Landw. Vers.-Stat., 1900, 54, 161).

~ON THE DETERMINATION OF CELL-WALL CONSTITUENTS, HEMICELLULOSES AND
CELLULOSE IN PLANTS AND PLANT TISSUES.~

In a preliminary discussion the author critically compares the results
of various of the methods in practice for the isolation and estimation
of cellulose. The method of F. Schulze [digestion with dil. HNO_{3} with
KClO_{3}--14 days, and afterwards treating the product with ammonia,
&c.] is stated to be the 'best known' (presumably the most widely
practised); W. Hoffmeister's modification of the above, in which the
nitric acid is replaced by hydrochloric acid (10 p.ct. HCl) is next
noted as reducing the time of digestion from 14 days to 1-2 days, and
giving in many cases higher yields of cellulose. The methods of treating
with the halogens, viz. bromine water (H. Müller), chlorine gas (Cross
and Bevan), and chlorine water, are dismissed with a bare mention,
apparently on the basis of the conclusions of Suringar and Tollens
(_q.v._). The method of Lange, the basis of which is a 'fusion' with
alkaline hydrates at 180°, and the modified method of Gabriel, in which
the 'fusion' with alkali takes place in presence of glycerin, are
favourably mentioned.

These methods were applied to a range of widely different raw materials
to determine, by critical examination of the products, both as regards
yield and composition, what title these latter have to be regarded as
'pure cellulose.'

This portion of the investigation is an extension of that of Suringar
and Tollens, these latter confining themselves to celluloses of the
'normal' groups, i.e. textile and paper-making celluloses. The present
communication is a study of the tissue and cell-wall constituents of the
following types:--

     1. Green plants of false oat grass (_Arrhenatherium, E._).
     2. Green plants of lucerne (_Medicago sativa_).
     3. Leaves of the ash (_Fraxinus_).
     4. Leaves of the walnut (_Juglans_).
     5. Roots of the purple melic grass (_Molinia cærulea_).
     6. Roots of dandelion (_Taraxacum officinale_).
     7. Roots of comfrey.
     8. Coffee berries.
     9. Wheat bran.

These raw materials were treated for the quantitative estimation of
cellulose by the method of Lange (b), Hoffmeister (c), and Schulze
(d), and the numbers obtained are referred for comparison to the
corresponding yields of 'crude fibre' (Rohfaser) by the standard method
(a).

As a first result the author dismisses Lange's method as hopeless: the
results in successive determinations on the same materials showing
variations up to 60 p.ct. The results by c and d are satisfactorily
concordant: the yields of cellulose are higher than of 'crude fibre.'
This is obviously due to the conservation of 'hemicellulose' products,
which are hydrolysed and dissolved in the treatments for 'crude fibre'
estimation. A modified method was next investigated, in which the
process of digestion with acid chloroxy- compounds (c and d) was
preceded by a treatment with boiling dilute acid. The yields of
cellulose by this method (e) are more uniform, and show less
divergence from the numbers for 'crude fibre.'

The author's numerical results are given in a series of tables which
include determinations of proteids and ash constituents, and the
corresponding deductions from the crude weight in calculating to 'pure
cellulose.' The subjoined extract will illustrate these main lines of
investigation.

 ___________________________________________________________
|                |             |                            |
|                | Crude Fibre |       Pure Cellulose       |
|                |_____________|____________________________|
|                |             |             |              |
| Raw Material   |   Weende    | Hoffmeister | Hoffmeister, |
|                |   Method.   |   Method.   | modified by  |
|                |     (a)     |     (c)     |   Author.    |
|                |             |             |     (e)      |
|________________|_____________|_____________|______________|
|                |             |             |              |
| Oat grass      |   30.35     |    34.9     |     31.5     |
| Lucerne        |   25.25     |    28.7     |     20.5     |
| Leaves of ash  |   13.05     |    15.4     |     13.8     |
| Roots of melic |   21.60     |    29.1     |     21.4     |
| Coffee beans   |   18.30     |    35.1     |     23.3     |
| Bran           |    8.2      |    19.3     |      9.3     |
|________________|_____________|_____________|______________|

The final conclusion drawn from these results is that the method of
Hoffmeister yields a product containing variable proportions of
hemicelluloses. These are eliminated by boiling with a dilute acid (1.25
p.ct. H_{2}SO_{4}), which treatment may be carried out on the raw
material--i.e. before exposure to the acid chlorate, or on the crude
cellulose as ordinarily isolated.

~Determination of Tissue-constituents.~--By the regulated action of
certain solvents applied in succession, it appears that such
constituents of the plant-complex can be removed as have no organic
connection with the cellular skeleton: the residue from such treatments,
conversely, fairly represents the true tissue-constituents. The author
employs the method of digestion with cold dilute alkaline solutions
(0.15 to 0.5 p.ct. NaOH), followed by exhaustive washing with cold and
hot water, afterwards with cold and hot alcohol, and finally with ether.

The residue is dried and weighed as crude product. When necessary, the
proportions of ash and proteid constituents are determined and deducted
from the 'crude product' which, thus corrected, may be taken as
representing the 'carbohydrate' tissue constituents.

~Determination of Hemicelluloses.~--By the process of boiling with dilute
acids (1.25 p.ct. H_{2}SO_{4}) the hemicelluloses are attacked--i.e.
hydrolysed and dissolved. The action of the acid though selective is, of
course, not exclusively confined to these colloidal carbohydrates. The
proteid and mineral constituents are attacked more or less, and the
celluloses themselves are not entirely resistant to the action. The loss
due to the latter may be neglected, but in calculating the hemicellulose
constants from the gross loss the proteids and mineral constituents
require to be taken into account in the usual way.


QUANTITATIVE SEPARATION OF HEMICELLULOSE, CELLULOSE, AND LIGNIN.
PRESENCE OF PENTOSANES IN THESE SUBSTANCES.

WILHELM HOFFMEISTER (Landw. Versuchs-Stat, 1898, 50, 347-362).

(p. 88) The separation of the cellulose-like carbohydrates of sunflower
husks is described.

In order to ascertain the effect of dilute ammonia on the cellulose
substances of lignin, a dried 5 p.ct. caustic soda extract was extracted
successively with 1, 2, 3, and 4 p.ct. sodium hydroxide solution. Five
grams of the 2 p.ct. extract were then subjected to the action of
ammonia vapour; the cellulose did not completely dissolve in six weeks.
Cellulose insoluble in caustic soda (32 grms.) was next extracted with
ammonia, in a similar manner, for 10 days, dried, and weighed. 30.46
grms. remained, which, when treated with 5 p.ct. aqueous caustic soda,
yielded 0.96 grm. (3 per cent.) of hemicellulose.

When cellulose is dissolved in Schweizer's solution, the residue is, by
repeated extraction with aqueous sodium hydroxide, completely converted
into the soluble form. On evaporating the ammonia from the Schweizer's
extract, at the ordinary temperature and on a water-bath respectively,
different amounts of cellulose are obtained; more hemicellulose is
obtained, by caustic soda, from the heated solution than from that which
was not heated. In this operation the pentosanes are more influenced
than the hexosanes; pentosanes are not always readily dissolved by
caustic soda, and hexosanes are frequently more or less readily
dissolved. Both occur in lignin, and are then undoubtedly indigestible.
These points have to be considered in judging the digestibility of these
carbohydrates.

A comparison of analyses of clover, at different periods, in the first
and second years of growth, shows that both cellulose (Schweizer's
extract) and lignin increase in both constituents. In the second year
the lignin alone increased to the end; the cellulose decreased at the
end of June. In the first year it seemed an absolutely as well as
relatively greater amount of cellulose, and lignin was produced in the
second year; this, however, requires confirmation. The amount of
pentosanes in the Schweizer extract was relatively greater in the second
than in the first year, but decreased in the lignin more in the second
year than in the first: this result is also given with reserve.


DIE CONSTITUTION DER CELLULOSEN DER CEREALIEN.

C. F. CROSS, E. J. BEVAN, and C. SMITH (Berl. Ber., 1896, 1457).

~THE CONSTITUTION OF THE CEREAL CELLULOSES.~

(p. 84) Straw cellulose is resolved by two methods of acid hydrolysis
into a soluble furfural-yielding fraction, and an insoluble fraction
closely resembling the normal cellulose. (a) The cellulose is
dissolved in sulphuric acids of concentration, H_{2}SO_{4}.2H_{2}O,
H_{2}SO_{4}.3H_{2}O. As soon as solution is complete, the acid is
diluted. A precipitate of cellulose hydrate (60-70 p.ct.) is obtained,
and the filtered solution contains 90-95 p.ct. of the furfuroids of the
original cellulose. The process is difficult to control, however, in
mass, and to obtain the latter in larger quantity the cellulose (b) is
digested with six times its weight of 1 p.ct. H_{2}SO_{4} at 3 atm.
pressure, the products of the action being (1) a disintegrated cellulose
retaining only a small fraction (1/12) of the furfural-yielding groups,
and (2) a slightly coloured solution of the hydrolised furfuroids. An
investigation of the latter gave the following results: By oxidation
with nitric acid no saccharic acid was obtained; showing the absence of
dextrose. The numbers for cupric reduction were in excess of those
obtained with the hexoses. The yield of ozazone was high, viz. 30 to 40
p.ct. of the weight of the carbohydrate in solution. On fractionating,
the melting-points of the fractions were found to lie between 146° and
153°. Ultimate analysis gave numbers for C, H, and N identical with
those of a pentosazone. The product of hydrolysis appears, therefore, to
be xylose or a closely related derivative.

All attempts to obtain a crystallisation of xylose from the solution
neutralised (BaCO_{3}), filtered, and evaporated, failed. The reaction
with phloroglucol and HCl, moreover, was not the characteristic red of
the pentoses, but a deep violet. The product was then isolated as a dry
residue by evaporating further and drying at 105°. Elementary analysis
gave the numbers C 44.2, 44.5, and H 6.7, 6.3. Determinations of
furfural gave 39.5 to 42.5 p.ct. On treating the original solution with
hydrogen peroxide, and warming, oxidation set in, with evolution of
CO_{2}. This was estimated (by absorption), giving numbers for CO_{2},
19.5, 20.5, 20.1 p.ct. of the substance.

The sum of these quantitative data is inconsistent with a pentose or
pentosane formula; it is more satisfactorily expressed by the empirical
formula

                   O
                  / \
     C_{5}H_{8}O_{3} CH_{2},
                  \ /
                   O

which represents a pentose monoformal. Attempts to synthesise a compound
of this formula have been so far without success.


UEBER EINIGE CHEMISCHE VORGÄNGE IN DER GERSTENPFLANZE.

C. F. CROSS, E. J. BEVAN, and C. SMITH (Berl. Ber., 1895, 2604).

~THE CHEMICAL LIFE-HISTORY OF THE BARLEY PLANT.~

(p. 84) Owing to the presence of 'furfuroids' in large proportion as
constituents of the tissues of the stems of cereals, these plants afford
convenient material for studying the problem of the constitution of the
tissue-furfuroids, as well as their relationship to the normal
celluloses. The growing barley plant was investigated at successive
periods of growth. Yield of furfural was estimated on the whole plant
and on the residue from a treatment with alkaline and acid solvents in
the cold such as to remove all cell contents. This residue is described
as 'permanent tissue.' The observations were carried out through two
growing seasons--1894-5--which were very different in character, the
former being rainy with low temperature, the latter being abnormal in
the opposite direction, i.e. minimum rainfall and maximum sunshine. The
barley selected for observation was that of two experimental plots of
the Royal Agricultural Society's farm, one (No. 1) remaining permanently
unmanured, and showing minimum yield, the other (No. 6) receiving such
fertilising treatment as to give maximum yields.

The numerical results are given in the annexed tables:

Table Headings:

A: Date
B: Age of Crop
C: Plot
D: Dry Weight
E: Furfural p.ct. of dry weight (a)
F: Permanent tissue p.ct. dry weight
G: Furfural from permanent tissue
H: P.ct. of tissue
I: P.ct. of entire plant
J: Ratio a : c

BARLEY CROP, WOBURN, 1894.

 ________________________________________________________________________
|         |          |     |      |      |      |             |          |
|         |          |     |      |      |      |     [G]     |          |
|         |          |     |      |      |      |_____________|          |
|         |          |     |      |      |      |      |      |          |
|   [A]   |    [B]   | [C] | [D]  | [E]  | [F]  | [H]  | [I]  |   [J]    |
|_________|__________|_____|______|______|______|______|______|__________|
|         |          |     |      |      |      |      |      |          |
| May 7   |  6 weeks |  1  | 19.4 |  7.0 | 53.4 | 12.7 |  6.8 | 1.03 : 1 |
|         |          |  6  | 14.7 |  7.0 | 55.9 | 10.3 |  5.7 | 1.23 : 1 |
| June 4  | 10 weeks |  1  | 17.6 |  7.7 | 52.9 | 11.6 |  6.1 | 1.26 : 1 |
|         |          |  6  | 13.5 |  8.1 | 58.5 | 13.4 |  7.8 | 1.04 : 1 |
| July 10 | 15 weeks |  1  | 42.0 |  9.0 | 65.7 |  9.8 |  6.4 | 1.40 : 1 |
|         |          |  6  | 32.9 | 10.6 | 65.7 | 12.5 |  8.2 | 1.30 : 1 |
| Cut     | 21 weeks |  1  | 64.0 | 11.9 | 70.0 | 14.5 | 10.1 | 1.18 : 1 |
| Aug. 21 |          |  6  | 64.6 | 13.4 | 70.5 | 15.0 | 10.6 | 1.26 : 1 |
| Carried | 22 weeks |  1  | 84.0 | 12.7 | 75.0 | 16.5 | 12.4 | 1.02 : 1 |
| Aug. 31 |          |  6  | 86.4 | 12.4 | 78.4 | 15.1 | 11.8 | 1.05 : 1 |
|                                                                        |
|   BARLEY CROP, WOBURN, 1895.                                           |
|                                                                        |
| May 15  |  7 weeks |  1  | 20.6 |  6.6 | 53.9 | 10.2 |  5.5 | 1.20 : 1 |
|         |          |  6  | 17.8 |  5.8 | 56.7 |  9.6 |  5.4 | 1.07 : 1 |
| June 18 | 12 weeks |  1  | 34.6 |  8.0 | 38.2 | 14.7 |  5.6 | 1.42 : 1 |
|         |          |  6  | 33.4 |  7.6 | 44.5 | 15.0 |  6.7 | 1.14 : 1 |
| July 16 | 16 weeks |  1  | 52.8 | 12.1 | 55.6 | 16.3 |  9.1 | 1.33 : 1 |
|         |          |  6  | 54.4 | 10.6 | 46.2 | 19.1 |  8.8 | 1.20 : 1 |
| Aug. 16 | 20 weeks |  1  | 66.8 |  9.2 | 49.1 | 17.0 |  8.3 | 1.10 : 1 |
|         |          |  6  | 65.0 |  9.8 | 49.8 | 19.1 |  9.4 | 1.04 : 1 |
| Sept. 3 | 22 weeks |  1  | 84.3 | 10.4 | 45.7 | 17.6 |  8.0 | 1.31 : 1 |
|         |          |  6  | 86.3 | 10.2 | 45.3 | 17.3 |  7.8 | 1.30 : 1 |
|_________|__________|_____|______|______|______|______|______|__________|

The variations exhibited by these numbers are significant. It is clear,
on the other hand, that the assimilation of the furfuroids does not vary
in any important way with variations in conditions of atmosphere and
soil nutrition. They are essentially _tissue_-constituents, and only at
the flowering period is there any accumulation of these compounds in the
alkali-soluble form. It has been previously shown (ibid. 27, 1061)
that the proportion of furfuroids in the straw-celluloses of the
paper-maker differs but little from that of the original straws. For the
isolation of the celluloses the straws are treated by a severe process
of alkaline hydrolysis, to which, therefore, the furfuroid groups offer
equal resistance with the normal hexose groups with which they are
associated in the complex.

The furfuroids of the cereal straws are therefore not pentosanes. They
are original products of assimilation, and not subject to secondary
changes after elaboration such as to alter either their constitution or
their relationship to the normal hexose groups of the tissue-complex.


(1) CONSTITUTION OF THE CEREAL CELLULOSES

(Chem. Soc. J. 1896, 804).


(2) THE CARBOHYDRATES OF BARLEY STRAW

(Chem. Soc. J. 1896, 1604).


(3) THE CARBOHYDRATES OF THE CEREAL

STRAWS (Chem. Soc. J. 1897, 1001).


(4) THE CARBOHYDRATES OF BARLEY STRAW

(Chem. Soc. J. 1898, 459).

C. F. CROSS, E. J. BEVAN, and CLAUD SMITH.

These are a series of investigations mainly devoted to establishing the
identity of the furfural-yielding group which is a characteristic
constituent.

This 'furfuroid' while equally resistant to alkalis as the normal
cellulose group with which it is associated, is selectively hydrolysed
by acids. Thus straw cellulose dissolves in sulphuric acids of
concentration H_{2}SO_{4}.2H_{2}O - H_{2}SO_{4}.3H_{2}O, and on diluting
the normal cellulose is precipitated as a hydrate, and the furfuroid
remains in solution. But this sharp separation is difficult to control
in mass. By heating with a very dilute acid (1 p.ct. H_{2}SO_{4}) the
conditions are more easily controlled, the most satisfactory results
being obtained with 15 mins. heating at 3 atm. pressure.

(1) Operating in this way upon brewers' grains the furfuroid was
obtainable as the chief constituent of a solution for which the
following experimental numbers were determined:--Total dissolved solids,
28.0 p.ct. of original 'grains'; furfural, 39.5 p.ct. of total dissolved
solids, as compared with 12.5 p.ct. of total original grains; cupric
reduction (calc. to total solids), 110 (dextrose = 100) osazone; yield
in 3 p.ct. solution, 35 p.ct. of weight of total solids.

                                  Pentosazone
     Analysis       N  17.1  17.3    17.07
                    C  62.5  62.3    62.2
                    H   6.4   6.5     6.1
     Melting-point                146°-153°

From these numbers it is seen that of the total furfuroids of the
original 'grains' 84 p.ct. are thus obtained in solution in the fully
hydrolysed form, which is that of a pentose or pentose derivative. It
was, however, found impossible to obtain any crystallisation from the
neutralised (BaCO_{3}) and concentrated solution, the syrup being kept
for some weeks in a desiccator. It was noted at the same time that the
colour reaction of the original solution with phloroglucol and
hydrochloric acid was a deep violet, in contradistinction to the
characteristic red of the pentoses. On oxidation with hydrogen peroxide,
in the proportion of 1 mol. H_{2}O_{2} to 1 mol. of the carbohydrate in
solution, carbonic anhydride was formed in quantity = 20.0 p.ct. of the
latter.

Fermentation (yeast) experiments also showed a divergence from the
resistant behaviour of the pentoses, a considerable proportion of the
furfuroid disappearing in a normal fermentation.

(2) The quantitative methods above described were employed in
investigating the barley plant at different stages of its growth. The
green plant was extracted with alcohol, the residue freed from alcohol
and subjected to acid hydrolysis.

The hydrolysed extract was neutralised and fermented. In the early
stages of growth the furfuroids were completely fermented, i.e.
disappeared in the fermentation. In the later stages this proportion
fell to 50 p.ct. In the earlier stages, moreover, the normal hexose
constituents of the permanent tissue were hydrolysed in large proportion
by the acid, whereas in the matured straw the hydrolysis is chiefly
confined to the furfuroids. In the early stages also the permanent
tissue yields an extract with relatively low cupric reduction, showing
that the carbohydrates are dissolved by the acid in a more complex
molecular condition.

These observations confirm the view that the furfuroids take origin in a
hexose-pentose series of transformations. The proportion of furfuroid
groups to total carbohydrates varies but little, viz. from 1/3 in the
early stages to a maximum of 1/4 at the flowering period. At this period
the differentiation of the groups begins to be marked.

Taking all the facts of (1) and (2), they are not inconsistent with the
hypothesis of an internal transformation of a hexose to a
pentose-monoformal. Such a change of position and function of oxygen
from OH to CO within the group --CH.OH-- is a species of internal
oxidation which reverses the reduction of formaldehyde groups in
synthesising to sugars, and appears therefore of probable occurrence.

These constitutional problems are followed up in (3) by the indirect
method of differentiating the relationships of these furfuroids to yeast
fermentation, from those of the pentoses. Straw and esparto celluloses
are subjected to the processes of acid hydrolysis, and the neutralised
extracts fermented. With high furfural numbers indicating that the
furfuroids are the chief constituents of the extract, there is an active
fermentation with production of alcohol. The cupric reduction falls in
greater ratio to the original (unfermented) than the furfural.
Observations on the pure pentoses--xylose and arabinose added to
dextrose solutions, and then exposed to yeast action--show that in a
vigorous fermentation not unduly prolonged the pentoses are unaffected,
but that they do come within the influence of the yeast-cell when the
latter is in a less vigorous condition, and when the hexoses are not
present in relatively large proportion.

(4) The observations on the growing plant were resumed with the view of
artificially increasing the differentiation of the two main groups of
carbohydrates. From a portion of a barley crop the inflorescence was
removed as soon as it appeared. The crop was allowed to mature, and a
full comparison instituted between the products of normal and abnormal
growth. With a considerable difference in 'permanent tissue' (13 p.ct.
less) and a still greater defect in cellulose (24 p.ct.), the constants
for the furfuroids in relation to total carbohydrates were unaffected by
the arrested development. This was also true of the behaviour of the
hydrolysed extracts (acid processes) to yeast fermentation.

(5) The extract obtained from the brewers' grains by the process
described in (2) was investigated in relation to animal digestion. It
has been now generally established that the furfuroids as constituents
of fodder plants are digested and assimilated in large proportion in
passing through animal digestive tracts, and in this respect behave
differently from the pentoses. The furfuroids being obtained, as
described, in a fully hydrolysed condition (monoses) the digestion
problem presented itself in a new aspect, and was therefore attacked.

The result of the comparative feeding experiments upon rabbits was to
show that in this previously hydrolysed form the furfuroids are almost
entirely digested and assimilated, no pentoses, moreover, appearing in
the urine.

Generally we may sum up the present solution of the problem of the
relationship of the furfuroids to plant assimilation and growth as
follows:--The pentoses are not produced as such in the process of
assimilation; but furfural-yielding carbohydrates are produced directly
and in approximately constant ratio to the total carbohydrates; they are
mainly located in the permanent tissue; in the secondary changes of
dehydration, &c., accompanying maturation they undergo such
differentiation that they become readily separable by processes of acid
hydrolysis from the more resistant normal celluloses; but in relation to
alkaline treatments they maintain their intimate union with the latter.
They are finally converted into pentoses by artificial treatments, and
into pentosanes in the plant, with loss of 1 C atom in an oxidised form.
The mechanism of this transformation of hexoses into pentoses is not
cleared up. It is independent of external conditions, e.g.
fertilisation and atmospheric oxidations, and is probably therefore a
process of internal rearrangement of the character of an oxidation.


ZUR KENNTNISS DER IN DEN MEMBRANEN DER PILZE ENTHALTENEN BESTANDTHEILE.

E. WINTERSTEIN (Ztschr. Physiol. Chem., 1894, 521; 1895, 134).

~ON THE CONSTITUENTS OF THE TISSUE OF FUNGI.~

(p. 87) These two communications are a contribution of fundamental
importance, and may be regarded as placing the question of the
composition of the celluloses of these lowest types on a basis of
well-defined fact. In the first place the author gives an exhaustive
bibliography, beginning with the researches of Braconnot (1811), who
regarded the cellular tissue of these organisms as a specialised
substance, which he termed 'fungin.' Payen rejects this view, and
regards the tissue, fully purified by the action of solvents, as a
cellulose (C_{6}H_{10}O_{5}). This view is successively supported by
Fromberg [Mulder, Allg. Phys. Chem., Braunschweig, 1851], Schlossberger
and Doepping [Annalen, 52, 106], and Kaiser. De Bary, on a review of the
evidence, adopts this view, but, as the purified substance fails to give
the characteristic colour-reactions with iodine, he uses the qualifying
term 'pilzcellulose' [Morph. u. Biol. d. Pilze u. Flechten, Leipzig,
1884].

C. Richter, on the other hand, shows that these reactions are merely a
question of methods of purification or preparation [Sitzungsber. Acad.
Wien, 82, 1, 494], and considers that the tissue-substance is an
ordinary cellulose, with the ordinary reactions masked by the presence
of impurities. In regard to the lower types of fungoid growth, such as
yeast, the results of investigators are more at variance. The researches
of Salkowski (p. 113) leave little doubt, however, that the
cell-membrane is of the cellulosic type.

The author's researches extend over a typical range of products obtained
from _Boletus edulis, Agaricus campestris, Cantharellus cibarius,
Morchella esculenta, Polyporus officinalis, Penicillium glaucum_, and
certain undetermined species. The method of purification consisted
mainly in (a) exhaustive treatments with ether and boiling alcohol,
(b) digestion with alkaline hydrate (1-2 p.ct. NaOH) in the cold,
(c) acid hydrolysis (2-3 p.ct. H_{2}SO_{4}) at 95°-100°, followed by a
chloroxidation treatment by the processes of Schulze or Hoffmeister, and
final alkaline hydrolysis.

The products, i.e. residues, thus obtained were different in essential
points from the celluloses isolated from the tissues of phanerogams
similarly treated. Only in exceptional cases do they give blue reactions
with iodine in presence of zinc chloride or sulphuric acid. The
colourations are brown to red. They resist the action of cuprammonium
solutions. They are for the most part soluble in alkaline hydrate
solution (5-10 p.ct. NaOH) in the cold. They give small yields (1-2
p.ct.) of furfural on boiling with 10 p.ct. HCl.Aq.

Elementary analyses gave the following results, which are important in
establishing the presence of a notable proportion of nitrogen, which has
certainly been overlooked by the earlier observers:--

 _________________________________________________________
|                                      |      |     |     |
|     'Cellulose' or residue from      |  C   |  H  |  N  |
|______________________________________|______|_____|_____|
|                                      |      |     |     |
| Boletus edulis (Schulze process)     | 42.4 | 6.5 | 3.9 |
| Boletus edulis (Hoffmeister process) | 44.6 | 6.3 | 3.6 |
| Polyporus off.                       | 43.7 | 6.5 | 0.7 |
| Cantharellus cib.                    | 44.9 | 6.8 | 3.0 |
| Agaricus campestris                  | 44.3 | 6.6 | 3.6 |
| Botrytis                             | 42.1 | 6.3 | 3.9 |
| Penicillium glaucum                  |      |     | 3.3 |
| Morchella esculenta                  |      |     | 2.5 |
|______________________________________|______|_____|_____|

It is next shown that this residual nitrogen is not in the form of
residual proteids (1) by direct tests, all of which gave negative
results, and (2) indirectly by the high degree of resistance to both
alkaline and acid hydrolysis. The 'celluloses' are attacked by boiling
dilute acids (1 p.ct. H_{2}SO_{4}), losing in weight from 10 to 23
p.ct., the dissolved products having a cupric reduction value about 50
p.ct. that of an equal weight of dextrose. As an extreme hydrolytic
treatment the products were dissolved in 70 p.ct. H_{2}SO_{4}, allowed
to stand 24 hours, then considerably diluted (to 3 p.ct. H_{2}SO_{4})
and boiled to complete the inversion. The yields of glucose, calculated
from the cupric reduction, were as follows:--

     Boletus edulis       65.2 p.ct.
     Polyporus off.       94.7   "
     Agaricus campestris  59.1   "
     Morchella esculenta  60.1   "
     Cantharellus cib.    64.9   "
     Botrytis             60.8   "

It will be noted that the exceptionally high yield from the Polyporus
cellulose is correlated with its exceptionally low nitrogen. By actual
isolation of a crystalline dextrorotary sugar, by preparations of
osazone and conversion into saccharic acid, it was proved that dextrose
was the main product of hydrolysis. The second main product was shown to
be acetic acid, the yield of which amounted to 8 p.ct. in several cases.

Generally, therefore, it is proved that the more resistant tissue
constituents of the fungi are not cellulose, but a complex of
carbohydrates and nitrogenous groups in combination, the former being
resolved into glucoses by acid hydrolysis, and the latter yielding
acetic acid as a characteristic product of resolution together with the
nitrogenous groups in the form of an uncrystallisable syrup.

In the further prosecution of these investigations (2) the author
proceeded from the supposition of the identity of the nitrogenous
complex of the original with chitin, and adopted the method of
Ledderhose (Ztschr. Physiol. Chem. 2, 213) for the isolation of
glucosamin hydrochloride, which he succeeded in obtaining in the
crystalline form. In the meantime E. Gilson had shown that these tissue
substances in 'fusion' with alkaline hydrates yield a residue of a
nitrogenous product (C_{14}H_{28}N_{2}O_{10}), which is soluble in
dilute acids [Recherches Chim. sur la Membrane Cellulaire des
Champignons, La Cellule, v. II, pt. 1]. This residue, which was termed
mycosin by Gilson, has been similarly isolated by the author. It is
proved, therefore, that the tissues of the fungi do contain a product
resembling chitin. [See also Gilson, Compt. Rend. 120, 1000.] This
constituent is in intimate union with the carbohydrate complex, which is
resolved similarly to the hemicelluloses. Various intermediate terms of
the hydrolytic series have been isolated. But the only fully identified
product of resolution is the dextrose which finally results.


UEBER DIE KOHLENHYDRATE D. HEFE.

E. SALKOWSKI (Berl. Ber., 27, 3325).

~ON THE CARBOHYDRATES OF YEAST.~

The author has isolated the more resistant constituents of the
cell-membrane by boiling with dilute alkalis, and exhaustively purifying
with alcohol and ether.

The residue was only a small percentage (3-4 p.ct) of the original, and
retained only 0.45 p.ct. N.

It was heated in a digester with water at 2-3 atm. steam-pressure, and
thus resolved into approximately equal portions of soluble cellulose
(a) and insoluble (b). The latter, giving no colour-reaction with
iodine, is termed achroocellulose; the former reacts, and is therefore
termed erythrocellulose. The former is easily separated from its
opalescent solution. It has the empirical composition of cellulose. In
the soluble form it resembles glycogen. The achroocellulose is isolated
in the form of horny or agglomerated masses. It appears to be resolved
by ultimate hydrolysis into dextrose and mannose.




SECTION V. FURFUROIDS, i.e. PENTOSANES AND FURFURAL-YIELDING
CONSTITUENTS GENERALLY


(1) ~Reactions of the Carbohydrates with Hydrogen Peroxide.~

C. F. CROSS, E. J. BEVAN, and CLAUD SMITH (J. Chem. Soc., 1898, 463).


(2) ~Action of Hydrogen Peroxide on Carbohydrates in the Presence of
Ferrous Salts.~

R. S. MORRELL and J. M. CROFTS (J. Chem. Soc., 1899, 786).


(3) ~Oxidation of Furfuraldehyde by Hydrogen Peroxide.~

C. F. CROSS, E. J. BEVAN, and T. HEIBERG (J. Ch. Soc., 1899, 747).


(4) EINWIRKUNG VON WASSERSTOFFHYPEROXID AUF UNGESÄTTIGTE
KOHLENWASSERSTOFFE.

C. F. CROSS, E. J. BEVAN, and T. HEIBERG (Berl. Ber., 1900, 2015).

~ACTION OF HYDROGEN PEROXIDE ON UNSATURATED HYDROCARBONS.~

The above series of researches grew out of the observations incidental
to the use of the peroxide on an oxidising agent in investigating the
hydrolysed furfuroids (102). Certain remarkable observations had
previously been made by H. J. H. Fenton (Ch. Soc. J., 1894, 899; 1895,
774; 1896, 546) on the oxidation of tartaric acid by the peroxide,
acting in presence of ferrous salts, the --CHOH--CHOH-- residue losing
H_{2} with production of the unsaturated group, --OH.C=C.OH--. These
investigations have subsequently been considerably developed and
generalised by Fenton, but as the results have no immediate bearing on
our main subject we must refer readers to the J. Chem. Soc., 1896-1900.

From the mode of action diagnosed by Fenton it was to be expected that
the CHOH groups of the carbohydrates would be oxidised to CO groups, and
it has been established by the above investigations (1) and (2) that the
particular group to be so affected in the hexoses is that contiguous to
the typical

        |
     --CO

group. There results, therefore, a dicarbonyl derivative ('osone'),
which reacts directly with 2 mol. phenyl hydrazine in the cold to form
an osazone. This was directly established for glucose, lævulose,
galactose, and arabinose (2). While this is the main result, the general
study of the product shows that the oxidation is not simple nor in
direct quantitative relationship to the H_{2}O_{2} employed. The
molecular proportion of the aldoses affected appears to be in
considerable excess, and the reaction is probably complicated by
interior rearrangement.

In the main, the original aldehydic group resists the oxidation. But a
certain proportion of acid products are formed, probably tartronic acid.
On distillation with condensing acids a large proportion of volatile
monobasic acids (chiefly formic) are obtained. The proportion of
furfural obtained amounts to 3-4 per cent. of the weight of the original
carbohydrate.

Since the general result of these oxidations is the substitution of an
OH group for an H atom, it was of interest to determine the behaviour of
furfural with the peroxide. The oxidation was carried out in dilute
aqueous solution of the aldehyde at 20°-40°, using 2-3 mols. H_{2}O_{2}
per 1 mol. C_{5}H_{4}O_{2}. The main product is a hydroxyfurfural, which
was separated as a hydrazone. A small quantity of a monobasic acid was
formed, which was identified as a hydroxypyromucic acid. Both aldehyde
and acid appear to be the alpha beta derivatives. The aldehyde gives
very characteristic colour reactions with phloroglucinol and resorcinol
in presence of hydrochloric acid, which so closely resemble those of the
lignocelluloses that there is little doubt that these particular
reactions must be referred to the presence of the hydroxyfurfural as a
normal constituent.

The study of these oxidations was then extended to typical unsaturated
hydrocarbons--viz. acetylene and benzene. (4) From the former the main
product was acetic acid, but the attendant formation of traces of ethyl
alcohol indicates that the hydrogen of the peroxide may take a direct
part in this and other reactions. This view receives some support from
the fact that the interaction of the H_{2}O_{2} with permanganates has
now been established to be an oxidation of the H_{2} of the peroxide by
the permanganate oxidation, with liberation, therefore, of the O_{2} of
the peroxide as an unresolved molecule [Baeyer].

Benzene itself is also powerfully attacked by the peroxide when shaken
with a dilute solution in presence of iron salts. The products are
phenol and pyrocatechol, with some quantity of an amorphous product
probably formed by condensation of a quinone with the phenolic products
of reaction.

       *       *       *       *       *

These types of oxidation effects now established give a definite
significance to the physiological functions of the peroxide, which is a
form of 'active oxygen' of extremely wide distribution. It would have
been difficult _a priori_ to devise an oxidant without sensible action
on aldehydic groups, yet delivering a powerful attack on hydrocarbon
rings; or to have suggested a synthesis of the sugars from tartaric acid
with a powerful oxidising treatment as the first and essential stage in
the transformation.

Our present knowledge of such actions and effects suggests a number of
new clues to genetic relationships of carbon compounds within the plant.
The conclusion is certainly justified that the origin of the pentoses is
referable to oxidations of the hexoses, in which this form of 'active
oxygen' plays an important part.

We must note here the researches of O. Ruff, who has applied these
oxidations with important results in the systematic investigation of the
carbohydrates.


UEBER DIE VERWANDLUNG DER _D_-GLUCONSÄURE IN _D_-ARABINOSE (Berl. Ber.,
1898, 1573).

~CONVERSION OF _D_-GLUCONIC ACID INTO _D_-ARABINOSE.~

       *       *       *       *       *

_D_ UND _L_ ARABINOSE (_Ibid._ 1899, 550).

       *       *       *       *       *

ZUR KENNTNISS DER OXYGLUCONSÄURE (_Ibid._ 1899, 2269).

~ON OXYGLUCONIC ACID.~

Ruff in these researches has realised a simple and direct transition
from the hexoses to the pentoses. By oxidising gluconic acid with the
peroxide the beta --CHOH-- group is converted into carbonyl at the same
time that the terminal COOH [alpha] is oxidised to CO_{2}. The yields of
the resulting pentose are large. Simultaneously there is formed an
oxygluconic acid, which appears to be a ketonic acid of formula
--CH_{2}OH.CO.(CHOH)_{3}.COOH--.

From these results we see a further range of physiological
probabilities; and with the concurrent actions of oxygen in the forms of
or related to hydrogen peroxide on the one side, and ozone on the other,
we are able to account in a simple way for the relationships of the
'furfuroid' group, which may include a number of intermediate terms in
the hexose-pentose series.

Following in this direction of development of the subject is a study of
the action of persulphuric acid upon furfural.


EINWIRKUNG DES CARO'SCHEN REAGENS AUF FURFURAL.

C. F. CROSS, E. J. BEVAN, and J. F. BRIGGS (Berl. Ber., 1900, 3132).

Regarding this reagent as another form of 'active oxygen,' it is
important to contrast its actions with those of the hydrogen peroxide.
Instead of the beta-hydroxyfurfural (_ante_, 115) we obtain the
delta-aldehyde as the first product. The aldehydic group is then
oxidised, and as a result of attendant hydrolysis the ring is broken
down and succinic acid is formed, the original aldehydic group of the
furfural being split off in the form of formic acid. The reactions take
place at the ordinary temperature and with the dilute form of the
reagent described by Baeyer and Villiger (Ber. 32, 3625). These results
have some special features of interest. The alpha delta-hydroxyfurfural
has similar colour reactions to those of the alpha beta-derivative, and
may also therefore be present as a constituent of the lignocelluloses.
The tendency to attack in the 1·4 position in relation to an aldehydic
group further widens the capabilities of 'active oxygen' in the plant
cell. Lastly, this is the simplest transition yet disclosed from the
succinyl to furfural grouping, being effected by a regulated proportion
of oxygen, and under conditions of reaction which may be described as of
the mildest. In regard to the wide-reaching functions of asparagin in
plant life, we have a new suggestion of genetic connections with the
furfuroids.


VERGLEICH DER PENTOSEN-BESTIMMUNGSMETHODEN VERMITTELST PHENYLHYDRAZIN
UND PHLOROGLUCIN.

M. KRÜGER (Inaug.-Diss., Göttingen, 1895).

~COMPARISON OF METHODS OF ESTIMATING FURFURAL AS HYDRAZONE AND
PHLOROGLUCIDE.~

The author traces the development of processes of estimating furfural
(1) by precipitation with ammonia (furfuramide), (2) by volumetric
estimation with standardised phenylhydrazine, (3) by weighing the
hydrazone.

In 1893 (Chem. Ztg. 17, 1745) Hotter described a method of quantitative
condensation with pyrogallol requiring a temperature of 100°-110° for
two hours. The insoluble product collected, washed, dried at 103°, and
weighed, gives a weight of 1.974 grm. per 1 grm. furfural.

Councler substitutes phloroglucinol for pyrogallol, with the advantage
of doing away with the digestion at high temperature. (_Ibid._ 18, 966.)
This process, requiring the presence of strong HCl, has the advantage of
being applied directly to the acid distillate, in which form furfural is
obtained as a product of condensation of pentoses, &c. A comparative
investigation was made, precipitating furfural (a) as hydrazone in
presence of acetic acid, and (b) as phloroglucide in presence of HCl
(12 p.ct). In (a) by varying the weights of known quantities of
furfural, and using the factor, hydrazone × 0.516 [+ 0.0104] in
calculating from the weights of precipitates obtained, the maximum
variations from the theoretical number were +1.71 and -1.74. In (b) it
was found necessary to vary the factor from 0.52 to 0.55 in calculating
from phloroglucide to furfural. The greatest _total_ range of variation
was found to be 2.5 p.ct. The phenol process is therefore equally
accurate, has the advantages above noted, and, in addition, is less
liable to error from the pressure in the distillates obtained from
vegetable substances of volatile products, e.g. ketonic compounds,
accompanying the furfural.

This method has been criticised by Helbel and Zeisel [Sitz.-ber, Wiener
Akad. 1895, 104, ii. p. 335] on two grounds of error, viz. (1) the
presence of diresorcinol in all ordinary preparations of phloroglucinol,
and (2) changes in weight of the precipitate of phloroglucide on drying.
The process was carried out comparatively with ordinary preparations,
and with specially pure preparations of the phenol. The quantitative
results were identical. The criticisms in question are therefore
dismissed. Although the process is to be recommended for its simplicity
and the satisfactory concordance of results it is to be noted that it
rests upon an empirical basis, since the phloroglucide is not formed by
the simple reaction 2 [C_{5}H_{4}O_{2} + C_{6}H_{6}O_{3}] - H_{2}O =
C_{22}H_{18}O_{9}, but appears to have the composition
C_{16}H_{12}O_{6}.

In part ii. of this paper the author discusses the question of the
probable extent in the sense of diversity of constitution of
furfural-yielding constituents of plant-tissues. Glucoson was isolated
from glucosazon, and found to yield 2.9-3.6 p.ct. furfural. Gluconic
acid distilled with hydrochloric acid gave traces of furfural; so also
with sulphuric acid and manganic oxide.

Starch was oxidised with permanganate, and a mixture of products
obtained of which one gave a characteristic violet colouration with
phloroglucol, with an absorption-band at the D line. On distilling with
HCl furfural was obtained in some quantity. The product in question was
found to be very sensitive to the action of bases, and was destroyed by
the incidental operation of neutralising the mixture of oxidised
products with calcium carbonate. It was found impossible to isolate the
compound.


UNTERSUCHUNGEN UEBER DIE PENTOSANBESTIMMUNG MITTELST DER
SALZSÄURE-PHLORO-GLUCIN-METHODE.[8]

E. KRÖBER (Journ. f. Landwirthschaft, 1901, 357).

~INVESTIGATION OF THE HYDROCHLORIC ACID-PHLOROGLUCINOL METHOD OF
DETERMINING PENTOSANES.~

This paper is the most complete investigation yet published of the now
well-known method of precipitating and estimating furfural in acid
solution by means of the trihydric phenol. In the last section of the
paper is contained the most important result, the proof that the
insoluble phloroglucide is formed according to the reaction

     C_{5}H_{4}O_{2} + C_{6}H_{6}O_{3} - 2H_{2}O = C_{11}H_{6}O_{3},

also, by varying the proportions of the pure reagents interacting, that
the condensation takes place invariably according to this equation.

Incidentally the following points were also established:--The solubility
of the phloroglucide, under the conditions of finally separating in a
condition for drying and weighing, is 1 mgr. per 100 c.c. of total
solution, made up of the original acid solution, in which the
precipitation takes place, and the wash-water required to purify from
the acid. The phloroglucide is hygroscopic, and must be weighed out of
contact with the air. The presence of diresorcinol is without influence
on the result, provided a sufficient excess of actual phloroglucinol is
employed. Thus even with a preparation containing 30 p.ct. of its weight
of diresorcinol the influence of the latter is eliminated, provided a
weight be taken equal to twice that of the furfural to be precipitated.
The phenol must be perfectly dissolved by warming with dilute HCl (1.06
sp.gr.) before adding to the furfural solution. For collecting the
precipitate of phloroglucide the author employs the Gooch crucible.

The paper contains a large number of quantitative results in proof of
the various points established, and concludes with elaborate tables,
giving the equivalents in the known pentoses and their anhydrides for
any given weight of phloroglucide from 0.050 to 0.300 grm.


UEBER DEN PENTOSAN-GEHALT VERSCHIEDENER MATERIALIEN.

B. TOLLENS and H. GLAUBITZ (J. für Landwirthschaft, 1897, 97).

~ON THE PENTOSANE CONSTITUENTS OF FODDER-PLANTS AND MALT.~

(p. 171) (a) The authors have re-determined the yield of furfural from
a large range of plant-products, using the phloroglucol method. The
numbers approximate closely to those obtained by the hydrazone method.
The following may be cited as typical:

     Substance              Furfural p.ct.

     Rye (Göttingen)            6.03
     Wheat (square head)        4.75
     Barley (peacock)           4.33
     Oats (Göttingen)           7.72
     Maize (American)           3.17
     Meadow hay                11.63
     Bran (wheat)              13.06
     Malt                       6.07
     Malt-sprouts               8.56
     Sugar-beet (exhausted)    14.95

(b) A comparison of wheat with wheat bran, &c. was made by grinding in
a mortar and 'bolting' the flour through a fine silk sieve. The results
showed:

                              Furfural p.ct.
     Original wheat               4.75
     Fine flour                   1.73
     Bran (24 p.ct. of wheat)    11.25
     Wheat-bran of commerce      13.06

It is evident that the pentosanes of wheat are localised in the more
resistant tissues of the grain.

(c) An investigation of the products obtained in the analytical
process for 'crude fibre' gave the following:

(1) In the case of brewers' grains:

     100 grms. grains       gave furfural   = 29.43 pentosane
                                              ---------------
      20   "   crude fibre       "          =  2.52
     Acid extract                "          = 22.76
     Alkali  "                   "          =  1.20
     Deficiency from total of original grains  2.95
                                              -----

                                              29.43

(2) In the case of meadow hay:

The crude fibre (30 p.ct.) obtained retained about one fourth (23.63
p.ct.) of the total original pentosanes.

(d) An investigation of barley-malt, malt-extract or wort, and
finished beer showed the following: An increase of furfuroids in the
process of malting, 100 pts. barley with 7.97 of 'pentosane' yielding 82
of malt with 11.18 p.ct. 'pentosane'; confirming the observations of
Cross and Bevan (Ber. 28, 2604). Of the total furfuroids of malt about
1/4 are dissolved in the mashing process. In a fermentation for lager
beer it was found that about /10 of the total furfuroids of the malt
finally survive in the beer; the yield of furfural being 2.92 p.ct. of
the 'total solids' of the beer. In a 'Schlempe' or 'pot ale,' from a
distillery using to 1 part malt 4 parts raw grain (rye), yield of
furfural was 9 p.ct. of the total solids.

In a general review of the relationships of this group of plant-products
it is pointed out that they are largely digested by animals, and
probably have an equal 'assimilation' value to starch. They resist
alcoholic fermentation, and must consequently be taken into account as
constituents of beers and wines.


UEBER DAS VERHALTEN DER PENTOSANE DER SAMEN BEIM KEIMEN.[9]

A. SCHÖNE and B. TOLLENS (Jour. f. Landwirthschaft, 1901, 349).

~BEHAVIOUR OF PENTOSANES OF SEEDS IN GERMINATION.~

The authors have investigated the germination of barley, wheat, and
peas, in absence of light, and generally with exclusion of assimilating
activity, to determine whether the oxidation with attendant loss of
weight, which is the main chemical feature of the germination proper,
affects the pentosanes of the seeds. The following are typical of the
quantitative results obtained, which are stated in absolute weights, and
not percentages.

 _____________________________________________________________
|        |               |                    |               |
|        | Original seed |      Malt or       | Pentosane in  |
|        |               | germinated product |               |
|        |               |                    |_______________|
|        |               |                    |       |       |
|        |      A        |         B          |   A   |   B   |
|________|_______________|____________________|_______|_______|
|        |               |                    |       |       |
| Barley |    500.00     |       434.88       | 39.58 | 40.38 |
|   "    |    500.00     |       442.26       | 40.52 | 41.17 |
| Peas   |    300.00     |       286.60       | 15.25 | 15.97 |
|________|_______________|____________________|_______|_______|

The authors conclude generally that there is a slight absolute increase
in the pentosanes, and that the pentosanes do not belong to those
reserve materials which undergo destructive oxidation during
germination.

In this they confirm the previously published results of De Chalmot,
Cross and Bevan, and Gotze and Pfeiffer.


UEBER DEN GEHALT DER BAUMWOLLE AN PENTOSAN.

H. SURINGAR and B. TOLLENS (Ztschr. angew. Chem., 1897, I).

~PENTOSANE CONSTITUENTS OF COTTON.~

(p. 290) It has been stated by Link and Voswinkel (Pharm. Centralhalle,
1893, 253), that raw cotton yields 'wood gum' as a product of
hydrolysis. The authors were unable to obtain any pentoses as products
of acid hydrolysis of raw cotton, and traces only of furfural-yielding
carbohydrates. They conclude that raw cotton contains no appreciable
quantity of pentosane.

FOOTNOTES:

[8] This paper appears during the printing of the author's original MS.

[9] This paper appears during the printing of the author's original MS.




SECTION VI. THE LIGNOCELLULOSES


(p. 131) ~Lignocellulose Esters.~--By a fuller study of the ester
reactions of the normal celluloses we have been able to throw some light
on the constitutional problems involved; and we have extended the
investigations to the jute fibre as a type of the lignocelluloses, from
the results of which we get a clearer idea of the relationships of the
constituent groups.

Taking the empirical expression for the complex, i.e. the entire
lignocellulose, the formula C_{12}H_{18}O_{9}, we shall be able to
compare the ester derivatives with those of the celluloses, which we
have also referred to a C_{12} unit. But we shall require also to deal
with the constituent groups of the complex, which for the purposes of
this discussion may be regarded as (a) a cellulose of normal
characteristics--cellulose alpha; (b) a cellulose yielding furfural on
boiling with condensing acids--cellulose beta; and (c) a much
condensed, and in part benzenoid, group which we may continue to term
the lig_none_ group.

The latter has been specially examined with regard to its proportion of
OH groups, as a necessary preliminary to the investigation of esters, in
producing which the entire complex is employed. It will be shown that
the ester groups can be actually localised in various ways, as in the
main entering the cellulose residues alpha and beta. But that the
lignone group takes little part in the reactions may be generally
concluded on the evidence of its non-reactivity as an isolated
derivative, (1) By chlorination, &c. it is isolated in the form of an
amorphous body, but of constant composition, represented by the formula
C_{19}H_{18}Cl_{4}O_{9}. This compound, soluble in acetic anhydride, was
boiled with it for six hours after adding fused sodium acetate, and the
product separated by pouring into water. The dilute acid filtered from
the product contained no hydrochloric acid nor by-products of action.
The product showed an increase of weight of 7.5 p.ct. For one acetyl per
1 mol. C_{19}H_{18}Cl_{4}O the calculated increase is 8.0 p.ct. It is
evident from the nature of the derivative that this result cannot be
further verified by the usual analytical methods. (2) The chlorinated
derivative is entirely soluble in sodium sulphite solution. This
solution, shaken with benzoyl chloride, with addition of sodium hydrate
in successive portions, shows only a small formation of insoluble
benzoate, which separates as a tarry precipitate. (3) The empirical
formula of the lignone complex in its isolated forms indicates that very
little hydrolysis occurs in the processes of isolation. Thus the
chlorinated product we may assume to be derived from the complex
C_{19}H_{22}O_{9}. In the soluble by-products from the bisulphite
processes of pulping wood the lignone exists as a sulphonated
derivative, C_{24}H_{23}(OCH_{3})_{2}.(SO_{3}H).O_{7}. The original
lignone may be regarded as passing into solution as a still condensed
complex derived from C_{24}H_{26}O_{12} (Tollens). There is evidently
little attendant hydroxylation, and another essential feature is the
small molecular proportion of groups showing the typical sulphonation.

It appears that in the lignone the elements are approximately in the
relation C_{6} : H_{6} : O_{3}, and it may assist this discussion to
formulate the main constitutional types consistent with this ratio,
viz.:

     (1) The trihydroxybenzenes C_{6}H_{3}(OH)_{3}.

     (2) Methylhydroxyfurfural C_{5}H_{2}O.(OH)(CH_{3}).

                                  (CH_{3})
                                 /        \
     (3) Methylhydroxypyrone CO<C_{4}H_{2} O
                                 \        /
                                    (OH)

                             __________________
                            |                  |
     (4) Trioxycyclohexane CH--CH--CH--CH--CH--CH
                            \   /   \   /   \   /
                              O       O       O

It is probable that all these types of condensation are represented in
the lignone molecules, since the derivatives yielded in decompositions
of more or less regulated character are either directly derived from or
related to such groups. For the moment we pass over all but the general
fact of complexity and the marked paucity of OH-groups. It would be of
importance to be able to formulate the exact mode of union of the
lignone with the cellulose residues to constitute the lignocellulose.
The evidence, however, does not carry us farther than the probability of
union by complicated groups and of large dimensions; for not only is the
lignone isolated in condensed and non-hydroxylated forms, but the
cellulose also is not hydrated or hydrolysed further than in the ratio
3C_{6}H_{10}O_{5}.H_{2}O. It is probable, therefore, that the water
combining with the residues at the moment of their resolution is
relatively small.

Lastly, we have to remember, when dealing with the statistical results
of the reactions to be described, that the approximate proportions per
cent. of the constituent groups are:

     Cellulose alpha  65
          "    beta   15  =  100 lignocellulose.
     Lignone                  20

~Jute Benzoates.~--In preparing the jute for treatment it was boiled in
alkaline solution (1 per cent. NaOH), washed with water and dilute acid,
again washed, dried, and weighed.

In the ester reaction the reagents were employed in the proportion
C_{12}H_{18}O_{9} : 3NaOH : 2C_{6}H_{5}COCl. A series of quantitative
experiments gave yields of 126-130 p.ct. of benzoate [calculated for
monobenzoate 134 p.ct.].

The results were confirmed by ultimate analysis. The monobenzoate
therefore represents a maximum, and this molecular proportion is
one-half of that observed with the normal cellulose, calculated to the
same unit.

_Localisation of Benzoyl Group._--The entrance of the ester group
affects the typical colour reactions of the lignocellulose, which are
fainter. The ferric ferricyanide reaction almost disappears. The lignone
group is unaffected, and combines with chlorine as in the original. The
lignone chloride is removed by sodium sulphite solution, and the residue
is a _cellulose benzoate_. The loss of weight due to the elimination of
the lignone was 12.7 p.ct. Calculating per 100 of the original
lignocellulose this becomes 16. These statistics further confirm the
localisation of the benzoyl group in the cellulose residue. It is to be
noted that the presence of the benzoyl group renders the cellulose more
resistant to hydrolytic actions. Thus, to bring out this fact more
prominently, we may calculate the yield of residual cellulose benzoate
p.ct. of original jute, and we find it 109 p.ct. Taking a maximum
proportion for original cellulose--viz. 85--this benzoate represents a
yield of 129 p.ct., as against the theoretical for a monobenzoate, 132
p.ct.

_Furfural Numbers._--The percentage of furfural obtained by boiling with
HCl of 1.06 sp.gr. was 3.02 and 3.29 in separate determinations.
Calculating to the original lignocellulose, the percentage, 4.21,
indicates a considerable loss of the furfural-yielding constituent. The
effect was also apparent in the cellulose (benzoate) isolated by
chlorination &c., the percentage being 1.39 p.ct., and calculated to the
original jute benzoate 1.59 p.ct. Under the conditions adopted in
dissolving away the chlorinated lignone the original non-benzoated
lignocellulose would have yielded a cellulose giving 6 to 7 p.ct.
furfural.

Since the benzoyl group is hardly calculated to produce a constitutional
change affecting the furfural constants, it was necessary to examine the
effect of the preliminary alkaline treatment, and the change in the
furfuroid group was in fact localised in this reaction. It was found
that, on washing the alkali from the mercerised jute, and further
purifying the residue, this latter yielded only 4.2 p.ct. furfural [3.4
p.ct. on original fibre]. The alkaline solution and washings were
acidified and distilled from 10 p.ct. HCl, yielding an additional 3.6
p.ct. calculated to the original lignocellulose. By treatment with the
concentrated alkali, therefore, the furfuroid of the original
lignocellulose undergoes little change, but is selectively dissolved.
This point is under further investigation.

(p. 132) ~Acetylation of Lignocelluloses.~--Acetates are readily formed by
boiling the lignocelluloses with acetic anhydride. The derivatives
obtained from jute are only generally mentioned in the 1st edition (p.
132). A further study of the reactions in regard to special points has
led to some more definite results. The _yields_ of product by the
ordinary and simple process are 114-115 p.ct. But on analysing the
product an important discrepancy is revealed.

For the saponification we employ a solution of sodium ethylate in the
cold. The following numbers were obtained:

                                       Acetic acid  Hydrocellulose residue
                                           27.2            77.8
Calc. for diacetate on C_{12}H_{18}O_{9}   30.8            78.4

The derivative is approximately a diacetate, and on the assumption of a
simple ester reaction the yield should be 127 p.ct. Assuming that the
difference of 13 p.ct. is due to loss of water by internal condensation,
it appears that for each acetyl group entering, 2 mol. H_{2}O are split
off.

The jute acetate showed the normal reaction with chlorine, and the
lignone chloride was dissolved by treatment with sodium sulphite
solution. The fibrous residue was colourless. It proved to be a
cellulose acetate. The following numbers were obtained on
saponification:

                                          Acetic acid  Cellulose
                                              31.6       70.0
                                              30.9       68.8
Calc. for diacetate on C_{12}H_{20}O_{10}     29.4       79.9

The interpretation of these numbers appears to be this: in the original
reaction with the lignocellulose it is the cellulose residue which is
acetylated, and at the same time condensed. The cellulose residue which
undergoes condensation is not of the normal constitution, since the
normal cellulose is acetylated without condensation (see p. 41). On
saponification a portion of the cellulose, in again combining with
water, is hydrolysed to soluble products. The lignone group as it exists
in the lignocellulose has no free OH groups, and probably no free
aldehydic groups such as would react with the anhydride. Such groups
may, however, be originally present, and may take part in the internal
condensations which have been shown to occur. The furfural constants of
the lignocellulose are unaffected by the acetylation and condensation.
The hygroscopic moisture of the product is lowered from 10-11 p.ct. in
the original to 4.5 p.ct. The ferric ferricyanide reaction is inhibited
by the disappearance of the reactive groups, upon which this curious and
characteristic phenomenon depends (1st ed.).

~Acetylation of Benzoates.~--The cellulose dibenzoate (C_{12} basis) and
the jute monobenzoate were acetylated under comparative conditions The
results were as follows:

                                                   C_{12} basis
                                   Cellulose dibenzoate     Jute monobenzoate
                                              Calc. for             Calc. for
                                 Found     diacetate on  Found   diacetate on
Ester reaction                              dibenzoate           monobenzoate
Yield                            111 p.ct.    115 p.ct.  124 p.ct.  120 p.ct.

Saponification  {Cellulose}
                {Lignocellulose}    53.5        52.6        59.8       61.9
                 NaOH combining     21.3        23.9        28.4       24.3

From these results it would appear that the number of acetyl groups
entering the benzoates is the same as with the unbenzoylated fibres, the
benzoyl has no influence upon the hydroxyls as against the acetyl. At
the same time the internal condensation noticed in the acetylation of
the jute appears not to occur in the case of the benzoate.

~Nitric Esters.~--The numbers resulting from the quantitative study of the
ester reaction and product (1st ed. p. 133) show a very large divergence
of the yield of product from that which would be calculated from its
composition (N p.ct.) on the assumption that the ester reaction is
simple. We have repeated the results, and find with a yield of 145 p.ct.
that the product contains 11.8 p.ct. N.

The reaction

     C_{12}H_{18}O_{9} + 4HNO_{3} - 4H_{2}O

gives a tetranitrate with 11.5 p.ct. N and a yield of 159 p.ct. The
ester reaction, therefore, is not simple. There are two sources of the
loss of weight. The first of these is evident from the occurrence of
certain secondary reactions which result in the solution of a certain
proportion of the fibre substance in the acid mixture. To determine this
quantitatively we have devised a suitable variation of the method of
combustion with chromic acid (1st ed.).

The variation is required to meet the difficulty occasioned by the
tension of the nitric acid and products of deoxidation. The mixed acids
(10 c.c.), containing the organic by-products in solution, are
carefully diluted in a small flask with an equal volume of water,
preventing rise of temperature. Nitrous fumes are evolved during the
dilution. Strong sulphuric acid (15 c.c.) is now added, and the residue
of nitrous fumes expelled by a current of air, agitating the contents of
the flask from time to time. The combustion with CrO_{3} is then
proceeded with in the ordinary way. The gases evolved are measured
(total volume) and calculated to C present in the form of products
derived from the lignocellulose; and, assuming that this contains 47
p.ct. C, we may express the result approximately in terms of the fibre
substance. The method was controlled by blank experiments, in which
citric acid was taken as a convenient carbon compound for combustion.
The C found was 34.9 p.ct. as against 34.3 p.ct. calculated. By this
method we find that with maximum yields of nitrate at 143-145 p.ct. the
organic matter in solution in the acid mixture amounted to 4.9 to 5.3
p.ct. of the original lignocellulose.

Introducing this quantity as a correction of the yield of nitrate in the
original reaction, we must express the 143 parts as obtained from 95 of
fibre substance instead of 100.

The yield per molecule C_{12}H_{18}O_{9} (= 306) is therefore 462,
whereas for a tetranitrate formed by a simple ester reaction the yield
should be 486. The difference (24) represents 1.5 mol. H_{2}O split off
by internal condensation.

The correction for total N is relatively small, raising it from 11.5 to
12.2, which remains in close agreement with the experimental numbers.

_Monobenzoate._--Treated with the acid mixture yields a mixed nitrate.
The yield is 130 p.ct., and the product contains 7.6 p.ct. O.NO_{2}
nitrogen. These numbers approximate to those required for reaction with
4HNO_{3} groups, three of the residues entering the cellulose, and one
(as NO_{2}) the benzene ring of the substituting group. For such a
reaction the calculated numbers are: Yield 144 p.ct.; O.NO_{2} nitrogen
7.1 p.ct.

The experimental numbers require correcting for the amount of loss in
the form of products soluble in the acid mixture, viz. 7.6 p.ct.; but
they remain within the range of the experimental errors sufficiently to
show that the benzoyl group limits the number of OH groups taking part
in the ester reaction to three. The corrected yield per 1 mol. of jute
benzoate (410) is 576, as against the calculated 590 for 4HNO_{3}
reacting. A loss of 1H_{2}O per molecule by internal condensation is
therefore indicated.

~Denitration.~--The removal of the nitric groups from the esters is
effected by digestion with ammonium sulphide. But the reactions are by
no means simple. There is considerable hydrolysis of the lignocellulose
to soluble products. Thus the _tetranitrate_ yields only 46.4 of
denitrated fibre in place of the calculated 66. The product is a
cellulose, yielding only 0.5 per cent. furfural. The hydrolysed
by-products, moreover, when freed from sulphur and distilled from
hydrochloric acid, yielded only an additional 2.5 p.ct. furfural,
calculated to the original lignocellulose.

These statistics confirm the evidence that the ester reaction is not
simple. Such changes take place in the lignone-beta-cellulose complex
that they revert, not to their original form, but to soluble derivatives
of different constitution. The mixed nitrate from the benzoate is
denitrated to a cellulose amidobenzoate, which confirms the localisation
of a nitro-group in the benzoyl residue.

(p. 157) ~General Characteristics of the Lignocelluloses.~--Later
investigations have somewhat modified and simplified our views of the
constitution of the typical lignocellulose (jute), so far as this can be
dealt with by the statistics of its more important decompositions
(original, pp. 157-161).

~Cellulose.~--There is little doubt that the furfural-yielding groups of
the original are isolated in the form of the beta-cellulose. Tollens
emphasises this fact in his studies of cellulose-estimation methods. We
had previously shown (original, p. 159) that the yield of furfural is
not affected by the _chlorination_, but it appears from our numbers that
only 50 p.ct. of these groups remain in the isolated cellulose, the
residue undergoing hydrolysis to soluble compounds. In a carefully
regulated hydrolysis following the chlorination it appears that the
furfuroids are almost entirely conserved in the form of a cellulose.

Moreover, an investigation of the products dissolved by sodium sulphite
solution from the chlorinated fibre has shown that they are practically
free from furfuroids. This enables us to exclude the furfural-yielding
groups from the lignone complex. At the same time, through our later
studies of the hydroxyfurfurals, it is certain that these products are
represented in the fibre substance and probably in the lignone complex.

~Chlorination Statistics.~--It has been pointed out by a correspondent--to
whom we express our indebtedness--that we have made a mistake in
calculating the proportion of lignone from the ratio of the Cl combining
with the fibre substance or lignocellulose (p.ct), to that of the Cl
_present in_ the isolated lignone chloride (p.ct.). The lignocellulose
combines with chlorine in the ratio 100 : 8, but the lignone chloride
_containing_ 26.7 of chlorine means that, neglecting the hydrogen
substituted, 73 of lignone combine with the 27 of chlorine
approximately. On the uniform percentage basis the calculated proportion
of lignone would be 8/37, or a little over 20 p.ct.

In regard to the proportion of hydration attending the resolution, we
have shown on constitutional grounds that this must be relatively small.
Assuming approximately the formula C_{19}H_{22}O_{9} for the lignone
residue as it exists in combination, and the anhydride formula for the
cellulose, these revised statistics now appear, as regards the carbon
contents of the lignocellulose:

          Cellulose, 44.4 C; lignone, 57.8.
     80 × 44.4 ÷ 100 = 35.52
     20 × 57.8 ÷ 100 = 11.56
                       _____

                       47.08 p.ct. C in lignocellulose.

These conclusions are in accordance with the experimental facts, and,
taken together with the new evidence we have accumulated from a study of
the lignocellulose esters, we may sum up the constitutional points as
follows: The lignocellulose is a complex of

      Cellulose alpha        Cellulose beta                  Lignone
           65 p.ct.              15 p.ct.                       20
     Allied to the normal      Yielding furfural        One-third of which
          celluloses         approximately 50 p.ct.      is of benzenoid
                                                               type

The lignone contains but little hydroxyl. The celluloses are in
condensed hydroxyl union with the lignone, but the combination occurs by
complexes of relatively large molecular weight.


DIE CHEMIE DER LIGNOCELLULOSEN--EIN NEUER TYPUS.

W. C. HANCOCK and O. W. DAHL (Berl. Ber., 1895, 1558).

~Chemistry of Lignocelluloses--A New Type.~

The stem of the aquatic _Æschynomene aspera_ offers an exceptional
instance of structural modification to serve the special function of a
'float,' 1 grm. of substance occupying an apparent volume of 40-50 c.c.
This pith-like substance is morphologically a true wood (De Bary), and
the author's investigations now establish that it is in all fundamental
points of chemical composition a lignocellulose, although from its
colour reactions it has been considered by botanists to be a cellulose
tissue containing a proportion of lignified cells. Thus the main tissue
is stained blue by iodine in presence of hydriodic acid (1.5 s.g.), and
the colour is not changed on washing. The ordinary lignocelluloses are
stained a purple brown changed to brown on washing. The reactions with
phloroglucol and with aniline salts, characteristic of these compounds,
is only faintly marked in the main tissue, though strongly in certain
individual cells.

The following quantitative determinations, however, establish the close
similarity of the product to the typical lignocelluloses:

_Elementary Analysis._--C 46.55, H 6.7. _Furfural_ 11.6 p.ct., of which
there remained in the residue from alkaline hydrolysis (71 p.ct.) 8.0,
i.e. about 70 p.ct. The distribution of the furfuroids is therefore not
affected by the alkaline treatment.

_Chlorination._--The substance (after alkaline hydrolysis) takes up 16.9
p.ct. Cl, of which approximately one-half is converted into hydrochloric
acid.

_Methoxyl._--O.CH_{3} estimated = 2.9 p.ct.

_Ferric Ferricyanide Reaction._--Increase of weight due to blue cyanide
fixed (1) 75 p.ct., (2) 96 p.ct. Ratio, Fe : CN = 1 : 2, 4.

_Hydroxyl Reactions._--In the formation of nitric esters and in the
sulphocarbonate reaction the substance gave results similar to those
obtaining for the jute fibre.

These results establish the general identity of this peculiar product of
plant life with the lignocelluloses, at the same time that they show
that certain of the colour reactions supposed to characterise the
lignocelluloses are due to by-products which may or may not be present.

(p. 172) ~Composition of Elder Pith.~--In a systematic investigation of
the celluloses in relation to function we shall have to give special
attention to the parenchymatous tissues of all kinds. These are, for
structural reasons, not easily isolated, for which reason and their
generally 'inferior' functions they do not present themselves to
chemical observation in the same obvious way as do their fibrous
relatives. The pith of the elder, however, _is_ readily obtained in
convenient masses, and a preliminary investigation of the entire tissue
has established the following points:

The _reactions_ of the tissue are in all respects those of the
lignocelluloses.

_Composition._--Ash, 2.2 p.ct.; moisture in air-dry state, 12.3 p.ct.
Alkaline hydrolysis (loss): (a) 14.77, (b) 17.84. Cellulose (yield),
52.33 p.ct. Nitrate-reaction complicated by secondary reactions and
yields low, 90.95 p.ct. _Sulphocarbonate reaction:_ Resists the
treatment, less than 10 p.ct. passes into solution.

_Furfural._--The original tissue yields 7.13 p.ct.; the residue from
alkaline hydrolysis (b) 5.40 p.ct.

This tissue is, therefore, a lignocellulose having the chemical
characteristics typical of the group, but of less resistance to
hydrolytic actions.

The investigation will be prosecuted in reference to the cause of
differentiation in this latter respect. Probably the pectocelluloses are
represented in the tissue.


~The Insoluble Carbohydrates of Wheat (grain).~

H. C. SHERMAN (J. Amer. Chem. Soc., 1897, 291).

(p. 171) This is a study of the constituents of the cell-walls of wheat
grain. Bran was taken as the most convenient form of the raw material,
being freed from starch by treatment with malt extract, and further
treated (1) with cold dilute ammonia, (2) cold dilute soda lye (2 p.ct.
NaOH), and (3) boiling 0.1 p.ct. NaOH. The product retained only 1.25
p.ct. proteids, and yielded 15.62 p.ct. furfural.

_Acid Hydrolysis._--The product was boiled 30 mins. with dilute acid
(1.25 p.ct. H_{2}SO_{4}), and the solution boiled until the Fehling test
showed no further increase of monoses. At the limit the reducing power
of the dissolved carbohydrates was 91.3 p.ct., that of dextrose.
Converted into osazones the analysis showed them to be _pure
pentosazones_. The _hemicellulose_ of wheat is, therefore, according to
the author, _pure pentosane_.

_Residue._--This was a lignocellulose yielding 11.5 p.ct. furfural. It
was subjected to a series of treatments with ferric ferricyanide, and
the proportion of Prussian blue fixed was determined by increase of
weight, viz. from 10 p.ct. to 47 p.ct. according to the conditions. The
results confirmed those of Cross and Bevan first obtained with the
typical lignocellulose (jute).

_Chlorination._-The residue was boiled with dilute alkali, washed, and
exposed to chlorine gas. The resulting lignone chloride was isolated by
solution in alcohol, &c. It yielded 26.7 p.ct. Cl on analysis. In this
and its properties it appeared to be identical with the product isolated
by Cross and Bevan from jute, with the empirical formula
C_{19}H_{18}Cl_{4}O_{9}.

_Cellulose_ was isolated from the residue by three of the well-known
methods, and the following comparative numbers are noteworthy:

 _________________________________________________________________________
|                             |              |            |               |
|                             | F. Schulze   |   Lange    |  Cross and    |
|      Method                 | Dil. HNO_{3} | Fusion KOH |    Bevan      |
|                             |   KClO_{3}   |            | Chlorine, &c. |
|_____________________________|______________|____________|_______________|
|                             |              |            |               |
| Cellulose p.ct. obtained    |    66.0      | 39.3-43.1  |    66.5       |
| Furfural p.ct. of cellulose |     7.0      |   3.96     |     5.62      |
| Residual nitrogen           |     0.22     |   0.03     |     0.00      |
| Ferricyanide reaction,      |              |            |               |
|   Prussian blue fixed       |     6.04     |   0.89     |     0.92      |
|_____________________________|______________|____________|_______________|

The author remarks: 'It is evident no one feature can be urged as a
criterion in judging between the methods, but all must be taken into
consideration. Such a comparison shows the superiority of the
chlorination method.'

The cellulose is not of the normal (cotton) type, since on treatment
with sulphuric acid it dissolves with considerable discolouration, but
only to the extent of about 80 per cent. The dissolved monoses converted
into osazones were found to consist of hexoses only. The cellulose
treated with caustic soda solution (5 p.ct. NaOH) in the cold yielded 20
p.ct. of its weight of soluble constituents, but as the residue yielded
3.34 p.ct. furfural the attack of the alkali is by no means confined to
the furfuroids.

~Animal Digestion of the Constituents of Bran.~--Observations on a steer
fed upon wheat bran only established the following percentage digestion
of the several constituents:

     Soluble carbohydrates    96.9
     Starch                  100.0
     Free pentosanes          60.2
     Cellulose                24.8
     Lignin complex           36.7
     Proteid                  82.96
     Ether extract            42.73
     _____________________   ______

     Nitrogen-free extract    76.08
     Crude fibre              32.21


JOURNAL OF THE IMPERIAL INSTITUTE

(Research Department, Vols. 1-2, 1895-6).

(p. 109) In this journal appear a series of notices of the results of
analyses of vegetable fibres by the method described in 'Report on
Miscellaneous Fibres' (Col. Ind. Exhibition Reports, p. 368) [C. F.
Cross]. These investigations deal with the following subjects:

1895.     p. 29      Various Indian Fibres--more particularly Sida.
            118      (a) Fibres from Victoria; (b) Special Analyses of
       (a)               Samples of Jute; (c) Paper-making Fibres
                         from S. Australia.
            202      Fibres from Victoria.
            287      Fibres from Victoria.
            366      Sisal from Trinidad.
            373      Rope-fibres from Grenada.
       (b)  398      Report of Experiments on Indian Jute (1).
            435}     Fifth and Sixth Report on Australian Fibres.
            473}
1896.        68      Hibiscus and Abroma Fibres.
            104-5    Hibiscus, Urena, and Crotalaria Fibres.
            141      Indian Sisal
       (c)  182-3    Report of Experiments on Indian Jute (2).
            264      Sanseviera from Assam.

From the above we may draw the general conclusion that the scheme of
investigation has been found in practice to answer its main purpose,
viz. to afford such numerical constants as determine industrial values.
In illustration we may cite (a) the results of analyses of specially
selected samples of jute, from which it will be seen that there is a
close concordance of value as ordinarily determined from external
appearance, with the chemical constants as determined in the laboratory.

 __________________________________________________________________
|                            |                                     |
|                            |          Quality of Jute            |
|____________________________|_____________________________________|
|                            |       |        |       |            |
|                            |  Low  | Medium | Extra | Extra Fine |
|____________________________|_______|________|_______|____________|
|                            |       |        |       |            |
| Moisture                   | 11.0  |  10.4  | 11.1  |     9.6    |
| Ash                        |  0.87 |   2.8  |  1.0  |     0.7    |
| Alkaline hydrolysis (a)    |       |        |       |            |
|   5 mins. boiling          | 13.2  |  11.6  |  8.5  |     9.1    |
| Alkaline hydrolysis (b)    |       |        |       |            |
|   60 mins. boiling         | 16.1  |  17.5  | 12.5  |    13.1    |
| Mercerising treatment      |  9.2  |  10.5  | 10.3  |     8.5    |
| Nitration (increase p.ct.) | 36.6  |  35.7  | 37.5  |    36.7    |
| Cellulose (yield)          | 71.4  |  70.0  | 79.0  |    77.7    |
| Acid purification          |  2.6  |   1.3  |  1.9  |     2.0    |
|____________________________|_______|________|_______|____________|

A useful series of experiments, initiated by the Institute, is that
noted under (b) and (c) above.

(1) To ascertain the quality of the fibre extracted from the plant at
different stages of growth, quantities of 400 lbs. of the stalks were
cut at successive stages and the fibre isolated after steeping 14-20
days. The fibre was shipped to England and chemically investigated, with
the following results:

No. 1. Cut before appearance of inflorescence.
 "  2.  " after budding.
 "  3.  " in flower.
 "  4.  " after appearance of seed-pod.
 "  5.  " when fully matured.

 _________________________________________________________________
|                           |       |       |      |      |       |
|                           |  (1)  |  (2)  |  (3) |  (4) |  (5)  |
|___________________________|_______|_______|______|______|_______|
|                           |       |       |      |      |       |
| Moisture                  | 11.55 |  8.74 | 10.7 | 10.0 |  9.72 |
| Ash                       |  1.1  |  1.1  |  1.1 |  1.1 |  0.90 |
| Alkaline hydrolysis (a)   |  6.2  |  8.5  |  9.7 |  8.9 |  7.3  |
|    "         "      (b)   | 10.5  | 11.9  | 11.6 | 12.0 | 11.2  |
| Mercerising treatment     | 10.2  | 10.7  | 12.0 |  8.1 | 11.0  |
| Nitration                 | 37.2  | 32.1  | 32.2 | 33.2 | 36.6  |
| Cellulose                 | 74.0  | 76.2  | 74.1 | 74.8 | 76.4  |
| Acid purification         |  0.8  |  0.5  |  0.7 |  2.4 |  1.4  |
|___________________________|_______|_______|______|______|_______|

It will be thus seen that there are no changes of any essential kind in
the chemical composition of the bast fibre throughout the life-history
of the plant, confirming the conclusion that the 'incrustation' view of
lignification is consistent only with the structural features of the
changes, and so far as it has assumed the gradual overlaying of a
cellulose fibre with the lignone substance it is not in accordance with
the facts.

Examination of the samples from the point of view of textile quality
showed a superiority of No. 1 in fineness, softness, and strength; from
this stage there is observed a progressive deterioration, but the No. 4
sample (which was taken at the usual period of cutting) is superior to
No. 5.

In a further series of experiments (c) the jute was subjected to
certain chemical treatments immediately after the separation of the
fibre from the plant. These consisted in steeping (1) in solution of
sodium carbonate, as well as of plant ashes, and (2) in sulphite of
soda, the purpose of the treatments being to modify or arrest the
changes which take place in the fibre when press-packed in bales for
shipment. The samples were shipped from India under the usual conditions
and examined soon after arrival. It was found that the chemical
treatments had produced but small changes in chemical composition of the
fibre-substance. The sulphite treatment was the more marked in
influence, somewhat lowering the cellulose and nitration constants. The
conclusion drawn from the results was that they afford no prospect of
any useful modification, i.e. improvement of the textile quality of the
fibre by any chemical treatments such as could be applied to the fibre
on the spot before drying for press-packing and shipment.

The other matters investigated in the Institute laboratory and reported
on as indicated above are rather of commercial significance, and
contributed no points of moment to the chemistry of cellulose.


OBSERVATIONS ON SOME OF THE CHEMICAL SUBSTANCES IN THE TRUNKS OF TREES.

F. H. STORER (Bull. Bussey Inst., 1897, 386).

(p. 172) An examination of the outer and inner wood and of the bark of
the grey birch, at different seasons of the year, gave the following
yields of furfural p.ct. on the dry substance:

 ________________________________
|         |               |      |
|         |     Wood      |      |
|         |_______________| Bark |
|         |       |       |      |
|         | Inner | Outer |      |
|_________|_______|_______|______|
|         |       |       |      |
| May     | 21.3  | 19.6  | 16.7 |
| July    | 16.6  | 18.8  | 11.4 |
| October | 16.2  | 16.3  | 12.3 |
|_________|_______|_______|______|

The paper contains the results of treating the woods and various
vegetable products with hydrolysing agents in order of intensity: (a)
Malt-extract at 60°C., (b) boiling dilute HCl (1.0 p.ct. HCl), and
(c) boiling dilute HCl (2.5 p.ct.). The residues were found to yield
considerable proportions of furfural. The following numbers are typical:

 ________________________________________________________________________
|                               |             |                          |
|                               |     Birch   |        Stones of         |
|                               |_____________|__________________________|
|                               |      |      |        |         |       |
|                               | Bark | Wood |  Date  | Apricot | Peach |
|_______________________________|______|______|________|_________|_______|
|                               |      |      |        |         |       |
| Action of malt extract calcu- |      |      |        |         |       |
| lated as starch dissolved     | 4.24 |  3.5 |   5.2  |   1.5   |   --  |
|                               |      |      |        |         |       |
| Residue boiled, 1 p.ct. HCl   |      |      | Mannan |         |       |
| gave pentosanes dissolved.    |  --  | --   |  11.7  |  14.1   |  6.7  |
|                               |      |      |        |         |       |
| Residue yielded furfural      | 19.3 | 17.8 |   3.4  |   9.6   |  9.7  |
|_______________________________|______|______|________|_________|_______|

The proportion of pentosanes (furfuroids) removed, i.e. hydrolysed by
boiling with hydrochloric acid of 2.5 p.ct. HCl, is shown by the
following estimations of furfural:

 _________________________________________________________________
|                        |              |               |         |
|                        |    Birch     |  Sugar maple  |         |
|                        |______________|_______________| Apricot |
|                        |       |      |       |       | stones  |
|                        |  Bark | Wood | Outer | Inner |         |
|                        |       |      |  wood |  wood |         |
|________________________|_______|______|_______|_______|_________|
|                        |       |      |       |       |         |
| In original substance  | 16.7  | 19.6 |  18.2 |  20.7 |  18.4   |
|                        |       |      |       |       |         |
| In residue from action |  6.53 |  8.6 |   4.9 |   6.4 |   7.0   |
| of 2.5 p.ct. HCl       |       |      |       |       |         |
|________________________|_______|______|_______|_______|_________|

_Wood Gum._--The paper contains some observations on the various methods
of isolating this product. Attention is directed to the necessary
impurity of the product, and to the fact that the numbers for furfural
and for the xylose yielded by hydrolysis are considerably less than for
a pure pentosane.

_Estimation of Cellulose._--The author investigated the process of Lange
and the 'celluloses' obtained from various raw materials. The products
from the woods of birch and maple contained furfural-yielding
constituents, represented by yields of 6-8 p.ct. furfural. Preference is
given to the process by comparison with others, at the same time that it
is recommended in all cases to examine the product for furfural
quantitatively, converting the numbers into pentosane equivalents, and
subtracting from the total 'cellulose' to give the true cellulose.


ZUR KENNTNISS DER MUTTERSUBSTANZEN DES HOLZGUMMI.

E. WINTERSTEIN (Ztschr. Physiol. Chem., 1892, 381).

~ON THE MOTHER SUBSTANCES OF WOOD-GUM.~

(p. 188) According to the text-books beech-wood may be regarded as the
typical raw material for the preparation of the laboratory product known
as wood-gum. The author has subjected beech-wood and beech-wood
cellulose (Schulze process) to a range of hydrolytic treatments, acid
and alkaline, in order to determine the conditions of selective action
upon the mother substance of the wood-gum. In the main it appears that
this group of furfuroids is equally resistant with the cellulose
constituents of the wood; in fact, that the mother substance of wood-gum
is a modified cellulose, and exists in the wood in chemical combination
with the 'incrusting substances.'

Of the author's experimental results the following may be cited as
typical:

                                                     Yield of furfural
     Substance                                              p.ct.
Original beech-wood                                         13.8

After boiling 3 hrs. with 1.25 p.ct. H_{2}SO_{4} (residue)  10.1

   "       "      "    "   5.0    "       "            "     5.6

Cellulose--isolated by Schulze process (yield 53 p.ct.)      6.9

    "      after further 14 days' digestion with the
             Schulze acid (HNO_{3} + KClO_{3})               5.9

    "      after extraction with 5 p.ct. NaOH in
             cold (residue)                                  5.0

    "      after second extraction with 5 p.ct. NaOH
             in cold (residue)                               4.4


UEBER DIE FRAGE NACH DEM URSPRUNG UNGESÄTTIGER VERBINDUNGEN IN DER
PFLANZE.

C. F. CROSS, E. J. BEVAN, and C. SMITH (Berl. Ber., 1895, 1940).

~ON THE SOURCE OF THE UNSATURATED COMPOUNDS OF THE PLANT.~

(p. 179) In distilling for furfural by the usual methods of boiling
cellulosic products with condensing acids, the furfural is accompanied
by volatile acids, also products of decomposition of the cellulosic
complex. A series of distillations was carried out with dilute sulphuric
acids of varying concentration from 10-50 H_{2}SO_{4} : 90-50 H_{2}O by
weight, using barley straw as a typical cellulosic material. The
distillates were collected in successive fractions, and the furfural and
volatile acid determined. The results are given in the form of curves.
The aggregate yields were as follows:--

Concentration of acid
  (H_{2}SO_{4}) p.ct.            10    15    20    30    40    50

Furfural yield p.ct. of straw     2.0   2.0   4.4  10.1  11.5  11.0

Volatile acid (calculated
  as acetic acid) p.ct. of straw  1.7   1.9   3.1   4.3   6.3  14.8

With acids up to 20 p.ct. H_{2}SO_{4} both products are formed
concurrently and in nearly equal quantity. With the 30 p.ct. acid there
is a great increase in the total furfural, and with the 40 p.ct. acid it
reaches nearly the maximum obtainable with HCl of 1.06 s.g. (Tollens),
in this case 12.4 p.ct. The volatile acid increases, but in less ratio;
it is also produced concurrently. With 50 p.ct. H_{2}SO_{4} the
conditions are changed. The total furfural is rapidly formed, whereas
the volatile acid continues to be formed long after the aldehyde ceases
to come over. Moreover, whereas in the previous cases it was mainly
acetic acid, it is now mainly formic acid. The method was then extended
to a typical series of celluloses, heated with the more concentrated
acid (40-50 p.ct. H_{2}SO_{4}), with the following results:

 __________________________________________________
|                        |       |                 |
|                        |       |  Volatile acid  |
|                        |       |_________________|
|                        |       |        |        |
|                        |       | Acetic | Formic |
|________________________|_______|________|________|
|                        |       |        |        |
| Swedish filter-paper   |  0.3  |   2.7  |  17.2  |
| Esparto cellulose      | 12.4  |   3.2  |  16.6  |
| Bleached cotton        | trace |   3.1  |  13.2  |
| Raw cotton (American)  |  --   |   5.0  |   9.4  |
| Jute cellulose         |  5.2  |   4.9  |  22.7  |
| Beech (wood) cellulose |  6.4  |   3.5     14.6  |
|________________________|_______|________|________|

The tendency in the hexoses and their polyanhydrides to split off one
carbon atom in the oxidised form, throws some light on the furfurane
type of condensation, which is represented in the lignocelluloses. We
are still without any evidence as to the possible transition of the
hexoses to benzenoid compounds. Such transitions would be more easily
explained on the assumption that the celluloses are composed in part of
polyanhydrides of the ketoses.


SPIRITUS AUS CELLULOSE UND HOLZ.

E. SIMONSEN (Ztschr. angew. Chem., 1898, 3).

~PRODUCTION OF ALCOHOL FROM CELLULOSE AND WOOD.~

(pp. 50, 209) This investigation was undertaken with one main object--to
determine the optimum conditions of treatment of wood-cellulose and of
wood itself for conversion into 'fermentable sugar.' The process of
'inversion' or hydrolysis, by digestion with dilute acid at high
temperature, involves the four main factors: pressure (i.e.
temperature), concentration of acid, ratio of liquid to cellulose and
duration of digestion. Each of these was varied in definite gradations,
and the effect measured. The degree of action was measured in terms of
'reducing sugar,' calculated from the results of estimation by Fehling
solution, as 'glucose' per cent. of original cellulose (or wood).

(a) _Cellulose._ [Wood-cellulose obtained by bisulphite
process.]--With a proportion of total liquid to cellulose of 27 : 1, and
using sulphuric acid as the hydrolysing agent, the optimum results were
obtained with acids of 0.45-0.60 p.ct. (H_{2}SO_{4}) and pressures of
6-8 atm. The maximum yield of 'sugar' was 45 p.ct. of the cellulose.

Under the above conditions the maximum of conversion is attained in 2
hours.

Having now regard to the production of a solution of maximum
_concentration_ of dissolved solids, the following conditions were
asertained to fulfil the requirement, and, in fact, may be regarded as
the economic optimum:

     Proportion of total liquid  6 times wt. of cellulose
     Concentration of acid       0.5 p.ct. H_{2}SO_{4}
     Pressure                   10 atm.
     Duration of digestion       1.5 hour

giving a yield of 41 p.ct. 'reducing sugar' calculated to the original
cellulose (dry).

_Alcoholic Fermentation of Neutralised Extract._--The liquors were found
to ferment freely, and on distillation to yield a quantity of alcohol
equal to 70 p.ct. of the theoretical--i.e. on the basis of the numbers
for copper oxide reduction.

(b) _Hydrolytic 'Conversion' of Wood (Lignocellulose)._--A similarly
systematic investigation carried out upon pine sawdust established the
following as optimum conditions:

     Proportion of total liquid  5 times wt. of wood
     Concentration of acid       0.5 p.ct. H_{2}SO_{4}
     Pressure                    9 atm.
     Duration of digestion      15 minutes

giving a yield of 20 p.ct. 'reducing sugar,' calculated from the
'Fehling' test.

_Fermentation_ of the neutralised extracts gave variable results. The
highest yields obtained were 60 p.ct. of theoretical, the author finally
concluding that under properly controlled conditions of inversion and
fermentation 100 kg. wood yield 6.5 l. absolute alcohol.


ÜBER DIE URSACHE DER VON SIMONSEN BEOBACHTETEN UNVOLLSTÄNDIGKEIT DER
VERGÄHRUNG DER AUS HOLZ BEREITETEN ZUCKERFLÜSSIGKEITEN.

B. TOLLENS (Ztschr. angew. Chem., 1898, 15).

~ON THE CAUSE OF INCOMPLETE FERMENTATION OF SUGARS OBTAINED BY ACID
HYDROLYSIS OF WOOD.~

The author criticises Simonsen's explanation of the results obtained
with extracts from pine wood. The incompleteness of fermentation of the
products is certainly due in part to the presence of furfural-yielding
carbohydrates, which are resistant to yeast. The pine woods contain 8-10
p.ct. of these constituents in their anhydride form ('pentosanes'). They
yield readily to acid hydrolysis, and certainly constitute a
considerable percentage of the dissolved products. A similar complex was
obtained by the author in his investigation of peat (Berl. Ber. 30,
2571), and was found to be similarly incompletely attacked by yeast. The
yields of alcohol corresponded with the proportion of the total
carbohydrates disappearing. These were the hexose constituents of the
hydrolysed complex, the pentoses (or 'furfuroids') surviving intact.


UEBER SULFITCELLULOSEABLAUGE.

H. SEIDEL (Ztschr. angew. Chem., 1900).

~WASTE LIQUORS FROM BISULPHITE PROCESS.~

(p. 210) Later researches confirm the conclusion that in the soluble
by-products of these cellulose processes the S is combined as a SO_{3}H
group. The following analyses of the isolated lignin sulphonic acid are
cited:

 ________________________________________________
|                          |       |      |      |
|                          |   C   |  H   |  S   |
|__________________________|_______|______|______|
|                          |       |      |      |
| (a) Lindsey and Tollens  | 56.12 | 5.30 | 5.65 |
| (b) Seidel           (1) | 56.27 | 5.87 | 5.52 |
| (c) Seidel and Hanak (2) | 53.69 | 5.22 | 8.80 |
| (d) Street               | 50.22 | 5.64 | 7.67 |
|__________________________|_______|______|______|

The variations are due to the varying conditions of the digestion of the
wood and to corresponding degrees of sulphonation of the original
lignone group. Calculating the composition of the latter from the above
numbers on the assumption that the S represents SO_{3}H, the following
figures result:

 __________________________________
|   |             |       |       |
|   | (a) and (b) |  (c)  |  (d)  |
|___|_____________|_______|_______|
|   |             |       |       |
| C |  64.00      | 65.1  | 59.61 |
| H |   6.65      |  6.33 |  6.69 |
|___|_____________|_______|_______|

This author considers that beyond the empirical facts established by the
above named[10] very little is yet known in regard to the constitution
of the lignone complex.

Nor is there any satisfactory application of this by-product as yet
evolved. Evaporation and combustion involve large losses of sulphur
[D.R.P. 74,030, 83,438; Seidel and Hanak, Mitt. Techn. Gew. Mus. 1898].
A more complete regeneration of the sulphur has been the subject of a
series of patents [D.R.P. 40,308, 69,892, 71,942, 78,306, 81,338], but
the processes are inefficient through neglect of the actual state of
combination of the S, viz. as an organic sulphonate. The process of V.B.
Drewson (D.R.P. 67,889) consists in heating with lime under pressure,
yielding calcium monosulphite (with sulphate and the lignone complex in
insoluble form). The sulphite is redissolved as bisulphite by treatment
with sulphurous acid. This process is relatively costly, and yields
necessarily an impure lye. It has been proposed to employ the product as
a foodstuff both in its original form and in the form of benzoate
(D.R.P. 97,935); but its unsuitability is obvious from its composition.
A method of destructive distillation has been patented (D.R.P. 45,951).
The author has investigated the process, and finds that the yield of
useful products is much too low for its economical development. Fusion
with alkaline hydrates for the production of oxalic acid (D.R.P. 52,491)
is also excluded by the low yield of the product.

The application of the liquor for tanning purposes (D.R.P. 72,161)
appears promising from the fact that 28 p.ct. of the dry residue is
removed by digestion with hide powder. This application has been
extensively investigated, but without practical success. Various
probable uses are suggested by the viscosity of the evaporated extract.
As a substitute for glue in joinery work, bookbinding, &c., it has
proved of little value. It is applied to some extent as a binding
material in the manufacture of briquettes, also as a substitute for
gelatin in the petroleum industry. Cross and Bevan (E.P. 1548/1883) and
Mitscherlich (D.R.P. 93,944 and 93,945) precipitate a compound of the
lignone complex and gelatin by adding a solution of the latter to the
liquors. The compound is redissolved in weak alkaline solutions and
employed in this form for engine-sizing papers. Ekman has patented a
process (D.R.P. 81,643) for 'salting out' the lignone sulphonates, the
product being resoluble in water and the solution having some of the
properties of a solution of dextrin. Owing to its active chemical
properties this product--'dextron'--has a limited capability of
substituting dextrin. The suggestion to employ the evaporated extract as
a reducing agent in indigo dyeing and printing has also proved
unfruitful. The author's application of the soda salt of the lignone
sulphonic acid as a reducing agent in chrome-mordanting wool and woollen
goods (D.R.P. 99,682) is more successful in practice, and its industrial
development shows satisfactory progress. The product is known as
'lignorosin.'

FOOTNOTES:

[10] See more particularly: Lindsey and Tollens, _Annalen_, 267, 341;
Cross and Bevan's _Cellulose_, pp. 197-203; Street, Inaug.-Diss.,
Göttingen, 1892; Klason, _Rep. d. Chem. Ztg._ 1897, 261; Seidel and
Hanak, _Mitt. d. Techn. Gew. Mus._ 1897-1898.




SECTION VII. PECTIC GROUP


UNTERSUCHUNGEN ÜBER PECTINSTOFFE.

R. W. TROMP DE HAAS and B. TOLLENS (Lieb. Ann., 286, 278).

ÜBER DIE CONSTITUTION DER PECTINSTOFFE, B. TOLLENS (ibid. 292).

~INVESTIGATIONS OF PECTINS.~

(p. 216) It is generally held that the pectins are, or contain, oxidised
derivatives of the carbohydrates. The authors have isolated and analysed
a series of these products, and the results fail to confirm a high
ratio O : H. The following are the analytical numbers:

 ________________________________________________
|              |      |      |     |             |
| Pectin from  |  Ash |   C  |  H  | Ratio H : O |
|______________|______|______|_____|_____________|
|              |      |      |     |             |
| Apple        |  6.2 | 43.4 | 6.4 |   1 : 7.9   |
| Cherry       | 20.5 | 42.5 | 6.5 |   1 : 7.9   |
| Rhubarb      |  4.2 | 43.3 | 6.8 |   1 : 7.4   |
| Currant      |  5.0 | 47.1 | 5.9 |   1 : 8.5   |
| Greengage    |  3.3 | 43.0 | 5.9 |   1 : 8.5   |
| Turnip       |  7.3 | 41.0 | 5.9 |   1 : 9.0   |
|______________|______|______|_____|_____________|

Acid hydrolysis (4 p.ct. H_{2}SO_{4}) gave syrupy products not
crystallisable--in certain cases the hydrolysis was accompanied by
separation of insoluble cellulose. The insoluble product from currant
pectin had the composition C 54.4, H 5.0.

Tollens points out that the results of empirical analysis are
inconclusive; and that from the acid reactions of these products and
their combination with bases, carboxylic groups are present, though
probably in anhydride or ester form.

The pectins may be regarded as closely related to the mucilages
(_Pflanzenschleim_), differing from them only by the presence of the
oxidised groups in question.


UEBER DIE CONSTITUTION DER PECTINSTOFFE.

C. F. CROSS (Berl. Ber., 1895, 2609).

~CONSTITUTION OF PECTINS.~

It is pointed out that the composition of the pectin of white currants,
as given in the preceding paper, is that of the typical lignocellulose,
the jute fibre. The product was isolated and further investigated by the
author. It gave 9.8 p.ct. furfural on boiling with HCl (1.06 s.g.),
reacted freely with chlorine, giving quinone chlorides, and with ferric
ferricyanide to form Prussian blue. This 'pectin' is therefore a form
of soluble lignocellulose. The 'pectic' group consequently must be
extended to include hydrated and soluble forms of the mixed complex of
condensed and unsaturated groups with normal carbohydrates, such as
constitute the fibrous lignocelluloses.


UEBER DAS PFLANZLICHE AMYLOID.

E. WINTERSTEIN (Ztschr. Physiol. Chem., 1892, 353).

~ON VEGETABLE AMYLOID.~

(p. 224) A group of constituents of many seeds, distinguished by giving
slimy or ropy 'solutions' under the action of boiling water are
designated 'amyloid.' They are reserve materials, and in this, as in the
physical properties of their 'solutions,' they are very similar to
starch. They are, however, not affected by diastase; and generally are
more resistant to hydrolysis. Typical amyloids have been isolated by the
author from seeds of _Tropoeolum majus, Poeonia officinalis_, and
_Impatiens Balsamina_. The raw material was carefully purified by
exhaustive treatment with ether and alcohol, &c.; the amyloid then
extracted by boiling with water, and isolated by precipitation with
alcohol. Elementary analysis gave the numbers C 43.2, H 6.1. On boiling
with 12 p.ct. HCl it gave 15.3 p.ct. furfural; oxidised with nitric acid
it yielded 10.4 p.ct. mucic acid. Specimens from the two first-named raw
materials gave almost identical numbers.

_Hydrolysis._--On boiling with dilute acids these products are gradually
broken down, dissolving without residue. In this respect they are
differentiated from the mucilages, which give a residue of cellulose
(insoluble). From the solution the author isolated crystalline
galactose, but failed to isolate a pentose. Dextrose was also not
identified directly.

The tissue residues left after extracting the amyloid constituent, as
above described, were subjected to acid hydrolysis. A complex of
products was obtained, from which galactose was isolated. A
furfural-yielding carbohydrate was also present in some quantity, but
could not be isolated. The original seed tissues, therefore, contain an
amyloid and a hemicellulose, the latter differentiated in its resistance
to water. Both yield, however, to acid hydrolysis a complex of products
of similar composition and constitution.


UEBER DEN GEHALT DES TORFES AN PENTOSANEN ODER FURFUROLGEBENDEN STOFFEN
UND AN ANDEREN KOHLENHYDRATEN.

H. V. FEILITZEN and B. TOLLENS (Berl. Ber., 1897, 2,571).

~CARBOHYDRATE CONSTITUENTS OF PEAT.~

(p. 240) An investigation of typical peats taken at successive depths
showed increasing percentage of carbon, and inversely a decreasing yield
of furfural. The numbers may be compared with those for _Sphagnum
cuspidatum_--with C = 49.80 p.ct., and furfural 7.99 p.ct., calculated
to dry, ash-free substance:

 __________________________________________________
|                       |         |                |
|  Depth at which taken | C p.ct. | Furfural p.ct. |
|_______________________|_________|________________|
|      _                |         |                |
|     |      20-100 cm. |  51.08  |      6.93      |
|  I. |     100-200  "  |  53.52  |      5.30      |
|     |_    200-300  "  |  58.66  |      3.19      |
|      _                |         |                |
|     |  Surface-20  "  |  55.47  |      3.40      |
| II. |       20-60  "  |  55.06  |      3.48      |
|     |      60-100  "  |  58.25  |      1.45      |
|     |     100-120  "  |  58.23  |      1.19      |
|     |_    180-200  "  |  57.57  |      1.80      |
|_______________________|_________|________________|

_Cellulose_ was estimated by the Lange method. The yield from _Sphagnum_
was 21.1 p.ct.

From specimen I. at {  20-100 cm.   15.20
                    { 100-200  "     6.87

From the peat of lower depths no cellulose could be obtained.

_Hydrolysis_ (acid).--On heating with 1 p.ct. H_{2}SO_{4} at 130-135°,
soluble carbohydrates were obtained, amongst which mannose was
identified, and galactose shown to be present in some quantity. After
fermenting away the hexoses, the residue was treated with
phenylhydrazine and an osazone separated. It contained 17.3 p.ct. N, but
melted at 130°. The substance could not be identified as an osazone of
any of the yet known pentoses.




SECTION VIII. INDUSTRIAL AND TECHNICAL. GENERAL REVIEW


~The Industrial Uses of Cellulose.~

C. F. CROSS (Cantor Lectures, Soc. of Arts, 1897).

(p. 273) A series of three lectures, in which the more important
industries in cellulose and its derivatives are dealt with on their
scientific foundations, and by means of a selection of typical problems.
In reference to textiles, the small number of vegetable fibres actually
available, out of the endless variety afforded by the plant world, is
referred to the number of conditions required to be fulfilled by the
individual fibre, thus: yield per cent. of harvested weight or per unit
of field area, ease of extraction, the absolute dimensions of the
spinning unit, and the proportion of variation from the mean dimensions;
the relative facility with which the unit fibre can be isolated
preparatory to the final twisting operation; the chemical constants of
the fibre substance, especially the percentage of cellulose and degree
of resistance to hydrolysis. It is suggested that any important addition
to the very limited number fulfilling the conditions, or any great
improvement in these, can only result from very elaborate artificial
selection and cultural developments on this basis.

The paper making fibres are shown to fall into a scheme of
classification based on chemical constitution, and consisting of the
four groups: (a) Cotton [flax, hemp, rhea], (b) wood celluloses,
(c) esparto, straw, and (d) lignocelluloses. Papers being exposed to
the natural disintegrating agencies, more especially oxygen, water (and
hydrolysing agents generally), and micro-organisms, the relative
resistance of the above groups of raw materials is discussed as an
important condition of value. The indirect influence of the ordinary
sizing and 'filling' materials is discussed. The paper-making quality of
the fibrous raw materials is also discussed, not merely from the point
of view of the form and dimensions of the ultimate fibres, but their
capacity for 'colloidal hydration.' This is complementary to the action
of rosin, i.e. resin acids, in the engine-sizing of papers; and the
proof of the potency of this factor is seen in the superior effects
obtained in sizing jointly with solutions of cellulose and, more
particularly, viscose and rosin. Wurster's much-cited monograph of the
subject of rosin-sizing ['Le Collage des Papiers,' Bull. Mulhouse, 1878]
neglects to take into consideration the contribution of the cellulose
hydrates to the total and complex sizing effect, and hence gives a
partial view only of the function of the resin acids.

In further illustration of fundamental principles various developments
in the textile industries are discussed, e.g. the bleaching of jute,
cotton, and flax, and special developments in the spinning of rhea and
flax.

The concluding lecture deals with later progress in the industrial
applications of cellulose derivatives, chiefly the sulphocarbonate
(viscose); the nitrates, in their applications to explosives, on the one
hand, and the spinning of artificial fibres (lustra-cellulose), on the
other; and the cellulose acetates.


~La Viscose et le Viscoide.~

C. H. BARDY (Bull. Soc. d'Enc. Ind. Nationale, 1900, March).

This is a report presented to the Committee of Economic Arts of the
above Society, dealing with the industrial progress in products obtained
by means of the sulphocarbonate of cellulose (viscose).

The following developments are noted:

_Engine-sized Papers._--The viscose, by coating the fibres with
regenerated cellulose hydrate, adds very much to the tensile strength of
papers. Increase of 40-60 p.ct. is attainable by addition of cellulose
in this form from 1-4 p.ct. on the weight of the paper.

_Viscoid._--Solid aggregates are formed by incorporating viscose with
mineral matters, hydrocarbons, &c. Products are cast or moulded into
convenient forms, and, after purification and sufficient ageing, are
available for various structural uses.

_Paint._--The viscose is used as a vehicle for pigments, the mixture
being used either as a paint or for coating papers with fine surfaces,
such as required in the reproduction of photo-blocks. In these
applications the extraordinary viscosity of the product conditions the
economic use of the cellulose in competition with oils, on the one hand,
and organic colloids, such as gelatine, casein, &c., on the other.

By suitable alteration of the formula for making the paint a product is
obtained which has an extraordinary power of removing paint from old
painted surfaces. The product has been officially adopted by the French
Admiralty, and receives extensive application in removing the paint from
ships.

_Films._--Films are produced from the viscose itself in various ways.
Plane or flat by solidifying the viscose on glass surfaces, removing the
by-products and rolling the films. The film is also produced by
applying the viscose on textile fabrics, drying down, and fixing on a
stenter machine, then washing away the alkaline by-products from the
fixed film. A large number of industrial effects are obtained by
suitably varying the mixtures applied.

_Cellulose-indiarubber._--The viscose, in its concentrated form, can be
incorporated with rubber-hydrocarbon mixtures, and these mixtures can be
used both as water-proofing films, as applied to textiles, or can be
solidified into the class of goods known as 'mechanicals.' The cellulose
not only cheapens the mixture, but produces new technical effects.

_Spinning._--The viscose is spun by special methods, patented by C. H.
Stearn. As produced in thread form, the diameters are approximately
those of natural silk. In commercial form it is a multiple thread (of 15
or more units) at from 50-200 deniers on the silk counts. It is a thread
of high lustre, and more nearly approaches the normal cellulose in
chemical properties than any of the other artificial silks. It can also
be spun in threads of very much larger diameter, which can be used as a
substitute for horsehair, for carbonising for incandescent electric
lamps, &c.

_Cellulose Esters._--These are conveniently made from cellulose,
regenerated from the solution as sulphocarbonate. The tetracetate is
made from this product on the industrial scale. Nitrates are
conveniently made by treatment with the ordinary mixed acids. For fuller
details the original report may be consulted.


VISKOS.

R. W. STREHLENERT (Svensk Kemisk Tidskrift, Stockholm, 1900, p. 185).

A report on the industrial development of viscose, covering essentially
the same ground as the above.


~Ueber die Viscose.~

B. M. MARGOSCHES (Reprint from Zeitschrift für die gesammte
Textil-Industrie, 1900-01, Nos. 14-20).[11]


~Report of Committee on the Deterioration of Paper.~

(Soc. of Arts, 1898.)

(p. 304) The Report of a Representative Committee appointed by the
Society of Arts to inquire into the question of qualities of book papers
in relation to their several applications, and more especially for
documents of permanent value.

The report first discusses the two directions of depreciation of papers
in use: (1) Actual disintegration shown by loss of resistance to
fracture by simple strain, and by loss of elasticity--i.e. increase of
brittleness; (2) discolouration. These are independent effects, but
often concurrent. They are the result of chemical changes of the
cellulose basis of the paper, brought about by acids or oxidants used in
the process of manufacture, and not completely removed from the pulp, or
by acid products of bleaching--e.g. oxycelluloses or chlorinated
derivatives; again, by the changes of starch used as a 'sizing' agent,
or by oxidations induced by rosin constituents when the rosin is used in
excess. Discolouration is an attendant phenomenon of these changes, but
is more frequently due to the presence of the lower-grade celluloses
(esparto and straw) and the lignocelluloses (mechanical wood-pulp).

The physical and chemical qualities of papers depending primarily upon
their fibrous or pulp basis, and in a secondary degree upon the kind and
proportion of the constituents added for the purpose of filling and
'sizing,' the report concludes with the following recommendations,
positive and negative, under these heads:

The Committee find that the practical evidence as to permanence fully
confirms the classification given in the Cantor Lectures on 'Cellulose,'
1897 [J. Soc. Arts, xlv. 690-696], and which ranges the paper-making
fibres in four classes:

(A) Cotton, flax, and hemp (rhea).

(B) Wood celluloses, (a) sulphite process and (b) soda and
'sulphate' process.

(C) Esparto and straw celluloses.

(D) Mechanical wood-pulp.

In regard, therefore, to papers for books and documents of permanent
value, the selection must be taken in this order, and always with due
regard to the fulfilment of the conditions of normal treatment above
dealt with as common to all papers.

The Committee have been desirous of bringing their investigations to a
practical conclusion in specific terms--viz. by the suggestion of
standards of quality. It is evident that in the majority of cases there
is little fault to find with the practical adjustments which rule the
trade. They are, therefore, satisfied to limit their specific findings
to the following--viz. (1) normal standard of quality for book-papers
required for publications of permanent value. For such papers they
specify as follows:

Fibres: Not less than 70 p.ct of fibres of class A; class D excluded.

Sizing: Not more than 2 p.ct. rosin, and finished with the normal
acidity of pure alum; starch excluded.

Loading: Not more than 10 p.ct. total mineral matter (ash).

(2) With regard to written documents, it must be evident that the proper
materials are those of class A, and that the paper should be pure and
sized with gelatin, and not with rosin. All imitations of high-class
writing-papers which are, in fact, merely disguised printing-papers,
should be carefully avoided.

_Appendix._--To the Report is added 'Abstracts of Papers' in
'Mittheilungen aus den Koniglichen Technischen Versuchsanstalten,
Berlin,' for the years 1885-1896 inclusive--which is, in fact, a summary
of the investigations of the Institution in connection with paper and
paper-standards.

       *       *       *       *       *

(p. 273) ~Special Industrial Developments.~--From the point of view of the
chemist there has been a very large development of the cellulose
industries during the last five years. This is not so much marked by the
gradual and progressive growth of the well-established industries, as by
the success of the newer ones, with the attendant forecast of enormous
developments of the industries in artificial products, the manufacture
of which rests upon a purely chemical basis. We can, of course, only
treat them from this limited standpoint, and so far as they involve and
elucidate chemical principles.


~I. Chemical Treatments of Raw Materials.~

(a) ~Flax-spinning.~--The treatment of the roving on the spinning-frame
by the addition of reagents to the macerating liquid--otherwise and
usually hot water--continues to be justified by results. The technical
basis of the process and the reactions determined in the spinning-trough
by the alkaline salts used--chiefly sulphite and phosphate of soda--is
set forth in the original work, p. 280. Since that time a sufficient
period has elapsed to judge the effects, both technical and industrial,
by the results of a commercial undertaking based on the exclusive use of
the process. Such a concern is the Irish Flax Spinning Company of
Belfast. At this mill the experience is uniform and fully established
that by means of the process the drawing, i.e. spinning, quality of
inferior flaxes is very considerably appreciated, enabling the spinner
to use such flaxes for yarns of fineness which are unattainable by the
ordinary method of spinning through hot water. Notwithstanding the
success of this undertaking the development of the method is still
inconsiderable. It is none the less a further and forcible demonstration
of the existence of margins of increased technical effect which it is
the work of the scientific technologist to exploit.

(b) ~Wood-pulp and Methods of Manufacture.~--There is a steady growth in
the consumption of wood-pulps (cellulose) relatively to other materials.
In regard to the paper-trade of the world, this continues to be one of
the most prominent characteristics of its evolution. In the United
Kingdom the conditions of its competition are of a more special kind by
reason of the firm foothold of esparto, which is a most important staple
in the manufacture of fine printings. Whereas the consumption of esparto
remains nearly stationary at about 200,000 tons per annum, the
importation of wood-pulps has shown the extraordinary rate of increase
of doubling itself every five years. But in the group 'wood-pulps' the
trade returns have until recently included the 'mechanical' or ground
wood-pulps. From 1898 we have separate returns for the chemical or
cellulose pulps, and in 1899 the tonnage reached nearly to that of
esparto, with a total money value about 80 p.ct. greater. When it is
remembered that this is one of the newer chemical industries in
cellulose products, and that these large commercial results have been
accomplished during a period of twenty years, we are impressed with the
scope of the industrial outlook to the chemist, afforded by the arts of
which cellulose is the foundation.

It may be noted that there have been no important developments in the
purely chemical processes involved in the several systems of preparing
cellulose from wood. The acid methods (bisulphite processes) have
developed much more extensively than the alkaline, the latter including
the caustic soda and the mixed sulphide ('Dahl') process. The bisulphite
processes depended in the earlier stages upon the efficiency of
lead-lined digesters. But the problem of acid-resisting linings has been
much more perfectly solved in later years in the various types of cement
and other silicate linings now in use. The relative permanency of these
linings has had an important effect on the costs of production. Further
economies result from the use of digesters of enormous capacity, dealing
with as much as 100 tons of wood at one operation. As a combined result
of economic production and active competition, the selling prices of
'sulphite pulp' have moved steadily downwards in relation to other
half-stuffs and raw materials. As a necessary consequence the prices of
those which it has gradually displaced have depreciated, and a study of
the price and tonnage-equilibrium as between rags, esparto, and
wood-pulp over a series of years forms an interesting object-lesson in
the struggle for survival which is an especial mark of modern industry.
For these matters the reader is referred to the special literature of
the paper-making industry.[12]

It is not a little remarkable that the main by-product of these
bisulphite processes--the sulphonated derivatives of the lignone
constituents of the wood--is still for the most part an absolute waste,
notwithstanding the many investigations of technologists and attempts to
convert it to industrial use (see p. 149). Seeing that it represents a
percentage on the wood pulped equal to that of the cellulose obtained,
it is a waste of potentially valuable material which can only be termed
colossal. Moreover, as a waste to be discharged into water-courses, it
becomes a source of burden and expense to the manufacturer, and with the
increasing restrictions on the pollution of rivers it is in many
localities a difficulty to be reckoned with only by the cessation of the
industry. The problem in such cases becomes that of dealing with it
destructively, i.e. by evaporation and burning. In this treatment the
obviously high calorific value of the dissolved organic matter (lignone)
appears on the 'credit' side. But where calcium and magnesium
bisulphites are used, the residue from calcination is practically
without value. It appears, however, that by substituting soda as the
base the alkali is recoverable in such a form as to be directly
available for the alkaline-sulphide or 'Dahl' process. As a more
complicated alternative the soda admits of being recovered on the lines
of the old black-ash or Leblanc process, and the sulphur by the now
well-established 'Chance' process, for which, of course, an addition of
lime is necessary to the fully evaporated liquors previously to
calcining. The engineering features of the system, so far as regards
evaporating and calcining, are the same. For economic working there is
required (a) evaporation by multiple effect and (b) calcining on the
continuous rotary principle. For the latter a special modification has
been devised so that the draught of air is concurrent with the movement
of the charge in the furnace, securing a progressively increasing
temperature within the furnace. This interesting development of the
chemical engineering of wood-pulp systems has been elaborated by two
well-known technologists, Drewson and Dorenfeldt, and readers who wish
to inform themselves in detail of these developments are referred to the
various publications of these inventors.

Assuming the present necessity of a destructive treatment of the
by-products of the bisulphite processes, the scheme has many advantages.
The soda-bisulphite liquors are more economically prepared; the pulp
obtained is superior in paper-making quality to that resulting from the
lime or magnesia (bisulphite) processes: it is more economically
bleached.

Then, as pointed out, the soda may on the one plan be obtained in a form
in which it is immediately available as a powerful hydrolysing alkali in
the manufacture of a 'soda' pulp. These two systems become, therefore,
in a new sense complementary to one another. Lastly, it is obvious that
the employment of soda as the base opens out a new vista for developing
the electrolytic processes of decomposing common salt.

The authors have assisted in preparing plans for a comprehensive
industrial scheme combining all these more modern developments. In this
scheme it is only the combination which is novel, and as it involves no
new principles in the chemical treatments of the materials we are not
further concerned with it than to have briefly sketched its economic
basis. This may be summed up in result in the important question of cost
and selling price, and the estimate is well grounded that by means of
this scheme _bleached wood-pulp_ can be sold on the English market at
10l. a ton. It is important to note this figure and to compare it with
the prices of twenty years ago. The fall has been continuous,
notwithstanding the influence of the opposing factors of increasing
consumption, exhaustion of accessible supply of timber, and relative
appreciation of the essential costs of steam, chemicals, and labour. It
is important in forecasting the future, since the youngest and
apparently most promising of the 'artificial' cellulose industries
employs wood-cellulose by preference as its raw material (see p. 173).

As a last point it must be considered that as chemists we are bound to
anticipate the realisation of value in the soluble by-products of the
bisulphite processes. Outside the intrinsic interest attaching to the
solution of this problem, it carries with it the promise of a further
economy in the production of wood-cellulose.

~Bleaching of Vegetable Textiles.~--By far the largest of these industries
are those which are engaged in producing the 'pure white' on cotton and
flax goods. The process, considered chemically, is simply that of
isolating a pure cellulose, and we endeavoured to give due prominence to
this view in the original work. It is important to insist upon it for
the reason that this view gives the due proportion of chemical value to
the several contributory treatments--alkaline hydrolyses (caustic lime
and soda boils), hypochlorite oxidations, and incidental acid treatments
(souring). The first of these is by far the largest contributor of
'chemical work,' though the second, by being the agent for the actual
whitening effect or bleaching action proper, occupies a position of
often exaggerated importance.

In bleaching processes there has been no radical change of system on the
large scale since the introduction of the 'Mather' kier in 1885, and the
associated change from lime and ash boiling to the caustic soda
circulating boil with reduced volume of lye, which this mechanical
device rendered practicable. It is outside the scope of this work to
follow up this branch of technology in any detail, and we cannot discuss
the evolution of systems on variations of detail where no essential
principle is involved. But we have to notice a very recent development
which has only just begun its industrial career, and which does give
effect to a principle of treatment not previously applied. This is
tersely stated by its originator, William Mather,[13] in the
expression, 'it is more economical to make liquids pass through cloth
than to make cloth pass through liquids.' The starting point of this
development is the invention of a complete self-contained machine in
which a rolled batch of cloth can receive a succession of chemical
treatments, with accessory washings--the solutions, or wash waters,
being circulated through the cloth. The essential fact on which this
system is based is that a perfect liquid circulation can be maintained
from selvedge to selvedge through the folds of a tightly rolled batch of
cloth. Such circulation is therefore quite independent of the diameter
of the batch. If we consider a cloth under chemical treatment with
solutions, it is clear that the reactions and interchanges of soluble
matters within the cloth, within the twisted elements of the yarn, and
in the last grade of distribution within the actual ultimate fibres, are
subject to capillary transmission, and osmotic exchange. There is a
mixture of these molecular effects, with the circulation in mass,
sweeping both faces of the cloth. It is obvious that for the mass effect
a relatively very small volume of circulating liquid is necessary to
maintain uniform conditions of action. In the actual disposition of the
machine the rolled batch of cloth nearly fills the cylindrical space of
what we may call the reaction chamber, and the circulation of the liquid
is maintained by a circulating pump and a differential pressure in the
horizontal plane across and through the folds of the batch. This is in
the meantime kept in slow revolution. For a full description of these
mechanical details the reader is referred to the original patent
specifications [Engl. Pat. 23,400, 23,401; 1900, W. Mather]. If we again
consider the principles involved, they are very much as set forth in
our original work (pp. 288-291). Boiling processes in which a
relatively large volume of liquid is used are wasteful of steam, the
active agent is unnecessarily diluted or used in superfluous quantity,
and the soluble by-products, being continually removed as formed, cannot
so effectively contribute by secondary actions to the chemical work. The
new mechanical appliance enables us to further reduce the volume of
liquid required in the alkaline-hydrolytic treatment of vegetable
textiles, and where advantageous to bring the treatment down (or up) to
a process of steaming with the active agent dissolved in a minimum
proportion of water relative to the cloth. This concentration of effect
is of importance in flax cloth, and especially linen treatment, where
the peculiarly resistant cutocelluloses have to be attacked and a
considerable proportion of waxy by-products to be removed. These points
are the basis of the special process of Cross and Parkes [Engl. Pat.
25,076/ 99] for steaming flax (and cotton) goods with an emulsion
containing, in addition to the special hydrolysing agent--caustic
soda--mixtures of soap with 'mineral' or other oils, the presence of
which effectually aids the removal of the by-products in question.

A complete system on these lines is now working on the industrial scale
in the Belfast district. The results are not merely economical in
largely reducing the number of alkaline boiling treatments required on
the old plan of pan or 'pot' boiling, but are visible in the strength
and finish of the linens so treated.

For cotton bleaching the costs may be put down at a fraction of those of
the Irish linen bleach. The economical advantages of the new system are
obviously less in relation to the lesser total costs. But there are
other points which have come into more prominent influence. The
mechanical wear and tear on the cloth is considerable in the ordinary
process, more especially in the mangle-washes. As a result the
adjustment of warp and weft is more or less disturbed. These defects are
absent from a system which operates on the cloth in a fixed position.

But as we are mainly concerned with the purely chemical factors we
cannot pretend to deal with textile questions. We have to notice the
remaining element of chemical economy as it involves a fundamental
principle. The practice of washing residues or products of reaction free
from reagents and soluble by-products involves a well-known mathematical
law, under which the rate of purification is a function rather of the
_number_ of successive changes of washing liquid than of the volume of
the latter. The ordinary practice of textile washings entirely ignores
this principle, and the consumption of water in consequence may reach
many thousand times the economic minimum. With supplies of water often
in indefinite excess of requirements, even in this most wasteful method,
bleachers are in no need to consider the question of consumption. But
leaving aside particular and local considerations of advantage the fact
is that the new system gives control of the practice of washing,
enabling the operator to adapt an important element of the daily routine
to a fundamental principle which has been almost universally ignored.

In the oxidising processes which follow the alkaline treatments, the
hypochlorites are still the staple agents. Owing to the steady relative
fall in the selling prices of the permanganates these are coming into
more extensive use, but the consumption is still small, and they are
mainly used for certain special effects, chiefly in linen or more
generally flax cloth bleaching.

~Paper-pulp Spinning.~--Paper is a continuous web or fabric produced by
the interlocking of the structural fibrous units of the well-known short
length. In Japan and other countries paper is made to serve for all or
some of the purposes for which we employ string or twine, and to give
the necessary tensile strength the paper is twisted or rolled on itself.
Such twisting, however, adds nothing to the intrinsic tensile qualities
of the original paper.

A new technical effect is realised in this direction by the treatment of
paper-pulp in the process of its conversion into a continuous web: The
pulp is formed into continuous strips of convenient breadth (usually
from 2 to 8 mm.), these receive a 'rolling-up' treatment immediately
following the squeeze of the press rolls by which the superfluous water
is removed: they are then further but incompletely dried, and in this
condition are subjected to a final spinning or twisting treatment on
ring-spinning machinery of special construction.

Such a process was originally patented by C. Kellner in this country
(E.P. No. 20,225/1891), and is fully described in his specification.
Later improvements in detail were patented by G. Türk (E.P. 4621/1892).

A joint system is now being industrially developed in Germany by the
Altdamm-Stahlhammer Pulp and Paper Company under the technical direction
of Dr. Max Müller, and there appears to be every prospect of the product
taking a position as a staple textile.

The process has only the incidental interest in connection with our main
subject, that it employs chiefly the 'chemical' pulps or celluloses as
raw materials. The industrial future of the application must, of course,
be largely determined by costs of production, as the directions of
application in the weaving industries will be limited by the necessarily
inferior grade of tensile strength belonging to these products and the
degree by which this is lowered on complete wetting. All these questions
have been duly weighed by those engaged in this interesting development,
and the conclusion of those qualified to judge is that the new industry
has vindicated for itself a permanent position.

~II. The Chemical Derivatives of Cellulose~, in their industrial aspects,
have come to occupy a profoundly important position in the world's
affairs. In the way of any essential alteration of the perspective from
that obtaining in 1895 we have nothing to chronicle. No new derivatives
of industrial importance have been added in that period; but certain new
methods incidental to the preparation of well-known compounds or for
converting them into more generally available forms have been
introduced, and these are contributing to the rapid expansion of the
'artificial' cellulose industries.

Of the cellulose esters the nitrates are still the only group in
industrial use. There uses for explosives have attained immense
proportions, and their applications for structural purposes are
continually on the increase. The manufacture of smokeless powders on the
one hand, and of celluloid and xylonite (both in the form of films and
solid aggregates) on the other, has taken no new departure. The industry
in 'artificial silks' or 'lustra-celluloses,' by the collodion processes
also, whilst presenting features of unusual interest attaching to rapid
expansion, has been barren of contribution of fundamental scientific or
technical importance. The tetracetate is now manufactured on the large
scale, but the product has yet to make its market.

The process of mercerising cotton yarns and cloth has been developed to
an industry of colossal dimensions, and the growth has been especially
rapid during the last five years. Significant of the technical progress
in these two industries, with their common aim of appreciating cellulose
in the scale of textiles by approximating its external properties in
those of silk, is the appearance of a monograph of the technology of
each, notices of which have been previously given (pp. 22-26).

There is little doubt, however, that the question of the future
industry in the various forms of cellulose, thread, film, structureless
powder or solid aggregate, obtainable by artificial means, mainly turns
upon cost of production. Irrespective of cost, there would, no doubt, be
a market for all these products, based upon such of their properties or
effects as are indispensable and not otherwise obtainable. As an
illustration, we may cite the extraordinary selling prices of 40-50 fr.
per kilo, for the 'artificial silks' (collodion process) which ruled
some three years ago; and we may note that for a special application of
viscose the dissolved cellulose is paid for at the rate of 10 per
lb. These facts are certainly worthy of mention, and should be borne in
mind as an index of some special features of modern manufacturing
industry. But with a material like cellulose rendered available in a new
shape the question which always arises more prominently than that of
limited uses at high prices is that of consumption on the extensive
scale which marks the older and well-known products. That question is
rapidly solving itself in this country as regards the 'artificial
silks.' There is at present a limited market at 9s.-10s. per lb., a
price which on the one side excludes extensive consumption, and on the
other practically bars manufacture in this country by any of the
collodion systems. It will appear from a very elementary calculation of
what we may call the theoretical costs that the above selling price
would not have a remunerative margin. The theoretical costs are made up
of

Raw materials[14]  {Cotton. Nitrating acid. Ether-alcohol (solvent).
                   {Denitrating chemicals.

                   {(a) Nitrating and preparing collodion. Denitrating
                   { and bleaching.
Labour             {(b) Textile operations. Spinning. Winding and twisting.
                   {Rewinding.

Power              {Making, filtering, and distributing collodion.
                   {Driving textile machinery.

Added to which are the costs of expert management and supervision and
general establishment expenses. It is evident that raw materials make up
a large fraction of the total cost; also that a very large item is the
waste work of converting the cellulose into nitrate, only to remove the
nitric groups so soon as the cellulose is obtained as thread.

It is clear that the aqueous solutions of cellulose have a double
advantage in this respect--not only do they readily yield an
approximately pure cellulose as a direct product of regeneration or
decomposition, but the first cost of the solution is very much less.
With these newer products, therefore, the spinning problem enters on a
new phase of struggle. It is certain that at selling prices at or about
5s. to 7s., very large markets will be open to the product or
products. The two processes which are or may be able to fulfil this
demand are those based (1) on cuprammonium solutions of cellulose, (2)
on the sulphocarbonate or viscose. As regards _first cost_ of the
solution the latter has a large advantage. One ton of wood pulp (at
12l.) can certainly be obtained in solution in a condition ready for
spinning at a total cost (materials) of less than 30l. The
cuprammonium process, so far as 'outside' information goes, requires for
production of the solution (1) cotton as raw material, (2) ammonia
(calc. as concentrated aqueous) equal to 1-1/2 times its weight, and
(3) metallic copper 25 p.ct. of its weight; and the costs are
approximately 100l. per ton. It is obvious that the materials are
recoverable from the precipitating-bath, but at a certain added cost. We
have no statements as to the proportion recoverable nor the costs
incurred, and we are therefore unable to measure the total net cost of
the regenerated cellulose by this process. It is certainly much less
than by the collodion processes. As to the textile quality of the
thread, the product has not yet been on a sufficiently wide selling
basis for that to have been determined. There are a great many factors
which enter here. Not merely the external characters of lustre,
softness, and translucency, but the all-important quality of uniformity
of thread. The collodion-spinning is a process still very defective in
this respect, and the defect is no doubt referable to the difficulty of
securing absolute physical invariability of the collodion. It is to be
regretted, in the interests of scientific development, that none of the
technologists who have published investigations of these processes have
entered into the discussion of the fundamental factors of the spinning
processes; we are, therefore, unable at this stage to discuss these
elements of a full comparison in greater detail. We cannot, for this
reason, say how far the cuprammonium process diverges in point of
control from the standard of the collodion processes. Of the 'viscose'
product we have a more intimate knowledge, and it certainly reaches a
higher general standard than the older and now well-known artificial
silks. The process is also sufficiently developed to enable the total
costs of production to be estimated at a figure less than one-half that
of the 'collodion' processes. This would assure to this system an
_entrée_ in this country, and a basis of expansion limited only by the
ordinary laws of supply and demand.

This prospect is opened up precisely at the moment when, for various
reasons connected both with the difficulties of manufacture and the
narrowing of the margin of profit, the proprietors of the two systems of
collodion-spinning have decided to abandon all idea of manufacturing by
these systems in this country.[15] We leave the discussion of the
industrial problem at this point.

In regard to other developments based upon the exceptional character and
properties of the sulphocarbonate, their further discussion will
exemplify no general principles; and as regards technical detail they
have been dealt with in the papers previously noticed.

As a purely general question, if there is to be any industry in these
'artificial' forms of cellulose, commensurate with the magnitude that
usually belongs to the cellulose industries, it must come by way of a
plastic or soluble form prepared at low cost, and conserving the
essential molecular properties of the cellulose aggregate. These are the
particular features of the sulphocarbonate. The obvious difficulties in
the way of its industrial applications are those caused by the presence
of alkali and sulphur compounds. These are dealt with by appropriate
chemical means; but the fact that there is a special chemistry of the
product has rendered its industrial progress slow. The work of the last
five years in this, as in other applications of cellulose in its many
derived forms, has resulted in a considerable addition to the domain of
practical chemistry.

Further developments will make an increasing demand upon our grasp of
the fundamental constitutional problems, to which it is the main purpose
of the present volume to contribute.

FOOTNOTES:

[11] This is the most complete notice that has appeared and the
bibliography is exhaustive. The publication comes into our hands too
late to be noticed in detail.

[12] _Text-book on Paper-making_, Cross and Bevan (Spon, London: second
edition, 1900). _Chemistry of Paper-making_, Griffin and Little (New
York, 1894: Howard Lockwood & Co.). _Handbuch d. Papierfabrikation_, C.
Hofmann (Berlin). _Paper Trade Review_, London (weekly).
_Papier-Zeitung_, Berlin.

[13] William Mather, M.P., of the firm of Mather & Platt, Limited,
Manchester.

[14] The actual costs varying considerably in the various countries, we
cannot make any specific statement. But from estimates we have made, the
costs of obtaining cotton in filtered solution as collodion multiply its
value by 12-14, the denitrations adding further costs and raising this
multiple to 18-20. In the same estimates we arrived at the conclusion
that the item for raw materials made up 60 p.ct. of the total cost of
the yarn.

[15] The recent failure of a French company founded for the exploitation
of the cuprammonium process may be taken as showing that it presents
very considerable technical difficulties. It is a matter of common
knowledge that this company _estimated_ the costs of production to be
such as to enable the product to be sold at 12 fr. per kilo., whereas
the costs actually obtaining were a large multiple of this figure.




INDEX OF AUTHORS


Bardy, C. H., 157

Bokorny, T., 43

Bronnert, E., 54

Bumcke, G., and Wolffenstein, R., 67

Buntrock, 25


Cross, C. F., 139, 152, 155

Cross, C. F., and Bevan, E. J., 92

Cross, C. F., Bevan, E. J., and Briggs, J. F., 118

Cross, C. F., Bevan, E. J., and Heiberg, T., 114

Cross, C. F., Bevan, E. J., and Smith, C., 101, 103, 105, 114, 145


De Haas, R. W. T., and Tollens, B., 151


Faber, O. v., and Tollens, B., 71

Feilitzen, H. v., and Tollens, B., 154

Fenton, H. J. H., 8

Fenton, H. J. H., and Gostling, M., 86

Fraenkel, A., and Friedlaender, P., 26


Gardner, P., 22

Gilson, E., 112


Hancock, W. C., and Dahl, O. W., 135

Hoffmeister, W., 96, 100


Kleiber, A., 97

Kröber, E., 121

Krüger, M., 119


Lange, H., 25

Lewes, V. H., 15

Luck, A., and Cross, C. F., 45


Margosches, B. M., 159

Morrell, R. S., and Crofts, J. M., 114

Mylius, F., 21


Nastukoff, H., 74


Omelianski, V., 76


Ruff, O., 117


Salkowski, E., 113

Schöne, A., and Tollens, B., 124

Seidel, H., 149

Sherman, H. C., 137

Simonsen, E., 146

Storer, F. H., 142

Strehlenert, R. W., 158

Suringar, H., and Tollens, B., 16, 124

Süvern, C., 63


Tollens, B., 148, 151

Tollens, B., and Glaubitz, H., 122


Vignon, L., 43, 70, 72, 94


Will, W., and Lenze, P., 41

Winterstein, E., 109, 144, 153




INDEX OF SUBJECTS


Acetone, action on cellulose nitrates of diluted, 46

Acid-cellulose, 68

Acids, volatile, from cellulose, 145

_Æschynomene aspera_, 135

Alcohol from cellulose and wood, 146

Alcoholic soda, mercerisation results with, 26

Alkali-cellulose, effects of long storage on, 31

Amyloid, vegetable, 153

Arabinose from gluconic acid, 117

'Ash' of plants, 13


_Bacterium xylinum_, 85

Barley plant, chemical processes in the, 103

---- straw, carbohydrates of, 105

Bleaching, 166

Bran, digestion of, 139

Brommethylfurfural, 8, 84, 86


Carbohydrates, action of hydrogen bromide on, 86;
  action of hydrogen peroxide on, 114;
  nitrated, as food for mould fungi, 43;
  nitrates of, 41;
  quantitative separation of, 96

Carbohydrates of barley straw, 105;
  of wheat, 137;
  of yeast, 113

'Caro's reagent,' 118

'Celloxin,' 71

Cellulose, alcohol from, 146;
  constitution of, 77, 92;
  fermentation of, 76;
  industrial uses of, 155;
  iodine reaction of, 21;
  methods for the estimation of, 3, 4, 16, 19, 97;
  nitration of, 43;
  saccharification of, 73;
  ultimate hydrolysis of, 11;
  volatile acids from, 145

---- acetates, monoacetate, formation of, 40;
  tetracetate, constitution of, 80

---- benzoates, 34;
  from structureless cellulose, 36;
  from three varieties of cotton, 35;
  monobenzoate, properties of, 36;
  dibenzoate, properties of, 37;
  acetylation of, 130;
  nitration of, 38

---- derivatives, commercial aspects of, 171;
  saccharification of, 73

---- nitrates, 44, 45, 83;
  structureless, 45, 51;
  cupric reducing power of, 73;
  instability of, 50, 53

---- sulphocarbonate, 27;
  effects of the nature of the cellulose, 28;

---- ---- solutions, analysis of, 32;
  iodine reaction of, 33;
  loss of carbon bisulphide, 33;
  viscosity of, 30

Cell-wall constituents, 97

Cereal celluloses, 101, 105

Chitin, 112

Chlorination, Cross and Bevan's method, 19;
  statistics of, 134

Chloro-lignone, 126

Collodion. _See_ Silk, artificial

Cotton, lustreing effect of mercerisation, 23;
  mercerised, structural properties of, 25;
  pentosane content of, 148

'Crude fibre,' 17

Cuprammonium solvent, 21, 58, 173

Currants, pectin of, 152


Denitration of collodion silk, 56;
  of jute nitrate, 133;
  products of, 74

Dioxybutyric acid, 71


Elder pith, 137

Eriodendron, seed hair of, 92

Explosives, 44;
  sporting powders, 52


Fermentation of cellulose, 76;
  of furfuroids, 108;
  of sugar from wood, 148

Fibres, report on miscellaneous, 139

Flax boiling, 168;
  spinning, 161

Fodder plants, pentosanes of, 122

Fungi, tissue constituents of, 109

Furfural from cellulose, oxycellulose, and hydrocellulose, 70;
  derivative from lævulose, 8;
  estimation as hydrazone and phloroglucide, 119, 121;
  oxidation of, 114, 118 (_refer also_ 'Pentosanes')

Furfuroids, 8, 10, 102, 105;
  assimilation of, 108


Gabriel's method of cellulose estimation, 18

Gluconic acid, action of hydrogen peroxide on, 117

Glucosamin, 112


Hemicellulose, 96, 97;
  determination and separation of, 100

Hönig's method of cellulose estimation, 18

'Hydralcellulose,' 68

Hydrocellulose, 73;
  nitration of, 43

Hydrogen peroxide, oxidations with, 114

Hydroxyfurfural in lignocellulose, 9, 116, 118


Incandescent mantles of artificial silk, 14, 15

Industrial appliances of cellulose, 155

Iodine reaction of cellulose, 21

Isosaccharinic acid, 71


Jute, composition of, 141;
  quality of, 140;
  treatment of, 142 (_refer also_ Lignocellulose)

---- acetate, 129

---- benzoate, 127;
  acetylation of, 130;
  nitration of, 132

---- nitrate, 131


Ketoses, physiological importance of, 9


Lange method of cellulose estimation, 18, 98

Lead compounds of nitrated carbohydrates, 49

Lignin, 100

Lignocellulose, constitution of, 133;
  esters of, 125;
  hydroxyfurfural in, 9;
  new type of, 135

Lignone complex, properties of, 126

'Lignorosin,' 151

'Lustra-cellulose.' _See_ Silk, artificial


Malt, pentosanes of, 122

Mather system of boiling textiles, 167

Mercerization, 22; shrinkage during, 24

Mercerised yarn, strength and elasticity of, 25, 26

Methylhydroxyfurfural, 84

Mould fungi, nitrated carbohydrates as food for, 43

Mycosin, 113


Nitrated carbohydrates, lead compounds of, 49

Nitrates of carbohydrates, 41

Nitrocellulose (_see_ Cellulose nitrates);
  silk, 55

'Normal' cellulose, definition of, 27

Normal paper, 160


Oxycellulose esters, 72;
  nitration of, 43;
  researches on, 71, 72, 74;
  _résumé_ of properties, 94

Oxygluconic acid, 117


Paper, deterioration of, 155;
  normal standard, 160;
  pulp, spinning of, 169

Peat, constituents of, 154

Pectins, 151, 152

Pentosanes, 100, 109, 144;
  constituents of cotton, 124;
  constituents of fodder, 122;
  estimation of, 121;
  of seeds during germination, 124

'Permanent tissue,' 103

Phloroglucinol, 119, 121

Plant tissues, carbohydrates of, 96, 97, 99

Plants, source of unsaturated compounds in, 145

Powders, manufacture of sporting, 52


Saccharification of cellulose and derivatives, 73

Schulze method of cellulose estimation, 18, 98

Schweizer solution, 101

Seeds, pentosanes in germinating, 124

Silica in plant tissues, 13

Silk, artificial, 54, 62, 63, 172;
  bibliography of, 60;
  from cuprammonium, 58, 64, 173;
  from nitrocellulose (collodion), 55, 63, 172;
  from viscose, 59;
  from zinc chloride, 59;
  reactions of, 64

---- natural, reactions of, 64

Straws, 101, 105

Succinic acid from furfural, 118

Sulphite waste liquors, 149, 164

'Swedish' filter paper, 14


Tissue constituents, 99, 109

Trees, composition of trunk woods, 142


Viscose and viscoid, 157, 158, 159

---- silk, 59, 175

---- ---- specific gravity of, 34 (_refer also_ Cellulose
sulphocarbonate)

'Vulcanised fibre,' 20


Weende, method of cellulose estimation (crude fibre), 17, 98

Welsbach mantles, 14;
  Clamond type, 15

Wheat grain, insoluble carbohydrates of, 137

Wood, alcohol from, 146, 148

Wood-cellulose, waste liquors, 149

Wood-gum, 144

Wood-pulp, processes, 162

Wood, trunks of trees, 142


Yeast, carbohydrates of, 113


Zinc chloride, artificial silk, 59;
  solvent action of, 20








*** END OF THE PROJECT GUTENBERG EBOOK RESEARCHES ON CELLULOSE, 1895-1900 ***


    

Updated editions will replace the previous one—the old editions will
be renamed.

Creating the works from print editions not protected by U.S. copyright
law means that no one owns a United States copyright in these works,
so the Foundation (and you!) can copy and distribute it in the United
States without permission and without paying copyright
royalties. Special rules, set forth in the General Terms of Use part
of this license, apply to copying and distributing Project
Gutenberg™ electronic works to protect the PROJECT GUTENBERG™
concept and trademark. Project Gutenberg is a registered trademark,
and may not be used if you charge for an eBook, except by following
the terms of the trademark license, including paying royalties for use
of the Project Gutenberg trademark. If you do not charge anything for
copies of this eBook, complying with the trademark license is very
easy. You may use this eBook for nearly any purpose such as creation
of derivative works, reports, performances and research. Project
Gutenberg eBooks may be modified and printed and given away—you may
do practically ANYTHING in the United States with eBooks not protected
by U.S. copyright law. Redistribution is subject to the trademark
license, especially commercial redistribution.


START: FULL LICENSE

THE FULL PROJECT GUTENBERG LICENSE

PLEASE READ THIS BEFORE YOU DISTRIBUTE OR USE THIS WORK

To protect the Project Gutenberg™ mission of promoting the free
distribution of electronic works, by using or distributing this work
(or any other work associated in any way with the phrase “Project
Gutenberg”), you agree to comply with all the terms of the Full
Project Gutenberg™ License available with this file or online at
www.gutenberg.org/license.

Section 1. General Terms of Use and Redistributing Project Gutenberg™
electronic works

1.A. By reading or using any part of this Project Gutenberg™
electronic work, you indicate that you have read, understand, agree to
and accept all the terms of this license and intellectual property
(trademark/copyright) agreement. If you do not agree to abide by all
the terms of this agreement, you must cease using and return or
destroy all copies of Project Gutenberg™ electronic works in your
possession. If you paid a fee for obtaining a copy of or access to a
Project Gutenberg™ electronic work and you do not agree to be bound
by the terms of this agreement, you may obtain a refund from the person
or entity to whom you paid the fee as set forth in paragraph 1.E.8.

1.B. “Project Gutenberg” is a registered trademark. It may only be
used on or associated in any way with an electronic work by people who
agree to be bound by the terms of this agreement. There are a few
things that you can do with most Project Gutenberg™ electronic works
even without complying with the full terms of this agreement. See
paragraph 1.C below. There are a lot of things you can do with Project
Gutenberg™ electronic works if you follow the terms of this
agreement and help preserve free future access to Project Gutenberg™
electronic works. See paragraph 1.E below.

1.C. The Project Gutenberg Literary Archive Foundation (“the
Foundation” or PGLAF), owns a compilation copyright in the collection
of Project Gutenberg™ electronic works. Nearly all the individual
works in the collection are in the public domain in the United
States. If an individual work is unprotected by copyright law in the
United States and you are located in the United States, we do not
claim a right to prevent you from copying, distributing, performing,
displaying or creating derivative works based on the work as long as
all references to Project Gutenberg are removed. Of course, we hope
that you will support the Project Gutenberg™ mission of promoting
free access to electronic works by freely sharing Project Gutenberg™
works in compliance with the terms of this agreement for keeping the
Project Gutenberg™ name associated with the work. You can easily
comply with the terms of this agreement by keeping this work in the
same format with its attached full Project Gutenberg™ License when
you share it without charge with others.

1.D. The copyright laws of the place where you are located also govern
what you can do with this work. Copyright laws in most countries are
in a constant state of change. If you are outside the United States,
check the laws of your country in addition to the terms of this
agreement before downloading, copying, displaying, performing,
distributing or creating derivative works based on this work or any
other Project Gutenberg™ work. The Foundation makes no
representations concerning the copyright status of any work in any
country other than the United States.

1.E. Unless you have removed all references to Project Gutenberg:

1.E.1. The following sentence, with active links to, or other
immediate access to, the full Project Gutenberg™ License must appear
prominently whenever any copy of a Project Gutenberg™ work (any work
on which the phrase “Project Gutenberg” appears, or with which the
phrase “Project Gutenberg” is associated) is accessed, displayed,
performed, viewed, copied or distributed:

    This eBook is for the use of anyone anywhere in the United States and most
    other parts of the world at no cost and with almost no restrictions
    whatsoever. You may copy it, give it away or re-use it under the terms
    of the Project Gutenberg License included with this eBook or online
    at www.gutenberg.org. If you
    are not located in the United States, you will have to check the laws
    of the country where you are located before using this eBook.
  
1.E.2. If an individual Project Gutenberg™ electronic work is
derived from texts not protected by U.S. copyright law (does not
contain a notice indicating that it is posted with permission of the
copyright holder), the work can be copied and distributed to anyone in
the United States without paying any fees or charges. If you are
redistributing or providing access to a work with the phrase “Project
Gutenberg” associated with or appearing on the work, you must comply
either with the requirements of paragraphs 1.E.1 through 1.E.7 or
obtain permission for the use of the work and the Project Gutenberg™
trademark as set forth in paragraphs 1.E.8 or 1.E.9.

1.E.3. If an individual Project Gutenberg™ electronic work is posted
with the permission of the copyright holder, your use and distribution
must comply with both paragraphs 1.E.1 through 1.E.7 and any
additional terms imposed by the copyright holder. Additional terms
will be linked to the Project Gutenberg™ License for all works
posted with the permission of the copyright holder found at the
beginning of this work.

1.E.4. Do not unlink or detach or remove the full Project Gutenberg™
License terms from this work, or any files containing a part of this
work or any other work associated with Project Gutenberg™.

1.E.5. Do not copy, display, perform, distribute or redistribute this
electronic work, or any part of this electronic work, without
prominently displaying the sentence set forth in paragraph 1.E.1 with
active links or immediate access to the full terms of the Project
Gutenberg™ License.

1.E.6. You may convert to and distribute this work in any binary,
compressed, marked up, nonproprietary or proprietary form, including
any word processing or hypertext form. However, if you provide access
to or distribute copies of a Project Gutenberg™ work in a format
other than “Plain Vanilla ASCII” or other format used in the official
version posted on the official Project Gutenberg™ website
(www.gutenberg.org), you must, at no additional cost, fee or expense
to the user, provide a copy, a means of exporting a copy, or a means
of obtaining a copy upon request, of the work in its original “Plain
Vanilla ASCII” or other form. Any alternate format must include the
full Project Gutenberg™ License as specified in paragraph 1.E.1.

1.E.7. Do not charge a fee for access to, viewing, displaying,
performing, copying or distributing any Project Gutenberg™ works
unless you comply with paragraph 1.E.8 or 1.E.9.

1.E.8. You may charge a reasonable fee for copies of or providing
access to or distributing Project Gutenberg™ electronic works
provided that:

    • You pay a royalty fee of 20% of the gross profits you derive from
        the use of Project Gutenberg™ works calculated using the method
        you already use to calculate your applicable taxes. The fee is owed
        to the owner of the Project Gutenberg™ trademark, but he has
        agreed to donate royalties under this paragraph to the Project
        Gutenberg Literary Archive Foundation. Royalty payments must be paid
        within 60 days following each date on which you prepare (or are
        legally required to prepare) your periodic tax returns. Royalty
        payments should be clearly marked as such and sent to the Project
        Gutenberg Literary Archive Foundation at the address specified in
        Section 4, “Information about donations to the Project Gutenberg
        Literary Archive Foundation.”
    
    • You provide a full refund of any money paid by a user who notifies
        you in writing (or by e-mail) within 30 days of receipt that s/he
        does not agree to the terms of the full Project Gutenberg™
        License. You must require such a user to return or destroy all
        copies of the works possessed in a physical medium and discontinue
        all use of and all access to other copies of Project Gutenberg™
        works.
    
    • You provide, in accordance with paragraph 1.F.3, a full refund of
        any money paid for a work or a replacement copy, if a defect in the
        electronic work is discovered and reported to you within 90 days of
        receipt of the work.
    
    • You comply with all other terms of this agreement for free
        distribution of Project Gutenberg™ works.
    

1.E.9. If you wish to charge a fee or distribute a Project
Gutenberg™ electronic work or group of works on different terms than
are set forth in this agreement, you must obtain permission in writing
from the Project Gutenberg Literary Archive Foundation, the manager of
the Project Gutenberg™ trademark. Contact the Foundation as set
forth in Section 3 below.

1.F.

1.F.1. Project Gutenberg volunteers and employees expend considerable
effort to identify, do copyright research on, transcribe and proofread
works not protected by U.S. copyright law in creating the Project
Gutenberg™ collection. Despite these efforts, Project Gutenberg™
electronic works, and the medium on which they may be stored, may
contain “Defects,” such as, but not limited to, incomplete, inaccurate
or corrupt data, transcription errors, a copyright or other
intellectual property infringement, a defective or damaged disk or
other medium, a computer virus, or computer codes that damage or
cannot be read by your equipment.

1.F.2. LIMITED WARRANTY, DISCLAIMER OF DAMAGES - Except for the “Right
of Replacement or Refund” described in paragraph 1.F.3, the Project
Gutenberg Literary Archive Foundation, the owner of the Project
Gutenberg™ trademark, and any other party distributing a Project
Gutenberg™ electronic work under this agreement, disclaim all
liability to you for damages, costs and expenses, including legal
fees. YOU AGREE THAT YOU HAVE NO REMEDIES FOR NEGLIGENCE, STRICT
LIABILITY, BREACH OF WARRANTY OR BREACH OF CONTRACT EXCEPT THOSE
PROVIDED IN PARAGRAPH 1.F.3. YOU AGREE THAT THE FOUNDATION, THE
TRADEMARK OWNER, AND ANY DISTRIBUTOR UNDER THIS AGREEMENT WILL NOT BE
LIABLE TO YOU FOR ACTUAL, DIRECT, INDIRECT, CONSEQUENTIAL, PUNITIVE OR
INCIDENTAL DAMAGES EVEN IF YOU GIVE NOTICE OF THE POSSIBILITY OF SUCH
DAMAGE.

1.F.3. LIMITED RIGHT OF REPLACEMENT OR REFUND - If you discover a
defect in this electronic work within 90 days of receiving it, you can
receive a refund of the money (if any) you paid for it by sending a
written explanation to the person you received the work from. If you
received the work on a physical medium, you must return the medium
with your written explanation. The person or entity that provided you
with the defective work may elect to provide a replacement copy in
lieu of a refund. If you received the work electronically, the person
or entity providing it to you may choose to give you a second
opportunity to receive the work electronically in lieu of a refund. If
the second copy is also defective, you may demand a refund in writing
without further opportunities to fix the problem.

1.F.4. Except for the limited right of replacement or refund set forth
in paragraph 1.F.3, this work is provided to you ‘AS-IS’, WITH NO
OTHER WARRANTIES OF ANY KIND, EXPRESS OR IMPLIED, INCLUDING BUT NOT
LIMITED TO WARRANTIES OF MERCHANTABILITY OR FITNESS FOR ANY PURPOSE.

1.F.5. Some states do not allow disclaimers of certain implied
warranties or the exclusion or limitation of certain types of
damages. If any disclaimer or limitation set forth in this agreement
violates the law of the state applicable to this agreement, the
agreement shall be interpreted to make the maximum disclaimer or
limitation permitted by the applicable state law. The invalidity or
unenforceability of any provision of this agreement shall not void the
remaining provisions.

1.F.6. INDEMNITY - You agree to indemnify and hold the Foundation, the
trademark owner, any agent or employee of the Foundation, anyone
providing copies of Project Gutenberg™ electronic works in
accordance with this agreement, and any volunteers associated with the
production, promotion and distribution of Project Gutenberg™
electronic works, harmless from all liability, costs and expenses,
including legal fees, that arise directly or indirectly from any of
the following which you do or cause to occur: (a) distribution of this
or any Project Gutenberg™ work, (b) alteration, modification, or
additions or deletions to any Project Gutenberg™ work, and (c) any
Defect you cause.

Section 2. Information about the Mission of Project Gutenberg™

Project Gutenberg™ is synonymous with the free distribution of
electronic works in formats readable by the widest variety of
computers including obsolete, old, middle-aged and new computers. It
exists because of the efforts of hundreds of volunteers and donations
from people in all walks of life.

Volunteers and financial support to provide volunteers with the
assistance they need are critical to reaching Project Gutenberg™’s
goals and ensuring that the Project Gutenberg™ collection will
remain freely available for generations to come. In 2001, the Project
Gutenberg Literary Archive Foundation was created to provide a secure
and permanent future for Project Gutenberg™ and future
generations. To learn more about the Project Gutenberg Literary
Archive Foundation and how your efforts and donations can help, see
Sections 3 and 4 and the Foundation information page at www.gutenberg.org.

Section 3. Information about the Project Gutenberg Literary Archive Foundation

The Project Gutenberg Literary Archive Foundation is a non-profit
501(c)(3) educational corporation organized under the laws of the
state of Mississippi and granted tax exempt status by the Internal
Revenue Service. The Foundation’s EIN or federal tax identification
number is 64-6221541. Contributions to the Project Gutenberg Literary
Archive Foundation are tax deductible to the full extent permitted by
U.S. federal laws and your state’s laws.

The Foundation’s business office is located at 809 North 1500 West,
Salt Lake City, UT 84116, (801) 596-1887. Email contact links and up
to date contact information can be found at the Foundation’s website
and official page at www.gutenberg.org/contact

Section 4. Information about Donations to the Project Gutenberg
Literary Archive Foundation

Project Gutenberg™ depends upon and cannot survive without widespread
public support and donations to carry out its mission of
increasing the number of public domain and licensed works that can be
freely distributed in machine-readable form accessible by the widest
array of equipment including outdated equipment. Many small donations
($1 to $5,000) are particularly important to maintaining tax exempt
status with the IRS.

The Foundation is committed to complying with the laws regulating
charities and charitable donations in all 50 states of the United
States. Compliance requirements are not uniform and it takes a
considerable effort, much paperwork and many fees to meet and keep up
with these requirements. We do not solicit donations in locations
where we have not received written confirmation of compliance. To SEND
DONATIONS or determine the status of compliance for any particular state
visit www.gutenberg.org/donate.

While we cannot and do not solicit contributions from states where we
have not met the solicitation requirements, we know of no prohibition
against accepting unsolicited donations from donors in such states who
approach us with offers to donate.

International donations are gratefully accepted, but we cannot make
any statements concerning tax treatment of donations received from
outside the United States. U.S. laws alone swamp our small staff.

Please check the Project Gutenberg web pages for current donation
methods and addresses. Donations are accepted in a number of other
ways including checks, online payments and credit card donations. To
donate, please visit: www.gutenberg.org/donate.

Section 5. General Information About Project Gutenberg™ electronic works

Professor Michael S. Hart was the originator of the Project
Gutenberg™ concept of a library of electronic works that could be
freely shared with anyone. For forty years, he produced and
distributed Project Gutenberg™ eBooks with only a loose network of
volunteer support.

Project Gutenberg™ eBooks are often created from several printed
editions, all of which are confirmed as not protected by copyright in
the U.S. unless a copyright notice is included. Thus, we do not
necessarily keep eBooks in compliance with any particular paper
edition.

Most people start at our website which has the main PG search
facility: www.gutenberg.org.

This website includes information about Project Gutenberg™,
including how to make donations to the Project Gutenberg Literary
Archive Foundation, how to help produce our new eBooks, and how to
subscribe to our email newsletter to hear about new eBooks.